NASA NTRS1991

1000 to 1200 K time-dependent compressive deformation of single-crystalline and polycrystalline B2 Ni-40Al

The 1000-K and 1200-K time-dependent deformation of 100-line-oriented and non-100-line-oriented single crystals of Ni-40Al (made by a modified Bridgman technique) was examined over a large range of strain rates (from 0.1 to 10 to the -7th per sec). The results were compared with those for polycrystalline Ni-40Al made by hot pressing XD synthesized powder. The results from measurements of slow-plastic-strain-rate properties of the two materials show that single crystals offer no strength advantage over polycrystalline material. Both forms were found to deform via a dislocation climb mechanism.

Whittenberger, J. D.↗

NASA NTRS1991

1000 to 1300 K slow plastic compression properties of Al-deficient NiAl

Nickel aluminides containing 37, 38.5 and 40 at. pct Al have been fabricated by XD synthesis and hot pressing. Such materials were compression tested in air under constant velocity conditions between 1000 and 1300 K. Examination of the microstructures of hot pressed and compression tested aluminides indicated that the structure consisted of two phases, gamma-prime and NiAl, for essentially all conditions, where gamma-prime was usually found on the NiAl grain boundaries. The stress-strain behavior of all three intermetallics was similar where flow at a nominally constant stress occurred after about two-percent plastic deformation. Furthermore, the 1000 to 1300 K flow stress-strain rate properties are nearly identical for these materials, and they are much lower than those for XD processed Ni-50Al. The overall deformation of the two phase nickel aluminides appears to be controlled by dislocation climb in NiAl rather than processes in gamma-prime.

Whittenberger, J. D.↗

NASA NTRS1991

1200 and 1300 K slow plastic compression properties of Ni-50Al composites

XD synthesis, powder blending, and hot pressing techniques have been utilized to produce NiAl composites containing 4, 7.5, 15, and 25 vol pct alumina whiskers and hybrid composite materials with 15 vol pct Al2O3 + 10 or 20 vol pct, nominally 1 micron TiB2 particles. The resistance to slow plastic flow was determined at 1200 and 1300 K via compression testing in air under constant velocity conditions. The stress-strain behavior of the intermetallic composites depended on the fraction of second phases where the 4 and 7.5 percent Al2O3 materials flowed at a nominally constant stress after about 2 percent deformation, while all the other composites exhibited diffuse yielding followed by strain softening. The flow stress-strain rate properties increased with volume fraction of Al2O3 whiskers except for the 4 and 7.5 percent materials, which had similar strengths. The hybrid composite NiAl + 15Al2O3 + 10TiB2 was substantially stronger than the materials simply containing alumina. Deformation in these composites can be described by the Kelly and Street model of creep in perfectly bonded, rigid, discontinuous fiber materials.

Whittenberger, J. D.↗

NASA NTRS1990

High-temperature slow-strain-rate compression studies on CoAl-TiB2 composites

Results are presented of compressive deformation tests performed on particulate-reinforced CoAl-TiB2 composites in the temperature range 1100-1300 K. Hot-pressed and postdeformation microstructures were characterized by TEM and by optical microscopy. It was found that the addition of TiB2 particles improves the deformation resistance of the matrix, due to dislocation-particle interactions.

Mannan, S. K.↗

NASA NTRS1990

Slow plastic deformation of extruded NiAl-10TiB2 particulate composites at 1200 and 1300 K

A dispersion of 1-micron TiB2 particles in the B2 crystal structure NiAl intermetallic can effectively increase its elevated temperature strength, in association with increasing deformation resistance with TiB2 volume fraction. Attention is presently given to alternative densification methods, which may increase the initial as-fabricated dislocation density and lead to enhanced elevated-temperature strength. The 'XD' extrusion method was used to produce NiAl with 10 vol pct TiB2. Although apparent extrusion defects were occasionally found, neither grain-boundary cracking nor particle-matrix separation occurred.

Whittenberger, J. D.↗

NASA NTRS1990

Elevated temperature slow plastic deformation of NiAl-TiB2 particulate composites at 1200 and 1300 K

Elevated temperature compression testing has been conducted in air at 1200 and 1300 K with strain rates varying from about 10 to the -4th to about 10 to the -7th/sec on NiAl-TiB2 particulate composites. These materials, which consisted of a B2 crystal structure intermetallic Ni-50 at. pct Al matrix and from 0 to 30 vol pct of approximately 1- micron diameter TiB2 particles, were fabricated by XD synthesis and hot pressed to full density. Flow strength of the composites increased with volume fraction of the strengthening phase with NiAl-30TiB2 being approximately three times stronger than NiAl. Comparison of the light optical and TEM microstructures of as-received and tested samples revealed that reactions did not occur between the two phases, and NiAl-TiB2 interfaces were not cracked during deformation. Additional TEM indicated that the particles stabilize a vastly different microstructure in the NiAl matrix of the composites than that formed in unreinforced NiAl.

Whittenberger, J. Daniel↗

NASA NTRS1989

1100 to 1300 K slow plastic compression properties of Ni-38.5Al composites

Compressive properties of Ni-38.5Al (in at. pct) composites containing 4, 7.5, and 15 vol pct Al2O3 whiskers or 20 vol pct TiB2 particles were investigated in samples compacted to full density by vacuum hot pressing at 20.7 MPa and 1725 K, followed by HIP at 207 MPa and 1725 K. Constant-velocity compression tests were conducted in air at 1100, 1200, and 1300 K to 8 percent strain. It was found that the elevated-temperature compressive properties of Ni-38.5Al+Al2O3 whisker composites were only marginally better than those of the matrix, and that the composite containing 20 vol pct TiB2 particles was only slightly stronger than unreinforced Ni-38.5Al.

Whittenberger, J. Daniel↗

NASA NTRS1989

1200 to 1400 K slow strain rate compressive behavior of small grain size NiAl/Ni2AlTi alloys and NiAl/Ni2AlTi-TiB2 composites

In order to impart ductility into NiAl-Ni2AlTi alloys, small grain size single (Ni-45Al-5Ti) and two (Ni-40Al-10Ti) phase intermetallics are fabricated by a process which yields fine microstructures in NiAl. The results of a study of elevated temperature compressive properties of two small grain size NiAl-Ni2AlTi alloys are then described. In addition, the behavior of the Ti-modified nickel aluminides with 20 vol pct TiB2 particles of approximately 1 micron in diameter is also investigated, since these compositions have the potential for being the matrix material in high temperature particulate-strengthened composites.

Whittenberger, J. Daniel↗

NASA NTRS1989

1200 to 1400 K slow strain rate compressive properties of NiAl/Ni2AlTi-base materials

An attempt to apply the Martin Marietta Corporation's XD technology to the fabrication of NiAl-Ni2AlTi materials with improved creep properties is presented. Composite materials, containing from 0 to 30 vol pct of nominally 1-micron-diameter TiB2 particles in the intermetallic matrix have been produced by the XD process and compacted by hot pressing. Such composites demonstrated significant strength increases, approaching 3-fold for the 20 vol pct materials, in comparison to the unreinforced aluminide. This behavior was accomplished without deleterious side effects as the grain boundaries and particle-matrix interfaces were intact after compressive deformation to 10 percent or more strain. Typical true compressive stress-strain diagrams for materials tested in air between 1200 and 1400 K at approximate strain rates of 1.7 x 10 to the -6th/sec are presented.

Whittenberger, J. Daniel↗

NASA NTRS1988

Elevated temperature slow plastic deformation of NiAl/TiB2 particulate composites

The 'XD' process for production of discontinuously-reinforced metal-matrix composites has been used to enhance the high-temperature strength of NiAl-TiB2 composites with particulate densities of up to 30 vol pct. SEM, TEM, and optical characterizations of the resulting microstructures showed the average TiB2 particle size to be about 1 micron, while the average grain of the NiAl matrix was of the order of 10 microns. Elevated temperature compression tests conducted at 1200 and 1300 K indicated flow strengths to increase with TiB2 content, so that the 20 vol pct TiB2-reinforced composite was three times stronger than the unreinforced NiAl; this is ascribed to the very high density of microstructural tangled dislocations, loops, and subgrain boundaries connecting the particles.

Whittenberger, J. Daniel↗