Cd-excess and CdCl2 treatment effects on Sb-doped CdTe devices
Cd-excess and CdCl2 treatment effects on Sb-doped CdTe devices
Engineering topics
Publications and source records attributed to Manoukian, Gregory.
Cd-excess and CdCl2 treatment effects on Sb-doped CdTe devices
Group-V doping can enhance the efficiency of CdTe photovoltaic devices by increasing the open-circuit voltage (Voc), if long lifetimes can be retained and radiative voltage loss can be avoided. In this preliminary study, ex-situ Sb doping via drive-in diffusion improved grain sizes compared to Sb-free films without CdCl2 treatment. Sb doping did not reduce the carrier lifetime for uniform CdSeTe absorbers. Additionally, the CST-air surface recombination decreased with Sb. No potential fluctuations were observed by PL at this doping level. The [Sb] and carrier concentration for this study are not yet measured so the conclusions drawn are all preliminary
Our team has achieved ~20% doping activation of CdSeTe with antimony (Sb), whose shallow acceptor level makes it a viable alternative to As.1,2 Arsenic (As)-doped graded CdSeTe photovoltaics have achieved record efficiencies of 22.3%. Remaining challenges include doping activation of only ~2% in polycrystalline films and radiative voltage losses of ~100 mV. Here we use (transient) terahertz and photoluminescence spectroscopy of CdTe:Sb and CdSeTe:Sb to show sufficiently long bulk lifetimes to enable high-efficiency devices. Early results also indicate dominant bandgap emission in CdSeTe:Sb and a lack of potential fluctuations with Sb-doping that have proven detrimental for As-doped films. While more work is needed, these results show significant promise for Sb doping.
The effect of high-temperature annealing (HTA) treatments and Cd-excess during the in-situ doping of CdSeTe:Sb is investigated. Optimized treatments eliminate the wurtzite phase from the as-deposited CdSeTe layer, while facilitating Se intermixing and grain size enhancement before CdCl2 treatment. The improved device stack quality results in a VOC improvement of 250 mV. VOC is further improved by tuning the Cd/Sb flux ratio during CdSeTe:Sb deposition. The lowest defect concentration is achieved at Cd/Sb of 1.4:1, which produced the best VOC CdSeTe:Sb cell with VOC = 849mV, despite a decreased carrier concentration due to the harsh CdCl2 treatment.
Arsenic (As)-doped graded Cd(Se,Te) photovoltaics have achieved record efficiency of 22.4%, but further increases in efficiency have been limited by doping activation of only ~1% and radiative voltage losses of ~100 meV. Antimony (Sb) can also act as a p-type dopant of Cd(Se,Te) but has received relatively little attention. We measured carrier dynamics and photoluminescence of Sb-doped CdTe and CdSeTe films grown by vapor-transport deposition, with dopant activation up to ~20% Time resolved terahertz (TRTS) and photoluminescence (TRPL) data were fit by simulating the semiconductor equations, revealing bulk lifetimes of >20 ns in CdTe:Sb and >65 ns in CdSeTe:Sb and surface recombination velocities <1000 cm/s at alumina interfaces. We also qualitatively compare transients and PL spectra of doped and undoped films, with no apparent variation associated with hole concentrations up to 1015 cm-3. Preliminary variable temperature steady state photoluminescence (VT-SSPL) indicates dominant band-gap emission in CdSeTe:Sb and no evidence of potential fluctuations with Sb-doping up to this hole concentration.
Our team has achieved ~20% doping activation of CdSeTe with antimony (Sb), whose shallow acceptor level makes it a viable alternative to As.1,2 Arsenic (As)-doped graded CdSeTe photovoltaics have achieved record efficiencies of 22.3%. Remaining challenges include doping activation of only ~2% in polycrystalline films and radiative voltage losses of ~100 mV. Here we use (transient) terahertz and photoluminescence spectroscopy of CdTe:Sb and CdSeTe:Sb to show sufficiently long bulk lifetimes to enable high-efficiency devices. Early results also indicate dominant bandgap emission in CdSeTe:Sb and a lack of potential fluctuations with Sb-doping that have proven detrimental for As-doped films. While more work is needed, these results show significant promise for Sb doping.
Quantifying Carrier Dynamics in CdSeTe Absorbers with Time Resolved Terahertz and Photoluminescence Spectroscopies