Machine tool cross beam design, fabrication, and testing using metal big area additive manufacturing

This paper describes the application of metal Big Area Additive Manufacturing (mBAAM) to the fabrication of a machine tool cross beam. The replacement of a traditional box design weldment with a new design printed by wire arc additive manufacturing using the MedUSA system at Oak Ridge National Laboratory (ORNL) is detailed. This requires a new design strategy based on the unique mBAAM capabilities. The intent of the new design is to reduce mass, while maintaining the dynamic stiffness. To compare the two designs, the natural frequencies and mode shapes are measured using impact testing and predicted using finite element analysis. It is confirmed that the printed structure dynamics agreed with the numerical model predictions, which demonstrates that it is feasible to model a large-scale mBAAM part and understand its behavior prior to printing. Another notable outcome of this study is that the significant residual stress and distortion in the print indicate that knowledge gaps remain for widespread implementation of mBAAM.

42 ENGINEERING↗
DOE OSTI2023

Effects of lead and lean in multi-axis directed energy deposition

Here, the present study examines the effect of varying laser incidence angles on textural, microstructural, and geometric characteristics of directed energy deposition (DED) processed materials, providing a more comprehensive outlook on participating laser-matter interaction phenomena and ultimately devising strategies to ameliorate print performance. In this study, single-layer, single-/multi-track specimens were processed to examine the effect of non-orthogonal angular configurations on bead morphology, microstructure, phase composition, and textural representation of DED-processed 316L stainless steel materials. It was observed that bead size decreased at increasing lead and lean angles. Asymmetry in the distribution of the bead morphology as a function of lead angle indicates better catchment for acute lead angle configurations over obtuse configurations. No significant differences in phase composition, texture, and microstructure were observed in moderate off-axis configurations. When the penetration depth for the deposits was below 20 μm, columnar structures dominated the microstructure of the deposited material. At deeper penetration depths, columnar and equiaxed structures were observed at the bead-substrate interface and center of the bead, respectively. Compared to powder-blown DED, wire-DED dilution profiles were found to be asymmetric in both orthogonal and non-orthogonal wire DED samples.

36 MATERIALS SCIENCE↗
DOE OSTI2020

Investigating the Linear Thermal Expansion of Additively Manufactured Multi-Material Joining between Invar and Steel

This work investigated the linear thermal expansion properties of a multi-material specimen fabricated with Invar M93 and A36 steel. A sequence of tests was performed to investigate the viability of additively manufactured Invar M93 for lowering the coefficient of thermal expansion (CTE) in multi-material part tooling. Invar beads were additively manufactured on a steel base plate using a fiber laser system, and samples were taken from the steel, Invar, and the interface between the two materials. The CTE of the samples was measured between 40 °C and 150 °C using a thermomechanical analyzer, and the elemental composition was studied with energy dispersive X-ray spectroscopy. The CTE of samples taken from the steel and the interface remained comparable to that of A36 steel; however, deviations between the thermal expansion values were prevalent due to element diffusion in and around the heat-affected zone. The CTEs measured from the Invar bead were lower than those from the other sections with the largest and smallest thermal expansion values being 10.40 μm/m-K and 2.09 μm/m-K. In each of the sections, the largest CTE was measured from samples taken from the end of the weld beads. An additional test was performed to measure the aggregate expansion of multi-material tools. Invar beads were welded on an A36 steel plate. The invar was machined, and the sample was heated in an oven from 40 °C and 160 °C. Strain gauges were placed on the surface of the part and were used to analyze how the combined thermal expansions of the invar and steel would affect the thermal expansion on the surface of a tool. There were small deviations between the expansion values measured by gauges placed in different orientations, and the elongation of the sample was greatest along the dimension containing a larger percentage of steel. On average, the expansion of the machined Invar surface was 42% less than the expansion of the steel surface. The results of this work demonstrate that additively manufactured Invar can be utilized to decrease the CTE for multi-material part tooling.

36 MATERIALS SCIENCE↗
DOE OSTI2020

An experimental investigation of the effectiveness of Ar-CO 2 shielding gas mixture for the wire arc additive process

Wire arc additive manufacturing (AM) is the process by which a large, metallic structure is built layer-by-layer using a welding arc to melt a wire feedstock. A novel opportunity exists to alter the shielding gas composition to fabricate distinct geometrical features without altering the other AM parameters. In this paper, shielding gases with varied concentrations of Argon (Ar) and CO 2 was used to deposit three distinct geometric shapes (walls, infill, and overhang) using a wire-based additive manufacturing system utilizing the gas metal arc welding (GMAW) surface tension transfer (STT) process. Computer-aided design (CAD) models were sliced with a custom-built slicer, and the sliced algorithm was converted into optimal robotic toolpaths. A custom virtual instrument (VI) was built in LabVIEW to compare the temperature profiles on the surface during each deposition process. After each deposition, the geometric features were scanned, and the surface waviness value was evaluated. Tensile and Charpy impact coupons were extracted from the wall geometries in the longitudinal and transverse directions and tested. The results indicated that a higher CO 2 content produced higher melt pool temperatures to an extent, while lower contents of CO 2 resulted in a dimensionally accurate geometry. The data also indicated that the 2%/98% CO 2 /Ar blend produced scatter in tensile strength and the analysis of variance (ANOVA) shows significant difference. However, the intermediate range of CO 2 (5–10%) resulted in uniform tensile properties. Altogether, these results indicate that a 5%/95% CO 2 /Ar blend is the ideal shielding gas for lowering process temperatures and improving mechanical properties in wire arc additive manufacturing using the gas metal arc welding surface tension transfer process. Additionally, varying concentrations of Ar/CO 2 can be used within the same part in order to modify the local properties or process parameters such as strength, toughness, temperature, or dimensional features. This may improve overall manufacturing quality without sacrificing specific properties.