Matanovic, Ivana

Publications and source records attributed to Matanovic, Ivana.

18 records
All sourcesNASA NTRSDOE OSTI
DOE OSTI2024

Corrosion-Resistant Non-Carbon Electrocatalyst Supports for PEFCS

Insufficient durability of commercial catalysts is a persistent issue for PEFC applications.1 Herein, Pt on Nb-doped-TiO 2 is reported as a highly durable electrocatalyst on which the direct 4-electron reduction of oxygen to water is more facile compared to Pt/C. All performance metrics are reported comparing Pt/Nb-TiO2 with a 15% Pt loading, against a commercial Pt/C catalyst (46.5% Pt loading, Tanaka, K. K.). Nb-doped-TiO 2 with high surface area and high electronic conductivity was synthesized using the supercritical fluid method. Initially, the durability of the catalyst was characterized using accelerated stability tests (ASTs) involving 10,000 high potential cycles (DOE/FCCJ protocol) and the Pt/Nb-TiO 2 was found to retain 78% of its initial electrochemically active surface area (ECSA) compared to the 57.6 % retained by Pt/C. These observations were in excellent agreement with previous reports that the Pt particle size of Pt/C grew from 2nm to 8nm during the AST protocol along with severe corrosion and amorphization of the carbon surface.2, 3 TEM and XPS studies of the Pt-Nb-doped-TiO 2 catalyst showed that the Pt particle size grew from 3nm to 6nm and the Nb(IV) and Ti(III) in the support were oxidized to Nb(V) and Ti(IV) after the durability test. Thus, the improvement in Pt/Nb-TiO 2 ECSA retention was attributed to the lower extent of particle growth and lack of oxidative support loss upon oxidation as compared to Pt/C. The oxygen reduction reaction (ORR) performance was characterized by linear polarization using a rotating disk electrode (RDE). The electrochemical surface areas of Pt/Nb-TiO 2 and Pt/C were found to be 48m2·g -1 and 83m2·g -1 respectively, and the mass activity for the ORR at 0.9V vs. RHE were found to be 150 mA·mg-1Pt and 124 mA·mg-1Pt respectively. The improved mass activity on Pt/Nb-TiO 2 was attributed to strong metal support interaction (SMSI) between the Nb-TiO 2 support and the Pt catalyst based on the 625 meV decrease in the binding energy of the Pt4f x-ray photo-electron spectroscopy (XPS) peaks of Pt/Nb-TiO 2 compared to Pt/C. To quantify the impact of the SMSI, a kinetic model was applied to calculate the elementary reaction rate constants for the various steps of the ORR on both catalysts. The reaction rate constant (k1) for the direct 4-electron transfer pathway to produce H 2 O was significantly larger in Pt/Nb-TiO 2 as compared to Pt/C. Thus, the reduction in the electron binding energy as observed in the XPS was found to aid the facile filling of the higher energy 2p orbitals of O 2 thereby leading to improved 4-electron transfer kinetics and improved overall activity.

08 HYDROGEN↗
DOE OSTI2023

Rapid Postgrafting Reaction to Prepare Quaternized Polycarbazoles

We report a rapid postgrafting reaction to prepare alkyl ammonium functionalized polycarbazoles from a commercially available monomer. This novel synthetic approach provides benefit to preparing the high molecular weight quaternized polycarbazoles within 1 h of Friedel–Crafts polycondensation, avoiding the synthesis and purification step to prepare a functionalized monomer. The postgrafting reaction produces hexyl alkyl ammonium functionalized polycarbazole with 100% grafting degree. However, the postgrafting reaction produced only 60% grafting with propyl alkyl ammonium due to the competitive elimination reaction because of the higher acidity of β-hydrogen in the propyl alkyl group resulting from the proximity of the bromide and ammonium groups. The hexyl alkyl ammonium functionalized polycarbazole has a high hydroxide conductivity of 103 mS cm –1 at 80 °C and showed excellent alkaline stability with less than 3% loss of ion group after 1 M NaOH treatment at 80 °C for 500 h. In conclusion, this study highlights that the postgrafting reaction provides a pathway for the scale-up synthesis of quaternized aryl ether-free polyaromatics.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗
DOE OSTI2023

Elucidating electrochemical nitrate and nitrite reduction over atomically-dispersed transition metal sites

Abstract Electrocatalytic reduction of waste nitrates (NO 3 − ) enables the synthesis of ammonia (NH 3 ) in a carbon neutral and decentralized manner. Atomically dispersed metal-nitrogen-carbon (M-N-C) catalysts demonstrate a high catalytic activity and uniquely favor mono-nitrogen products. However, the reaction fundamentals remain largely underexplored. Herein, we report a set of 14; 3 d -, 4 d -, 5 d - and f -block M-N-C catalysts. The selectivity and activity of NO 3 − reduction to NH 3 in neutral media, with a specific focus on deciphering the role of the NO 2 − intermediate in the reaction cascade, reveals strong correlations (R=0.9) between the NO 2 − reduction activity and NO 3 − reduction selectivity for NH 3 . Moreover, theoretical computations reveal the associative/dissociative adsorption pathways for NO 2 − evolution, over the normal M-N 4 sites and their oxo-form (O-M-N 4 ) for oxyphilic metals. This work provides a platform for designing multi-element NO 3 RR cascades with single-atom sites or their hybridization with extended catalytic surfaces.

36 MATERIALS SCIENCE↗
DOE OSTI2023

Electrochemical phenyl oxidation: A limiting factor of oxygen evolution reaction in water electrolysis

This mini review explains the electrochemical phenyl oxidation of ionomers in the anode catalyst layers of the water electrolyzer that significantly impacts the performance and durability of the device. Although the relevant studies on phenyl oxidation on platinum group metal-free catalysts under high electrode potential are scarce, several studies with platinum group metal catalysts indicated that the impact of electrochemical phenyl oxidation can be profound. In the first part, this review summarizes ionomer-catalyst interactions that impact alkaline electrochemical devices, emphasizing the importance of minimizing interactions between the phenyl moiety of ionomers and oxygen evolution reaction catalysts. In the second part, we discuss the adsorption energies of phenyl groups found in ionomer fragments on different oxygen evolution catalysts. Finally, the mitigation strategies of electrochemical phenyl oxidation for advanced water electrolyzers are briefly discussed at the end of the review.

25 ENERGY STORAGE↗
DOE OSTI2022

High Temperature Polymer Electrolyte Membrane Fuel Cells with High Phosphoric Acid Retention

Phosphoric acid loss poses immense hurdles for the durability of high-temperature polymer electrolyte membrane fuel cells (HT-PEMFCs). Here we report quaternary ammonium-biphosphate ion-pair HT-PEMFCs that do not lose phosphoric acids under normal and accelerated stress conditions. Additionally, our energetics study explains the acid loss behavior of the conventional phosphoric acid-polybenzimidazole (PA-PBI) system by two mechanisms. If PA loss occurs via acid evaporation, the acid loss is constant over time. On the other hand, when water activity in the PA-PBI system is high, exponential decay of PA loss occurs via the water replacement mechanism. Combined 31 P NMR and computational studies show that the proposed ion-pair system has six times higher interaction energy, which allows for containing all PAs in the membrane electrode assemblies under a broad range of operating conditions. In addition, polar interactions between the phosphonic acid ionomer and phosphoric acid explain acid retention in the electrodes of the ion-pair HT-PEMFCs.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗
DOE OSTI2022

Modelling single atom catalysts for water splitting and fuel cells: A tutorial review

Here, in this tutorial review, we report the state-of-the-art of the modeling approaches of Single Atom Catalysts (SAC) for water splitting and fuel cells reactions. The discussion applies for Hydrogen Evolution Reaction (HER), Oxygen Reduction Reaction (OER), Hydrogen Oxidation Reaction (HOR), and Oxygen Reduction Reaction (ORR). The main scope of this work is to underline the relevant aspects of SACs modelling. On the one hand, the review could help computational chemists aiming to start the study of SACs. On the other hand, experimentalists could find the critical analysis of DFT results of interest to understand better the strengths and weaknesses of simulations, and how to interpret computational results. After an introductory section of SACs, we start by briefly presenting the state-of-the-art methodologies. Then, we analyze the critical aspects for a reliable prediction of the electronic properties, and we discuss the robustness of the structural models and ways to validate them. Furthermore, we discuss the main approaches to predict catalytic activity and selectivity, which is the final goal of the computational catalysis. We conclude this review with a critical analysis of the current challenges in the field, and the main limitations of the modeling approaches that are described.

25 ENERGY STORAGE↗
DOE OSTI2022

Phenyl‐Free Polynorbornenes for Potential Anion Exchange Ionomers for Fuel Cells and Electrolyzers

Abstract Ionomers in the catalyst layer play a critical role in the performance of fuel cells and electrolyzers. Phenyl adsorption on hydrogen oxidation catalysts and electrochemical oxidation of phenyl moieties on oxygen evolution catalysts are detrimental to the alkaline devices’ performance. Here the adsorption energy of phenyl‐containing ionomers is compared to provide the rationale for implementing phenyl‐free ionomers. Density functional theory calculations indicated that the norbornane fragment has minimal adsorption energy on Pt(111) due to the absence of aromatic π electrons. A soluble quaternized polynorbornene ionomer is prepared by vinyl addition polymerization, and it exhibits high performance in both fuel cells and electrolyzers, proving the advantage of the phenyl‐free structure. This study establishes the phenyl adsorption energy‐electrode performance relationship, highlighting the importance of material interactions between the catalysts and ionomers.

25 ENERGY STORAGE↗
DOE OSTI2022

Mitigating cerium migration for perfluorosulfonic acid membranes using organic ligands

Improving the electrochemical stability of proton exchange membranes is a pressing priority for heavy-duty fuel cell vehicles. The lifetime of the most widely used perfluorosulfonic acid membranes is limited by reactive free radicals generated inside the system. Cerium has been found to reduce the chemical degradation of the membranes. However, cerium migration during fuel cell operation limits the chemical durability enhancement effect expected from the radical scavenging activity of cerium. Here we investigate a wide range of organic immobilizers for cerium, measuring their suitability concerning cerium retention, radical scavenging activity, and fuel cell performance. Further, we report that partially fluorinated phosphonic acids enhance cerium retention up to 45 times and reduce fluoride emission rate by 38% compared to the commercial Nafion™ XL membrane pre-impregnated with cerium. The energetics of cerium-phosphonic acid complex systems by density functional theory calculations rationalizes effective cerium immobilization.

25 ENERGY STORAGE↗
DOE OSTI2022

Robust palladium hydride catalyst for electrocatalytic formate formation with high CO tolerance

Palladium is unique in the electrocatalytic reduction of CO 2 to formate because of its low or even near-equilibrium onset potential. However, the inevitably produced CO molecules poison and deactivate the catalyst surface, resulting in an insufficient operating lifetime (<30 min) for conventional and optimized Pd catalysts. In this work, we present a hydrogen-rich Palladium hydride catalyst (PdH0.5/C) derived from a one-step solvothermal synthesis. This catalyst showed a 93.1 % faradaic efficiency towards formate at – 0.4 V (vs RHE). The working lifetime reached a record of 4 h, which was ~15 times longer than a commercial Pd catalyst and outperformed all previous Pd-based electrocatalysts for CO 2 -HCOO – conversion. The high CO tolerance was attributed to the selectivity improvement induced by lattice hydrogen and the weak CO adsorption strength on diverse active sites (i.e. kink, step, and terrace). Isotopic analysis revealed a direct participation of the lattice hydrogen in the protonation of CO 2 molecules in formate formation.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗
DOE OSTI2022

Protonated phosphonic acid electrodes for high power heavy-duty vehicle fuel cells

We report that state-of-the-art automotive fuel cells that operate at about 80 °C require large radiators and air intakes to avoid overheating. High-temperature fuel cells that operate above 100 °C under anhydrous conditions provide an ideal solution for heat rejection in heavy-duty vehicle applications. Here we report protonated phosphonic acid electrodes that remarkably improve the performance of high-temperature polymer electrolyte membrane fuel cells. The protonated phosphonic acids comprise tetrafluorostyrene-phosphonic acid and perfluorosulfonic acid polymers, where a perfluorosulfonic acid proton is transferred to the phosphonic acid to enhance the anhydrous proton conduction of fuel cell electrodes. By using this material in fuel cell electrodes, we obtained a fuel cell exhibiting a rated power density of 780 mW cm -2 at 160 °C, with minimal degradation during 2,500 h of operation and 700 thermal cycles from 40 to 160 °C under load.

25 ENERGY STORAGE↗
DOE OSTI2021

Self-Anchored Platinum-Decorated Antimony-Doped-Tin Oxide as a Durable Oxygen Reduction Electrocatalyst

The lifetime of commercial Proton Exchange Membrane Fuel Cells (PEMFCs) is circumscribed by the insufficient durability of commercial catalysts. The use of metal oxide supports in place of carbon significantly increases electrocatalyst durability. Herein, following density functional theory (DFT) predictions of improved Platinum (Pt) stability on antimony doped tin oxide (ATO) supports, we synthesized ATO whose morphology and crystal structure was engineered using a Pt anchoring technique. X-ray photoelectron spectroscopy (XPS) indicated that the Pt anchor sites aided in the reduction of Pt precursors to Pt on the ATO surface. X-ray absorption near-edge spectroscopy (XANES) revealed the existence of strong-metal-support interactions (SMSI) between Pt and ATO. The combination of SMSI and high control over Pt dispersion enabled the Pt/Pt-aerogel-ATO (Pt supported on aerogel ATO with Pt anchor sites) electrocatalyst to achieve 2x the area specific activity of Pt/C in ex-situ testing. In a H 2 /air PEMFC Pt/Pt-aerogel-ATO cathodes enabled 20% higher peak power density and <1/6 the loss of active surface area as compared to Pt/C. Notably, in a PEMFC under rigorous potential cycling, the Pt/Pt-aerogel-ATO retained its initial peak power density as opposed to a 58% loss for Pt/C. Further, cost models indicate that Pt/Pt-aerogel-ATO is 26% less expensive than Pt/C over its useful lifetime.

25 ENERGY STORAGE↗
DOE OSTI2020

Synergistically integrated phosphonated poly(pentafluorostyrene) for fuel cells

Modern electrochemical energy conversion devices require more advanced proton conductors for their broad applications. Phosphonated polymers have been proposed as anhydrous proton conductors for fuel cells. However, the anhydride formation of phosphonic acid functional groups lowers proton conductivity and this prevents the use of phosphonated polymers in fuel cell applications. Here, we report a poly(2,3,5,6-tetrafluorostyrene-4-phosphonic acid) that does not undergo anhydride formation and thus maintains protonic conductivity above 200 °C. We use the phosphonated polymer in fuel cell electrodes with an ion-pair coordinated membrane in a membrane electrode assembly. We find that this synergistically integrated fuel cell reached peak power densities of 1,130 mW cm -2 at 160 °C and 1,740 mW cm -2 at 240 °C under H2/O2 conditions, substantially outperforming polybenzimidazole- and metal phosphate-based fuel cells. Our result indicates a pathway towards using phosphonated polymers in high-performance fuel cells under hot and dry operating conditions.

25 ENERGY STORAGE↗
DOE OSTI2020

Identification of durable and non-durable FeN x sites in Fe–N–C materials for proton exchange membrane fuel cells

We report that while Fe–N–C materials are a promising alternative to platinum for catalysing the oxygen reduction reaction in acidic polymer fuel cells, limited understanding of their operando degradation restricts rational approaches towards improved durability. Here we show that Fe–N–C catalysts initially comprising two distinct FeN x sites (S1 and S2) degrade via the transformation of S1 into iron oxides while the structure and number of S2 were unmodified. Structure–activity correlations drawn from end-of-test 57 Fe Mössbauer spectroscopy reveal that both sites initially contribute to the oxygen reduction reaction activity but only S2 substantially contributes after 50 h of operation. From in situ 57 Fe Mössbauer spectroscopy in inert gas coupled to calculations of the Mössbauer signature of FeN x moieties in different electronic states, we identify S1 to be a high-spin FeN 4 C 12 moiety and S2 a low- or intermediate-spin FeN 4 C 10 moiety. These insights lay the groundwork for rational approaches towards Fe–N–C cathodes with improved durability in acidic fuel cells.

36 MATERIALS SCIENCE↗
DOE OSTI2020

Facile All-Optical Method for In Situ Detection of Low Amounts of Ammonia

As a key precursor for nitrogenous compounds and fertilizer, ammonia affects our lives in numerous ways. Rapid and sensitive detection of ammonia is essential, both in environmental monitoring and in process control for industrial production. Here we report a novel and nonperturbative method that allows rapid detection of ammonia at low concentrations, based on the all-optical detection of surface-enhanced Raman signals. We show that this simple and affordable approach enables ammonia probing at selected regions of interest with high spatial resolution, making in situ and operando observations possible.

09 BIOMASS FUELS↗
DOE OSTI2020

Energetics of Base–Acid Pairs for the Design of High-Temperature Fuel Cell Polymer Electrolytes

The interaction energy of base–acid plays a key role in acid retention of phosphoric acid (PA)-doped polymer electrolytes under fuel cell operating conditions. Here, we investigate the energetics of proton-accepting and hydroxide-donating organic bases using density functional theory calculations. Because of their weak basicity, proton-accepting organic bases such as benzimidazole have relatively low interaction energy with the acid in the absence of water (15.3–28.0 kcal mol –1 ). Energetics of the proton-accepting base–PA complex increases by adding water, indicating that the interactions in the base–acid complex strengthen in the presence of water. On the other hand, hydroxide-donating organic bases, such as tetramethylammonium hydroxide, have high interaction energy with PA (~110 kcal mol –1 ), which remains high in the presence of water. The chemical shifts of 31P NMR support the energetics of the base–acid complexes. Overall, this study further discusses the benefit of incorporating hydroxide-donating organic bases into the polymeric structure over proton-accepting bases as a way to increase acid retention.

25 ENERGY STORAGE↗
DOE OSTI2020

Assessing Stability of Transition Metal Nitrides in Aqueous Environments: The Case of Molybdenum, Iron, Vanadium and Nickel Nitride

Analysis of the MoN, Mo 2 N, VN, Fe 2 N, Fe 4 N, Ni 3 N stability in the aqueous media was performed based on the thermodynamic data available in HSC Chemistry software. Our analysis show that among all the studied nitrides, cubic Mo 2 N is the most resistant while cubic VN is the least resistant to oxidation and decomposition. The change in temperature up to 100 °C does not significantly influence the formation potentials of transition metal oxides from nitrides; however, pH significantly affects the stability of the studied transition metal nitrides. In the case of Mo 2 N, MoN, and VN changing pH from acidic to neutral and alkaline decreases the stability of the nitrides and the oxide formation potentials shift to more negative values. Additionally, based on thermodynamics, orthorhombic Fe 2 N should be stable only in alkaline conditions, while cubic Fe 4 N and hexagonal Ni 3 N should be the most stable at pH ~ 7 and pH ~ 9. Changing pH from these values decreases the stability of both Fe 4 N and Ni 3 N and the formation of oxy-, hydroxy- species becomes thermodynamically more favorable. Overall, the limited stability of the metal nitrides places severe constraints for their use in aqueous electrocatalytic applications.

36 MATERIALS SCIENCE↗