NASA NTRS2018

Evaluations of Candidate Materials for Advanced Space-Rated Vacuum Seals to Explore Space Environment Exposure Limits

For many materials used in space hardware, the environment in which they need to operate is harsher than the environment on earth. Exposure to vacuum conditions, atomic oxygen, and ultraviolet radiation can be detrimental, so testing of space hardware in simulated space environments is required. This is especially true for elastomeric components such as seals. NASA is developing advanced space-rated vacuum seals in support of future space exploration missions. These seals must exhibit extremely low leak rates to ensure that astronauts have sufficient breathable air during extended-duration missions. In some applications the seals are not mated during portions of the mission and are left uncovered and exposed to the conditions in space for prolonged periods of time prior to mating. Space-rated vacuum seals are often made of silicone because of the material's wide operating temperature range and ability to be molded or extruded into various shapes and cross sections. One approach being considered to achieve improved performance is to add titanium dioxide to the silicone material to make it more resistant to damage from ultraviolet radiation. In this study, seals made of the baseline material with and without 1.5% titanium dioxide additive (by weight) were exposed to atomic oxygen and increasing levels of ultraviolet radiation and then leak tested. Test results revealed that seals made of the new material could withstand longer exposures while still satisfying the leak rate requirement even under worst-case conditions of partial compression at the extremes of the anticipated operating temperature range.

Ultraviolet radiation↗

NASA NTRS2018

Evaluations of Candidate Materials for Advanced Space-Rated Vacuum Seals to Explore Space Environment Exposure Limits

For many materials used in space hardware, the environment in which they need to operate is harsher than the environment on earth. Exposure to vacuum conditions, atomic oxygen, and ultraviolet radiation can be detrimental, so testing of space hardware in simulated space environments is required. This is especially true for elastomeric components such as seals. NASA is developing advanced space-rated vacuum seals in support of future space exploration missions. These seals must exhibit extremely low leak rates to ensure that astronauts have sufficient breathable air during extended-duration missions. In some applications the seals are not mated during portions of the mission and are left uncovered and exposed to the conditions in space for prolonged periods of time prior to mating. Space-rated vacuum seals are often made of silicone because of the material's wide operating temperature range and ability to be molded or extruded into various shapes and cross sections. One approach being considered to achieve improved performance is to add titanium dioxide to the silicone material to make it more resistant to damage from ultraviolet radiation. In this study, seals made of the baseline material with and without 1.5 percent titanium dioxide additive (by weight) were exposed to atomic oxygen and increasing levels of ultraviolet radiation and then leak tested. Test results revealed that seals made of the new material could withstand longer exposures while still satisfying the leak rate requirement even under worst-case conditions of partial compression at the extremes of the anticipated operating temperature range.

Seals↗

NASA NTRS2017

Validation of Test Methods for Air Leak Rate Verification of Spaceflight Hardware

As deep space exploration continues to be the goal of NASAs human spaceflight program, verification of the performance of spaceflight hardware becomes increasingly critical. Suitable test methods for verifying the leak rate of sealing systems are identified in program qualification testing requirements. One acceptable method for verifying the air leak rate of gas pressure seals is the tracer gas leak detector method. In this method, a tracer gas (commonly helium) leaks past the test seal and is transported to the leak detector where the leak rate is quantified. To predict the air leak rate, a conversion factor of helium-to-air is applied depending on the magnitude of the helium flow rate. The conversion factor is based on either the molecular mass ratio or the ratio of the dynamic viscosities. The current work was aimed at validating this approach for permeation-level leak rates using a series of tests with a silicone elastomer O-ring. An established pressure decay method with constant differential pressure was used to evaluate both the air and helium leak rates of the O-ring under similar temperature and pressure conditions. The results from the pressure decay tests showed, for the elastomer O-ring, that neither the molecular flow nor the viscous flow helium-to-air conversion factors were applicable. Leak rate tests were also performed using nitrogen and argon as the test gas. Molecular mass and viscosity based helium-to-test gas conversion factors were applied, but did not correctly predict the measured leak rates of either gas. To further this study, the effect of pressure boundary conditions was investigated. Often, pressure decay leak rate tests are performed at a differential pressure of 101.3 kPa with atmospheric pressure on the downstream side of the test seal. In space applications, the differential pressure is similar, but with vacuum as the downstream pressure. The same O-ring was tested at four unique differential pressures ranging from 34.5 to 137.9 kPa. Up to six combinations of upstream and downstream pressures for each differential pressure were compared. For a given differential pressure, the various combinations of upstream and downstream dry air pressures did not significantly affect the leak rate. As expected, the leak rate of the O-ring increased with increasing differential pressure. The results suggested that the current leak test pressure conditions, used to verify spacecraft sealing systems with elastomer seals, produce accurate values even though the boundary conditions do not model the space application.

helium leak detector↗

NASA NTRS2016

Evaluation of a Conductive Elastomer Seal for Spacecraft

An electrically conductive elastomer was evaluated as a material candidate for a spacecraft seal. The elastomer used electrically conductive constituents as a means to reduce the resistance between mating interfaces of a sealed joint to meet spacecraft electrical bonding requirements. The compound's outgassing levels were compared against published NASA requirements. The compound was formed into a hollow O-ring seal and its compression set was measured. The O-ring seal was placed into an interface and the electrical resistance and leak rate were quantified. The amount of force required to fully compress the test article in the sealing interface and the force needed to separate the joint were also measured. The outgassing and resistance measurements were below the maximum allowable levels. The room temperature compression set and leak rates were fairly high when compared against other typical spacecraft seal materials, but were not excessive. The compression and adhesion forces were desirably low. Overall, the performance of the elastomer compound was sufficient to be considered for future spacecraft seal applications.

Daniels, Christopher C.↗

NASA NTRS2015

Leak Rate Quantification Method for Gas Pressure Seals with Controlled Pressure Differential

An enhancement to the pressure decay leak rate method with mass point analysis solved deficiencies in the standard method. By adding a control system, a constant gas pressure differential across the test article was maintained. As a result, the desired pressure condition was met at the onset of the test, and the mass leak rate and measurement uncertainty were computed in real-time. The data acquisition and control system were programmed to automatically stop when specified criteria were met. Typically, the test was stopped when a specified level of measurement uncertainty was attained. Using silicone O-ring test articles, the new method was compared with the standard method that permitted the downstream pressure to be non-constant atmospheric pressure. The two methods recorded comparable leak rates, but the new method recorded leak rates with significantly lower measurement uncertainty, statistical variance, and test duration. Utilizing this new method in leak rate quantification, projects will reduce cost and schedule, improve test results, and ease interpretation between data sets.

seal↗

NASA NTRS2015

Elastomeric Seal Performance after Terrestrial Ultraviolet Radiation Exposure

Ultraviolet radiation was evaluated to determine its negative effects on the performance of elastomeric gas pressure seals. The leak rates of the silicone elastomer S0383-70 O-ring test articles were used to quantify the degradation of the seals after exposure to vacuum-ultraviolet and/or middle-to-near-ultraviolet wavelength radiation. Three groups of seals were exposed in terrestrial facilities to 115-165 nm wavelength radiation, 230-500 nm wavelength radiation, or both spectrums, for an orbital spaceflight equivalent of 125 hours. The leak rates of the silicone elastomer S0383-70 seals were quantified and compared to samples that received no radiation. Each lot contained six samples and statistical t-tests were used to determine the separate and combined influences of exposure to the two wavelength ranges. A comparison of the mean leak rates of samples exposed to 115-165 nm wavelength radiation to the control specimens showed no difference, suggesting that spectrum was not damaging. The 230-500 nm wavelength appeared to be damaging, as the mean leak rates of the specimens exposed to that range of wavelengths, and those exposed to the combined 115-165 nm and 230-500 nm spectrums, were significantly different from the leak rates of the control specimens. Most importantly, the test articles exposed to both wavelength spectrums exhibited mean leak rates two orders of magnitude larger than any other exposed specimens, which suggested that both wavelength spectrums are important when simulating the orbital environment.

leakage↗

NASA NTRS2015

Helium Mass Spectrometer Leak Detection: A Method to Quantify Total Measurement Uncertainty

In applications where leak rates of components or systems are evaluated against a leak rate requirement, the uncertainty of the measured leak rate must be included in the reported result. However, in the helium mass spectrometer leak detection method, the sensitivity, or resolution, of the instrument is often the only component of the total measurement uncertainty noted when reporting results. To address this shortfall, a measurement uncertainty analysis method was developed that includes the leak detector unit's resolution, repeatability, hysteresis, and drift, along with the uncertainty associated with the calibration standard. In a step-wise process, the method identifies the bias and precision components of the calibration standard, the measurement correction factor (K-factor), and the leak detector unit. Together these individual contributions to error are combined and the total measurement uncertainty is determined using the root-sum-square method. It was found that the precision component contributes more to the total uncertainty than the bias component, but the bias component is not insignificant. For helium mass spectrometer leak rate tests where unit sensitivity alone is not enough, a thorough evaluation of the measurement uncertainty such as the one presented herein should be performed and reported along with the leak rate value.

error analysis↗