Material flammability is an important factor in determining the pressure and composition (fraction of oxygen and nitrogen) of the atmosphere in the habitable volume of exploration vehicles and habitats. The method chosen in this work to quantify the flammability of a material is by its ease of ignition. The ignition delay time was defined as the time it takes a combustible material to ignite after it has been exposed to an external heat flux. Previous work in the Forced Ignition and Spread Test (FIST) apparatus has shown that the ignition delay in the currently proposed space exploration atmosphere (approximately 58.6 kPa and32% oxygen concentration) is reduced by 27% compared to the standard atmosphere used in the Space Shuttle and Space Station. In order to determine whether there is a safer environment in terms of material flammability, a series of piloted ignition delay tests using polymethylmethacrylate (PMMA) was conducted in the FIST apparatus to extend the work over a range of possible exploration atmospheres. The exploration atmospheres considered were the normoxic equivalents, i.e. reduced pressure conditions with a constant partial pressure of oxygen. The ignition delay time was seen to decrease as the pressure was reduced along the normoxic curve. The minimum ignition delay observed in the normoxic equivalent environments was nearly 30% lower than in standard atmospheric conditions. The ignition delay in the proposed exploration atmosphere is only slightly larger than this minimum. Interms of material flammability, normoxic environments with a higher pressure relative to the proposed pressure would be desired.

Ignition delay time↗

NASA NTRS2008

Effect of Pressure on Piloted Ignition Delay of PMMA

In order to reduce the risk of decompression sickness associated with spacewalks, NASA is considering designing the next generation of exploration vehicles and habitats with a different cabin environment than used previously. The proposed environment uses a total cabin pressure of 52.7 to 58.6 kPa with an oxygen concentration of 30 to 34% by volume and was chosen with material flammability in mind. Because materials may burn differently under these conditions and there is little information on how this new environment affects the flammability of the materials onboard, it is important to conduct material flammability experiments at the intended exploration atmosphere. One method to evaluate material flammability is by its ease of ignition. To this end, piloted ignition delay tests were conducted in the Forced Ignition and Spread Test (FIST) apparatus subject to this new environment. In these tests, polymethylmethacylate (PMMA) was exposed to a range of oxidizer flow velocities and externally applied heat fluxes. The ultimate goal is to determine the individual effect of pressure and the combined effect of pressure and oxygen concentration on the ignition delay. Tests were conducted for a baseline case of normal pressure and oxygen concentration, low pressure (58.6 kPa) with normal oxygen (21%). Future work will focus on low pressure with 32% oxygen concentration (space exploration atmosphere - SEA) conditions. It was found that reducing the pressure while keeping the oxygen concentration at 21% reduced the ignition time by 17% on average. It was also noted that the critical heat flux for ignition decreases in low-pressure conditions. Because tests conducted in standard atmospheric conditions will underpredict the flammability of materials intended for use on spacecraft, fire safety onboard at exploration atmospheres may be compromised.

McAllister, Sara↗

NASA NTRS2007

Piloted Ignition Delay of PMMA in Space Exploration Atmospheres

In order to reduce the risk of decompression sickness associated with extravehicular activity (EVA), NASA is designing the next generation of exploration vehicles and habitats with a different cabin environment than used previously. The proposed environment uses a total cabin pressure of 52.7 to 58.6 kPa with an oxygen concentration of 30 to 34% by volume and was chosen with material flammability in mind. Because materials may burn differently under these conditions and there is little information on how this new environment affects the flammability of the materials onboard, it is important to conduct material flammability experiments at the intended exploration atmosphere. One method to evaluate material flammability is by its ease of ignition. To this end, piloted ignition delay tests were conducted in the Forced Ignition and Spread Test (FIST) apparatus subject to this new environment. In these tests, polymethylmethacylate (PMMA) was exposed to a range of oxidizer flow velocities and externally applied heat fluxes. Tests were conducted for a baseline case of normal pressure and oxygen concentration, low pressure (58.6 kPa) with normal oxygen (21%), and low pressure with 32% oxygen concentration conditions to determine the individual effect of pressure and the combined effect of pressure and oxygen concentration on the ignition delay. It was found that reducing the pressure while keeping the oxygen concentration at 21% reduced the ignition time by 17% on average. Increasing the oxygen concentration at low pressures reduced the ignition time by an additional 10%. It was also noted that the critical heat flux for ignition decreases at exploration atmospheres. These results show that tests conducted in standard atmospheric conditions will underpredict the ignition of materials intended for use on spacecraft and that, at these conditions, materials are more susceptible to ignition than at current spacecraft atmospheres.

McAllister, Sara↗