Report summarizing demonstration of thermal conductivity measurement methods for coated zirconium cladding
Thermal diffusivity measurements on Zirconium-based cladding materials have historically been a challenge due to the difficulty to measure on specimens with curved geometries, including nuclear grade Zircaloy cladding materials. In this work, we first used Laser Flash Analysis methods to measure the thermal diffusivity of Zircaloy tubes, which show good agreement with Zircaloy plates in this work, as well as previously published data. The consistent results proved the applicability of the Laser Flash Analysis setup for investigating thermal diffusivity of Zircaloy tubes. We further investigate the hydrogen effect on thermal diffusivity of Zircaloy tubes. Hydrogen plays significant roles in temperature dependent thermal diffusivity trends of Zircaloy tube. For low hydrogen concentration, where hydride dissolved into single phase α-Zr at higher temperature, thermal diffusivity is relatively unchanged at low temperature at two phase regions (α-Zr and δ-hydride), and it increases as a function of temperature at single phase α-Zr region. For high hydrogen concentration, where phase transformation (α-Zr + δ-hydride → α-Zr + β-Zr) occurs at 567 °C, thermal diffusivity decreases as a function of temperature below 567 °C before the transformation (α-Zr and δ-hydride), while increase at higher temperature after the transformation (α-Zr and β-Zr).