3 records

DOE OSTI2024

Antimony Chloride Treatments of CdTe-Based Solar Cells

Development of a new SbCl3-based solution treatment for chloride activation of CdTe-based solar cells is described. Activation was confirmed with CdSeTe:Sb devices exhibiting VOC > 550 mV and JSC > 25 mAcm-2. Treatment optimization showed strong effects of annealing time and temperature on cell properties. Material characterization indicated surface conversion of CdSeTe to CdCl2 and Sb2Te3 with SbCl3 treatment. However, no reaction products were formed with treatment under inert conditions, which was coupled with poor device performance. Drying the SbCl3 films at controlled humidity conditions confirmed that exposure to high relative humidity is critical for CdSeTe activation, through hydrolysis of SbCl3. Mechanistic details of SbCl3 speciation during hydrolysis and annealing to activate CdSeTe are discussed.

14 SOLAR ENERGY↗

DOE OSTI2021

Distinguishing bulk and surface recombination in CdTe thin films and solar cells using time-resolved terahertz and photoluminescence spectroscopies

Understanding the nature of recombination and its dependence on defects and interfaces is essential for engineering materials and contacts for higher open circuit voltage (V oc ) and power conversion efficiency in photovoltaic (PV) devices. Time-resolved photoluminescence (TRPL) has conventionally been used to evaluate recombination, but carrier redistribution often dominates the response at short times. In this work, we report on the quantification of carrier dynamics and recombination mechanisms by complementary use of both time-resolved terahertz spectroscopy (TRTS) and TRPL combined with numerical modeling of the continuity equations and Poisson’s equation. We have demonstrated this approach using CdTe thin films. A thin film stack with CdTe fabricated by vapor transport deposition and treated with CdCl 2 exhibited a bulk lifetime of 1.7 ± 0.1 ns, negligible CdTe/CdS interface recombination velocity, and back surface recombination velocity of 6.3 ± 1.3 x10 4 cm/s. In contrast, a film stack without CdCl 2 treatment had a bulk lifetime of only 68 ± 12 ps and a higher interface recombination velocity of 4 ± 2 x10 8 cm/s. By determining the locus and mechanisms of performance-limiting recombination, we can accelerate the development of thin-film PVs with higher V oc and efficiency. While the method has been demonstrated here using CdTe, it is also applicable to perovskites, Cu(InGa)Se 2 , Cu2ZnSn(S,Se) 4, and emerging technologies.

14 SOLAR ENERGY↗

DOE OSTI2021

Quantifying Bulk and Surface Recombination in CdTe Solar Cells Using Time-Resolved Terahertz Spectroscopy

Understanding the nature of recombination mechanisms is essential for higher power conversion efficiency in photovoltaic (PV) devices. Here we use a combination of time-resolved terahertz spectroscopy and numerical modeling to determine the bulk Shockley-Read-Hall lifetime and interface and back surface recombination velocities in CdTe thin film stacks. Furthermore, the measurement was facilitated by fabricating wire-grid device structures using conventional laser scribing. Evaluation of a glass/FTO/SnO2/CdS/CdTe stack treated with CdCl2 allowed separation of the CdTe absorber bulk lifetime, 1.6 ns, from the back surface recombination velocity, ~6x10 4 cm/s, and indicated that CdTe/CdS interface recombination velocity had no significant impact on carrier dynamics.

14 SOLAR ENERGY↗