McCord, Jeffrey | Search NASA

DOE OSTI2024

2024 roadmap on magnetic microscopy techniques and their applications in materials science

Considering the growing interest in magnetic materials for unconventional computing, data storage, and sensor applications, there is active research not only on material synthesis but also characterisation of their properties. In addition to structural and integral magnetic characterisations, imaging of magnetisation patterns, current distributions and magnetic fields at nano- and microscale is of major importance to understand the material responses and qualify them for specific applications. In this roadmap, we aim to cover a broad portfolio of techniques to perform nano- and microscale magnetic imaging using superconducting quantum interference devices, spin centre and Hall effect magnetometries, scanning probe microscopies, x-ray- and electron-based methods as well as magnetooptics and nanoscale magnetic resonance imaging. The roadmap is aimed as a single access point of information for experts in the field as well as the young generation of students outlining prospects of the development of magnetic imaging technologies for the upcoming decade with a focus on physics, materials science, and chemistry of planar, three-dimensional and geometrically curved objects of different material classes including two-dimensional materials, complex oxides, semi-metals, multiferroics, skyrmions, antiferromagnets, frustrated magnets, magnetic molecules/nanoparticles, ionic conductors, superconductors, spintronic and spinorbitronic materials.

2D materials↗

DOE OSTI2021

Spin waves excitation at micron-sized, anisotropy modified regions in amorphous Fe 80 B 20 stripes: Local properties and inter-regions coupling

We report on the measurement of the local magnetization dynamics occurring, at units of GHz, in large aspect ratio stripes lithographed from reduced damping amorphous Fe 80 B 20 films. The stripes were submitted to local anisotropy modifications by micrometric beam synchrotron X-ray irradiation. Our results include data on the dispersion relationships and group velocities corresponding to spin waves excited at both the non-irradiated and the irradiated regions. Whereas in the former case we observed standing spin waves with transverse-to-the stripe axis wave vector, in the latter one, for which the wave vector of the spin waves was parallel-to-the stripe axis, propagating spin waves were excited. In both regions, we measured the effective propagation distance of the spin waves, which resulted to be independent of the wave vector orientation. In the spin waves excited at the irradiated region, we also measured the decay time and effective damping coefficient, which was in good agreement with previously reported values obtained from FMR measurements in amorphous Fe 80 B 20 continuous films. We show that the interaction of the non-irradiated and irradiated zones results, at the stripe transverse saturation remanence and under an exciting field frequency of 4 GHz, in the introduction of a π phase shift between the standing spin waves excited at both sides of the irradiated region. This result opens the possibility of using the local, transverse to the stripe axis, magnetic anisotropy easy axis induced by the X-ray irradiation as a crucial constituent of a zero-applied field spin wave phase-shifter.

36 MATERIALS SCIENCE↗