DOE OSTI2021

Effects of Casting Parameters and Impurity Concentrations on As-Cast U–10Mo

This work investigates the effects of casting parameter changes on as-cast uranium-10 wt% molybdenum alloys on a 1-2kg scale. A commercial tilt-pour vacuum induction melting system was utilized to study the effects of casting atmosphere, total heating time, hold time at maximum temperature, mold temperature, and crucible type on the as-cast microstructure of U-10Mo. Ten thin plates (5.08 mm thick) and four thick plates (25.4 mm and 63.5 mm thick) were cast and analyzed for carbon, oxygen, hydrogen, and nitrogen impurities. Additionally, molybdenum content and primary dendrite length (PDL) of the microstructure was quantified. A statistical evaluation was performed to identify key carbon and oxygen relationships with operating parameters, impurities, and primary dendrite length. Additional factors investigated include: crucible material, time at maximum temperature, total heating time, and pour temperature. Zirconia crucibles reduced carbon content on average by 35%. Additionally, there was a significant statistical association between carbon and oxygen content, between oxygen content and maximum temperature hold time, between mold temperature and PDL, and between PDL, maximum temperature hold time and mold temperature.

Huber, Zachary F.↗
DOE OSTI2021

Enhancing isotope mixing in U-10Mo downblend castings with electromagnetic stirring

Uranium alloyed with 10 wt percent molybdenum (U-10Mo) is the proposed fuel for use in the United States’ high-performance research reactors. The U-10Mo fuel is fabricated by a two-step casting process that downblends highly enriched uranium with depleted uranium (DU) and/or natural uranium (NU) and subsequently alloys the resulting high-assay low-enriched uranium (HALEU) with Mo. Currently, a two-step casting process is needed to meet the ingots’ U-235 enrichment homogeneity specifications. This work demonstrates the ability to provide more homogeneous U-235 distributions during downblend casting by using zirconia for crucibles rather than graphite. When graphite is used as a crucible, the electromagnetic field produced by the induction heater couples directly with the graphite. Zirconia is nonconducting in this study, and therefore does not couple with the field. The induction field couples directly with the metal, and causes electromagnetic stirring (EMS) in the molten metal pool. Eight downblend casting experiments were carried out in this work. Four were performed with zirconia crucibles and four with graphite crucibles. The U-235 enrichment was measured at nine discrete points in each casting using laser ablation multi-collector inductively coupled mass spectrometry (LA-MC-ICP-MS). The enrichment homogeneity was approximately eight times better in zirconia crucible castings than in graphite crucible castings as measured by the plate enrichment range and enrichment coefficient of variation. The results show a single casting step could be used to meet USHPRR enrichment specifications if electromagnetic stirring is present during casting. A related investigation was carried out to determine whether it is appropriate to measure enrichment on as-cast ingots or whether heat treated specimens should be used to accurately characterize enrichment. The results show that the as-cast microstructure plays a significant role in enrichment homogeneity. It is recommended that all enrichment measurements be done after the homogenization heat treatment typical of U-10Mo processing.

36 MATERIALS SCIENCE↗
DOE OSTI2020

Thermomechanical Processing of Uranium Alloys with 10 and 50 Weight Percent Zirconium

This work focuses on casting and thermomechanical processing for moderate sized (500-1000g) 10% by weight and 50% by weight uranium-zirconium alloys. Three castings of uranium – 10wt% zirconium and a fourth casting of uranium – 50wt% zirconium were completed using different castings processes. The first casting process relied on only induction mixing within the VIM system thereby eliminating the need for an arc-melting feedstock preparation step. The second casting process used the arc-melting process prior for feedstock to the same VIM system. In this study, the induction mixing process alone with a graphite crucible appears insufficient for the fabrication of UZr alloys. Graphite is suitable with the use of master alloy UZr feedstock produced by arc-melting. There was a moderate increase of approximately 100 ppm of carbon within the U10Zr alloys. However, there was a near 1000 ppm increase of carbon in the U50Zr alloy. This carbon content is considered too high for forming processes, and therefore, warrants the use of a ceramic crucible for UZr castings near 50wt% zirconium. Zirconia does not appear suitable for UZr castings near 50wt% zirconium. The use of Beryllia or Thoria may be a more suitable option. However, due to the significantly lower liquidus and lower zirconium content, Zirconia crucibles do appear viable for carbon reduction in the U10Zr system. Two thermomechanical processes are also studied in this work - hot extrusion of the U50Zr system and heat treatment in an argon atmosphere. This work demonstrated that extrusion of the U50Zr alloy near 680°C is a viable choice even with +1000 ppm carbon. Extrusion of the U50Zr system near 630°C was unsuccessful and does not appear viable unless significant force and tooling strength is available. There appears to be a moderate increase in extrudate hardness when compared to as-cast. Heat-treatment reduced the hardness of as-cast alloys in the U10Zr castings as well as resolve some variance in the microstructures. However, for the U50Zr billet that did not successfully extrude at 630°C, heat treatment at 900°C for 96 hours did not have a significant impact on hardness or microstructure.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗