McHenry, M. E.

Publications and source records attributed to McHenry, M. E..

8 records
All sourcesNASA NTRSDOE OSTI
DOE OSTI2022

Nanostructure refinement and phase formation of flash annealed FeNi-based soft magnetic alloys

In this work, the resulting nanocomposite microstructures of FeNi nanocrystallites under different heating and cooling rates (5 °C/min vs 400-500 °C/s) is investigated. Conventional furnace annealing under low heating rates and slow cooling resulted in both BCC α-FeNi and FCC γ-FeNi nanocrystallites with an average grain size on the order of 25-27 nm whereas high heating rates achieved via flash annealing techniques have enabled a dramatically refined microstructure consisting of 5-7 nm grains with FCC γ-FeNi phase and found to be the dominant phase following primary crystallization. Grain size refinement and phase identity optimization yielded low values of coercivities-17 A/m and high permeability similar to 11 x 10 3 measured at 400 Hz/1 kA/m in flash annealed samples at 450 °C for 5 s. The magnetic behavior and the underlying mechanism of optimal soft magnetic properties are discussed in terms of the critical role of the grain size in domain wall pinning and coercivity.

36 MATERIALS SCIENCE↗
DOE OSTI2021

Development of high B s Fe–Ni-based metal amorphous nanocomposite by optimization of glass-forming ability

Thermocalc simulations identified compositions with good glass-forming ability (GFA) by locating minima in liquidus temperature, and solidification range in (Fe 70 Ni 30 ) x (B-Si-Nb) 100-x alloys with x = 82% and x = 85%, increased compared to previously developed x = 80% alloys. 3 compositions in the x = 82% system and 1 in the x = 85% system were successfully cast as amorphous magnetic ribbon. Magnetic properties of as-cast alloys showed improvements in Curie temperature and saturation induction, especially for the 85% alloy. Crystallization behavior in the 85% alloy was determined to occur as a 2-step process. Annealing studies showed (Fe 70 Ni 30 ) 82 Nb 2 Si 0 B 16 and (Fe 70 Ni 30 ) 82 Nb 3 Si 0 B 15 alloys to exhibit low coercivity and high B s with annealing. TEM results show significant crystallization in as-cast ribbon. The (Fe 70 Ni 30 ) 85 Nb 0.5 Si 0 B 14.5 alloy as-cast has small, uniformly distributed grains, allowing a useful nanocrystalline alloy to be produced as cast. Lastly, the parameter ΔT xg , the temperature range in which the material can be thermomechanically processed, was in the range of 12–23 °C.

36 MATERIALS SCIENCE↗
DOE OSTI2021

Nanostructure and compositional segregation of soft magnetic FeNi-based nanocomposites with multiple nanocrystalline phases

Soft magnetic metal amorphous nanocomposite alloys are produced through rapid solidification and thermal annealing yielding nanocrystals embedded within an amorphous precursor. Similar free energies in Co-rich and FeNi-based alloy systems result in multiple nanocrystalline phases being formed during devitrification. Studies of multi-phase crystallization processes have been reported for Co-rich alloys but relatively few have investigated FeNi-based systems. A detailed characterization of compositional partitioning and microstructure of an optimally annealed FeNi-based MANC (Fe 70 Ni 30 ) 80 Nb 4 Si 2 B 14 alloy is presented through complementary high-resolution transmission electron microscopy (HRTEM) and atom probe tomography (APT). HRTEM demonstrates orientation relationships between FCC and BCC nanocrystals, suggesting heterogeneous nucleation of nanocrystals in the amorphous matrix or a cooperative mechanism of nucleation between BCC and FCC nanocrystallites. APT results show evidence for (i) the segregation of Fe and Ni between nanocrystals of different phases, (ii) B partitioning to the amorphous phase, and (iii) an Nb-enriched shell surrounding nanocrystals.

36 MATERIALS SCIENCE↗
DOE OSTI2020

Surface oxidation and crystallization of FeNi-Based soft magnetic nanocrystalline and amorphous nanocomposite alloys

In this work, we present characterization of surface oxidation and crystallization behavior of Metal Amorphous Nanocomposite (MANC) (Fe 70 Ni 30 ) 80 Nb 4 Si 2 B 14 alloys via complementary x-ray diffraction, electron microscopy, and x-ray photoelectron spectroscopy techniques. An adherent amorphous oxide of roughly 15–20 nm in thickness is observed on the wheel side of the ribbon, enriched in Fe relative to Ni and with significant content of Si and Nb as would be expected based upon a comparison of the Gibbs free energy of formation of the stable oxide phases. The amorphous character of the oxide is likely to result from the significant Si-content coupled with the amorphous and nanocrystalline character of the underlying metallic layer. Higher density of FeNi-enriched nanocrystals is also observed within ~100 nm of the wheel-side surface, presumably due to reduction in local glass former concentration. A rough, crystalline copper oxide layer is also present and forms through contact between the copper wheel and the solidifying melt during the rapid solidification process. On the air side of the ribbon, a crystalline oxide layer of ~15–20 nm is formed as well as intergranular oxidation that penetrates along the grain boundaries between highly textured surface crystallites of ~50–100 nm in size. The crystalline nature of the oxide on these surfaces is asserted to result from the lack of significant Si-content and the pre-existing surface crystallites that form during the rapid solidification process which promote a crystalline oxide surface layer. Furthermore, these results shed new insights into the details of surface oxidation and can help to inform processing and alloy composition adjustments which seek to tailor surface properties.

36 MATERIALS SCIENCE↗
DOE OSTI2019

Virtual bound states elements and their effects on magnetic and electrical properties of Fe-Ni based metal amorphous nanocomposites

Metal amorphous nanocomposite alloys, with compositions (Fe 70 Ni 30 ) 80-x Nb 4 Si 2 B 14 TE x (0 ≤ x ≤ 5), where TE is a transition element, and (Fe 70 Ni 30 ) 80-y Nb 4+y Si 2 B 14 (0.5 ≤ y ≤ 2) were synthesized. Samples were annealed at 440 °C and strain-annealed at 440 °C and 300 MPa. Resistivity was found to increase with small substitutions of TE elements. Increasing V resulted in reduced B s from 1.2 T to 0.5 T. Further Mo additions lowered B s to 0.6 T, and consistently reduced the permeability. For Cr and Nb, resistivity increased, and strain-annealed permeability was lower than the annealed permeability. Finally, toroidal core losses on (Fe 70 Ni 30 ) 79.5 Nb 4 Si 2 B 14 V 1 yielded W1.0/400 = 2.1 W/kg, and W1.0/1 k = 6.0 W/kg.

36 MATERIALS SCIENCE↗
DOE OSTI2018

Metal Amorphous Nanocomposite (MANC) Alloy Cores with Spatially Tuned Permeability for Advanced Power Magnetics Applications

Metal amorphous nanocomposite (MANC) alloys are an emerging class of soft magnetic materials showing promise for a range of inductive components targeted for higher power density and higher efficiency power conversion applications including inductors, transformers, and rotating electrical machinery. Magnetization reversal mechanisms within these alloys are typically determined by composition optimization as well as controlled annealing treatments to generate a nanocomposite structure composed of nanocrystals embedded in an amorphous precursor. Here in this paper we demonstrate the concept of spatially varying the permeability within a given component for optimization of performance by using the strain annealing process. The concept is realized experimentally through the smoothing of the flux profile from the inner to outer core radius achieved by a monotonic variation in tension during the strain annealing process. Great potential exists for an extension of this concept to a wide range of other power magnetic components and more complex spatially varying permeability profiles through advances in strain annealing techniques and controls.

36 MATERIALS SCIENCE↗
NASA NTRS2004

Induced Anisotropy in FeCo-Based Nanocrystalline Ferromagnetic Alloys (HITPERM) by Very High Field Annealing

Very high magnetic field annealing is shown to affect the magnetic anisotropy in FeCo-base nanocrystalline soft ferromagnetic alloys. Alloys of composition Fe(44.5)Co(44.5)Zr(7)B(4) were prepared by melt spinning into amorphous ribbons, then wound to form toroidal bobbin cores. One set of cores was crystallized in a zero field at 600 deg. C for 1 h, then, field annealed at 17 tesla (T) at 480 deg. C for 1 h. Another set was crystallized in a 17-T field at 480 deg. C for 1 h. Field orientation was transverse to the magnetic path of the toroidal cores. An induced anisotropy is indicated by a sheared hysteresis loop. Sensitive torque magnetometry measurements with a Si cantilever sensor indicated a strong, uniaxial, longitudinal easy axis in the zero-field-crystallized sample. The source is most likely magnetoelastic anisotropy, caused by the residual stress from nanocrystallization and the nonzero magnetostriction coefficient for this material. The magnetostrictive coefficient lambda(5) is measured to be 36 ppm by a strain gage technique. Field annealing reduces the magnitude of the induced anisotropy. Core loss measurements were made in the zero-field-crystallized, zero-field-crystallized- than-field-annealed, and field-crystallized states. Core loss is reduced 30%-50% (depending on frequency) by field annealing. X-ray diffraction reveals no evidence of crystalline texture or orientation that would cause the induced anisotropy. Diffusional pair ordering is thought to be the cause of the induced anisotropy. However, reannealing the samples in the absence of a magnetic field at 480 deg. C does not completely remove the induced anisotropy.

FERROMAGNETIC ALLOYS↗