NON-DESTRUCTIVE POST IRRADIATION EXAMINATION OF FIRST CYCLE ACCIDENT TOLERANT AND ADVANCED ZIRCONIUM ALLOY HIGH BURNUP FUEL RODS

Post irradiation examination (PIE) of accident tolerant fuel concepts and high burnup uranium dioxide advanced zirconium alloy clad fuel contribute to near term nuclear industry goals of enhancing light water reactor safety and economics. Westinghouse is developing chromium coated zirconium alloy cladding as an accident tolerant fuel option for current pressurized water reactors. Examination of high burnup fuel further augments the technical foundation for extending the peak rod average burnup limits beyond the current regulatory limit of 62 MWd/kgU. Seven fuel rods were received at the Oak Ridge National Laboratory Irradiated Fuel Examination Facility. This includes three chromium coated zirconium alloy fuel rods and four high burnup advanced zirconium alloy fuel rods. Six of the seven rods were fueled with standard uranium dioxide while one of the chromium coated rods contained Westinghouse’s ADOPT fuel. The overall hot-cell PIE plan and some PIE results have been presented previously. This paper focuses on the additional non-destructive examination and fission gas release. Highlights from visual examination of these rods are presented. The chromium coating showed little to no visual change following irradiation. Observations of the axial burnup trends in the fuel rods are derived from full rod axial gamma-ray scans with additional observations related to local fission product migration. The axial dimensional changes of the seven rods are evaluated. As expected, creep down had not yet occurred in the chromium coated rods, and the maximum diameter strain in the high burnup advanced zirconium alloy cladding was less than 0.5%. Finally, the steady state fission gas release for these rods was measured ranging from 4.1% to 17.6% which matched expectation from literature. These fuel rods now await further destructive examination.

Harp, Jason↗
DOE OSTI2023

Advanced Multiscale Microscopy Characterization of High Burnup LWR UO 2 Before and After LOCA Testing

Previous microscopy work within the campaign has observed increased porosity coupled with subgrain formation in the mid-radial region of the fuel. However, examinations of high burnup fuel taken from multiple reactors with different operating conditions have shown that this structure can move radially inward depending on the fuel operating conditions. It is currently theorized that inter- and intragranular fission gas bubble nucleation is precursory to the grain subdivision observed in the mid-radial and central regions of the fuel. Characterization of samples after loss-of-coolant accident (LOCA) testing has revealed that these restructured regions with a high density of bubbles and subgrains pulverize during the transient test. It appears that the increase in fission gas bubbles coupled with grain subdivision renders the fuel mechanically weaker during a LOCA transient and thus susceptible to fuel fragmentation relocation and dispersal (FFRD). Work this past fiscal year has prioritized understanding this behavior by using advanced microscopy to investigate fission gas behavior in the as-irradiated and post-LOCA state. Additional work has been performed to verify the theory described above by analyzing multiple post-LOCA optical micrographs and comparing that to as-irradiated microstructural data. This document reports progress in the post-irradiation characterization of high burnup nuclear fuel with emphasis on the restructured fuel regions, particularly how microstructural features influence FFRD and fission gas release behavior in LOCA conditions.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗
DOE OSTI2023

Characterization of the radial microstructural evolution in LWR UO 2 using electron backscatter diffraction

Studies on high burnup UO 2 subjected to loss-of-coolant accident conditions have shown that restructured regions of the fuel are susceptible to pulverization and eventual dispersal. Due to a lack of pre-test characterization, the distinct microstructural features rendering the fuel prone to fragmentation remain ambiguous. Four samples of commercially irradiated light-water reactor UO 2 have been characterized utilizing electron backscatter diffraction to assess the susceptible microstructure. The microscopy focused on determining the burnup and temperature conditions responsible for the formation of the different microstructural regions where the regions were denoted as the high-burnup structure (HBS), HBS transition, mid-radial, restructured central, and central region. Previous works have outlined the specific conditions required for the restructuring of the microstructure into the HBS, but the conditions responsible for the restructuring in the central region of the fuel are not well understood. The four analyzed samples confirm a burnup threshold of 61 GWd/tU, and an unknown temperature range is needed to facilitate the formation of the restructured central region. In conclusion, additional fuel performance evaluations are needed to quantify the temperature range promoting restructuring in the central region.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗