Carbon corrosion in low-temperature CO 2 electrolysis systems
Mitigation of carbon corrosion, or the use of non-carbon based anodes, is required to achieve the necessary durability for industrial CO 2 electrolysis.
08 HYDROGEN↗
Engineering topics
McNeary, W. Wilson
Publications and source records attributed to McNeary, W. Wilson.
High Selectivity Reactive Carbon Dioxide Capture over Zeolite Dual-Functional Materials
Reactive carbon dioxide capture (RCC) is a process where carbon dioxide (CO 2 ) is captured from a mixed gas stream (such as air) and converted to products without first performing a separation step to concentrate the CO 2 . Here, in this work, zeolite dual-functional materials (ZFMs) are introduced and evaluated for simulated RCC. The studied ZFMs feature high surface area, crystalline, microporous zeolite faujasite (FAU) as the support. Sodium oxide (“Na 2 O”) is impregnated as an effective capture agent capable of scavenging low concentration CO 2 (1,000 ppm). Exchanged and impregnated sodium on FAU chemisorbs CO 2 as carbonates and bicarbonates but does not promote the conversion of sorbed CO 2 to products when heated in hydrogen. The addition of Ru promotes the formation of formates, while the addition of Pt generates carbonyl surface species when heated in hydrogen. The active metal then promotes extremely high selectivity for CO 2 hydrogenation to either methane on Ru catalyst (~150 °C) or carbon monoxide on Pt catalyst (~200 °C) when heated in reducing atmospheres.
36 MATERIALS SCIENCE↗
Modified Cu–Zn–Al mixed oxide dual function materials enable reactive carbon capture to methanol
A novel RCC process using modified CZA DFMs to produce renewable MeOH is presented. K/CZA provides exceptionally high productivity of MeOH compared to previously reported attempts of RCC to MeOH.
37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗
Optimization of Extended-Surface PtNi Nanowire Oxygen Reduction Electrocatalysts Produced via Atomic Layer Deposition
Polymer electrolyte membrane fuel cells (PEMFCs) produce electricity with only heat and water as byproducts, but sluggish kinetics of the oxygen reduction reaction (ORR) at the cathode and durability limitations restrict widespread commercialization, motivating the development of advanced catalysts. In this research, extended-surface platinum nickel (PtNi) nanowires (NWs) synthesized using the scalable atomic layer deposition (ALD) technique are investigated with the goal of exploring the durability benefits of high-aspect-ratio electrocatalysts and the tunability of beneficial kinetic properties. The surface and bulk composition and the structure of the PtNi NWs were investigated as a function of a series of postsynthesis modifications. The results from a combination of electron microscopy and X-ray spectroscopy characterization techniques were correlated to electrochemical performance to gain a comprehensive understanding of the structure-property-performance relationships. The robust structure of the ALD-derived NWs enabled additional postsynthesis optimization steps, which were not possible with previous-generation materials synthesized via spontaneous galvanic displacement, resulting in a catalyst with beneficial properties for catalyst kinetics as well as improved durability. Our study demonstrates potential pathways toward further improving the performance of this class of materials through optimization of bulk and surface properties of the catalyst.
30 DIRECT ENERGY CONVERSION↗
Atomic Layer Deposition for Improved Biomass Conversion Catalysts
Heterogeneous catalysts are a key enabler of the transition towards a sustainable, bio-based economy for fuels and chemicals. However, the harsh conditions in many biomass conversion processes lead to nanoparticle sintering, support collapse, and metal leaching in conventional PGM catalysts. Next-generation catalysts must be developed to address these stability challenges. This presentation will discuss ongoing work between the Catalytic Carbon Transformation and Scale-Up Center at NREL and various industrial partners to develop scalable and cost-effective atomic layer deposition (ALD) coatings for improving the performance of biomass conversion catalysts. The substantial focus will be devoted to the benefits of TiO2 ALD coatings on supported Pd hydrogenation catalysts. Ten cycles of TiO2 ALD were found to dramatically improve the activity of a conventional Pd/Al2O3 catalyst towards aromatic hydrogenation, despite partial coverage of the Pd sites by the ALD layer. Subsequent advanced characterization and atomic-scale computational modeling revealed that the ALD coating weakened the adsorption strength of hydrogenation surface intermediates, leading to higher reaction rates. Reaction testing after exposure to sulfur impurities, high temperature oxidation, and hydrothermal treatment demonstrated the improved stability of the ALD-coated catalyst. Additionally, the ALD synthesis process was found to be scalable over two orders of magnitude with minimal deviation in synthesized catalyst properties. These results were contextualized with cost models of industrial ALD coating and aromatic hydrogenation processes to further refine the value proposition of ALD coatings. Given the demonstrated improvements in hydrogenation, TiO2 ALD coatings have also been applied to supported Pt catalysts for use in other biomass conversion reactions, such as hydrodeoxygenation for the production of sustainable aviation fuel (SAF) and the oxidation of glucose to bio-derived gluconic acid. Recent findings from these experimental campaigns will also be shared. ALD technology holds great potential in the development of next-generation catalysts for biofuels and bioproducts, and this work constitutes an important examination of the impact of ALD coatings in a variety of reaction environments.
atomic layer deposition↗
Atomic Layer Deposition for Improved Biomass Conversion Catalysts
Heterogeneous catalysts are a key enabler of the transition towards a sustainable, bio-based economy for fuels and chemicals. However, the harsh conditions in many biomass conversion processes lead to nanoparticle sintering, support collapse, and metal leaching in conventional PGM catalysts. Next-generation catalysts must be developed to address these stability challenges. This presentation will discuss ongoing work between the Catalytic Carbon Transformation & Scale-Up Center at NREL and various industrial partners to develop scalable, cost-effective atomic layer deposition (ALD) coatings for improving the performance of biomass conversion catalysts. Substantial focus will be devoted to the benefits of TiO2 ALD coatings on supported Pd hydrogenation catalysts. Ten cycles of TiO2 ALD were found to dramatically improve the activity of a conventional Pd/Al2O3 catalyst towards aromatic hydrogenation, despite partial coverage of the Pd sites by the ALD layer. Subsequent advanced characterization and atomic-scale computational modeling revealed that the ALD coating influenced the adsorption strength of hydrogenation surface intermediates in unexpected ways, leading to higher reaction rates. Reaction testing after exposure to sulfur impurities, high temperature oxidation, and hydrothermal treatment demonstrated the improved stability of the ALD-coated catalyst. Additionally, the ALD synthesis process was found to be scalable over two orders of magnitude with minimal deviation in synthesized catalyst properties. These results were contextualized with cost models of industrial ALD coating and aromatic hydrogenation processes to further refine the value proposition of ALD coatings. Given the demonstrated improvements in hydrogenation, TiO2 ALD coatings have also been applied to supported Pt catalysts for use in other biomass conversion reactions, such as hydrodeoxygenation for production of sustainable aviation fuel (SAF) and the oxidation of glucose for bio-derived gluconic acid. Recent findings from these experimental campaigns will also be shared. ALD technology holds great potential in the development of next-generation catalysts for biofuels and bioproducts and this work constitutes an important examination of the impact of ALD coatings in a variety of reaction environments.
bioenergy↗
Atomic Layer Deposition for Improved Biomass Conversion Catalysts
Heterogeneous catalysts are a key enabler of the transition towards a sustainable, bio-based economy for fuels and chemicals. However, the harsh conditions in many biomass conversion processes lead to nanoparticle sintering, support collapse, and metal leaching in conventional PGM catalysts. Next-generation catalysts must be developed to address these stability challenges. This presentation will discuss ongoing work between the Catalytic Carbon Transformation and Scale-Up Center at NREL and various industrial partners to develop scalable and cost-effective atomic layer deposition (ALD) coatings for improving the performance of biomass conversion catalysts. The substantial focus will be devoted to the benefits of TiO2 ALD coatings on supported Pd hydrogenation catalysts. Ten cycles of TiO2 ALD were found to dramatically improve the activity of a conventional Pd/Al2O3 catalyst towards aromatic hydrogenation, despite partial coverage of the Pd sites by the ALD layer. Subsequent advanced characterization and atomic-scale computational modeling revealed that the ALD coating weakened the adsorption strength of hydrogenation surface intermediates, leading to higher reaction rates. Reaction testing after exposure to sulfur impurities, high temperature oxidation, and hydrothermal treatment demonstrated the improved stability of the ALD-coated catalyst. Additionally, the ALD synthesis process was found to be scalable over two orders of magnitude with minimal deviation in synthesized catalyst properties. These results were contextualized with cost models of industrial ALD coating and aromatic hydrogenation processes to further refine the value proposition of ALD coatings. Given the demonstrated improvements in hydrogenation, TiO2 ALD coatings have also been applied to supported Pt catalysts for use in other biomass conversion reactions, such as hydrodeoxygenation for the production of sustainable aviation fuel (SAF) and the oxidation of glucose to bio-derived gluconic acid.
29 ENERGY PLANNING, POLICY, AND ECONOMY↗
Atomic Layer Deposition with TiO2 for Enhanced Reactivity and Stability of Aromatic Hydrogenation Catalysts
Hydrogenation of aromatic molecules in fossil- and bio-derived fuels is essential for decreasing emissions of harmful combustion products and addressing growing concerns around urban air pollution. In this work, we used atomic layer deposition to significantly enhance the hydrogenation performance of a conventional supported Pd catalyst by applying an ultrathin coating of TiO2 in a scalable powder coating process. The TiO2-coated catalyst showed substantial gains in the conversion of multiple aromatic molecules, including a 5-fold improvement in turnover frequency versus the uncoated catalyst in the hydrogenation of naphthalene. This activity enhancement was maintained upon scaling the coating synthesis process from 3 to 100 g. Based on the results from Xray photoelectron spectroscopy, X-ray absorption spectroscopy, and computational modeling, the activity enhancement was attributed to ensemble effects resulting from partial TiO2 coverage of the Pd surface rather than fundamental changes to the Pd electronic structure. Additional durability testing confirmed that the TiO2 coating improved the thermal and hydrothermal stability of the catalyst as well as tolerance toward sulfur impurities in the reactant stream. Using an economic model of an industrial deep hydrogenation process, we found that an increase in catalyst activity or lifetime of 2× would justify even a relatively high estimate for the cost of TiO2 atomic layer deposition coatings at scale
atomic layer↗