Floating zone crystal growth, structure, and properties of a cubic Li 5.5 La 3 Nb 1.5 Zr 0.5 O 12 garnet-type lithium-ion conductor

As a promising candidate for solid-state electrolytes in Li-ion batteries, the garnet-type Li-ion conductor series Li 5+x La 3 Nb 2-x Zr x O 12 (LLNZO) (0 ≤ x ≤ 2) exhibits high ionic conductivity at room temperature. However, no previous single-crystal growth or characterization has been reported for LLNZO compositions 0 ≤ x ≤ 1. To obtain a complete understanding of the trend in the structure–property relationship in this class of materials, we used the floating zone (FZ) method to grow a single crystal of Li 5.5 La 3 Nb 1.5 Zr 0.5 O 12 that was 4 mm in diameter and 10 mm in length. Using Laue neutron single-crystal diffraction, two distinct Li sites were observed: tetrahedral 24d and octahedral 96h sites. The maximum entropy method (MEM) based on neutron single-crystal diffraction data was used to map Li nuclear density and estimate that the bottleneck of Li transport exists between neighboring tetrahedral and octahedral sites, and that Li is delocalized between split octahedral sites. Room-temperature Li-ion conductivity in Li 5.5 La 3 Nb 1.5 Zr 0.5 O 12 measured with electrochemical impedance spectroscopy (EIS) was 1.37 × 10 -4 S cm -1 . The Li migration activation energy was estimated to be 0.50 eV from EIS and 0.47 eV from dielectric relaxation measurements. The Li-ion jump attempt rate was estimated to be 1.47 × 10 12 Hz while the time scale of successful migration is 10 -7 to 10 -6 s.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗
DOE OSTI2021

Spin and Charge Interconversion in Dirac-Semimetal Thin Films

We use spin torque ferromagnetic resonance and ferromagnetic-resonance-driven spin pumping to detect spin-charge interconversion at room temperature in heterostructure devices that interface an archetypal Dirac semimetal, Cd 3 As 2 , with a metallic ferromagnet, Ni 0.80 Fe 0.20 (permalloy). Angle-resolved photoemission directly reveals the Dirac-semimetal nature of the samples prior to device fabrication and high-resolution transmission electron microscopy is used to characterize the crystalline structure and the relevant heterointerfaces. We find that the spin-charge interconversion efficiency in Cd 3 As 2 /permalloy heterostructures is comparable to that in heavy metals and that it is enhanced by the presence of an interfacial oxide. Spin torque ferromagnetic resonance measurements reveal an in-plane spin polarization regardless of an oxidized or pristine interface. We discuss the underlying mechanisms for spin-charge interconversion by comparing our results with first principles calculations and conclude that extrinsic mechanisms dominate the observed phenomena. Our results indicate a need for caution in interpretations of spin-transport and spin-charge conversion experiments in Cd 3 As 2 devices that seek to invoke the role of topological Dirac and Fermi arc states.

75 CONDENSED MATTER PHYSICS, SUPERCONDUCTIVITY AND↗