DOE OSTI2021

A Comparative Study on the Effect of Zr, Sn, and Ti on the Crystallization Behavior of Nepheline Glass

In alkali aluminosilicate glasses, additions of 4+ cations like Zr and Ti are often added to promote crystallization. In this study, Zr, Ti, or Sn are progressively substituted for Si in nepheline (NaAlSiO4) glass to determine their impact on the crystallization behavior. For glasses homogeneous on quenching, up to NaAlZr0.075Si0.925O4, NaAlSn0.100Si0.900O4, and NaAlTi0.300Si0.700O4, respectively, crystallization temperatures were investigated by thermal analysis. A subset of compositions was subjected to additional thermal analysis, varying heating rate and particle size, to investigate the subtleties of crystallization behavior. Subsequent heat treatment of glass powders was performed to maximize crystallization, and glass-ceramic microstructure was assessed by optical microscopy and electron microprobe, while crystalline phases were determined by X-ray diffraction. In all cases the major crystalline phase was orthorhombic carnegieite, which accommodated Ti in its structure but not Zr or Sn, and excess 4+ cations formed MO2, i.e., brookite, baddeleyite, and cassiterite, respectively.

Nienhuis-Marcial, Emily T.↗

DOE OSTI2020

A Data-driven Approach for Predicting Nepheline Crystallization in High-Level Waste Glasses

High-level waste (HLW) glasses with high aluminum content are prone to nepheline crystallization during the slow canister cooling that is experienced during large-scale production. Due to its detrimental effects on glass durability, nepheline precipitation must be avoided; however, developing robust, predictive models for nepheline crystallization behavior in HLW glasses is difficult due to their compositional complexity. Using overly conservative constraints to predict nepheline formation can limit the waste loading to lower than the achievable capacity. In this study, a robust data-driven model using five compositional features has been developed to predict nepheline formation. The analysis of the model and the data show that there is an overlap, instead of a distinct compositional boundary, between glasses that form and do not form nepheline. As a result, the model’s predictive accuracy is not the same throughout the feature space and instead is dependent on the location of the glass composition in the dimensionally reduced feature space.

Sargin, Irmak↗

DOE OSTI2020

Thermal Properties of Sodium Borosilicate Glasses as a Function of Sulfur Content

SO3 additions, up to 3.0 wt%, were systematically investigated for effects on the physical properties of sodium borosilicate glass melted in air, with a sulfur-free composition of 50SiO2-10Al2O3-12B2O3-21Na2O-7CaO (wt%). Solubility measurements, using electron microscopy chemical analysis, determined the maximum loading to be ~1.5 wt% SO3. It was found that sulfur (here as sulfate) in this glass increased the glass transition temperature, thermal diffusivity, heat capacity, and thermal conductivity, and decreased the mass density. Structural analysis, performed with Raman spectroscopy, indicated that the borosilicate network polymerized with sulfur additions, presumably due to Na2O being required to charge compensate the ionic SO42- additions, thus becoming unavailable to form non-bridging oxygen in the silicate network. It is postulated that this increased crosslinking of the borosilicate backbone lead to a structure with higher dimensionality and average bond energy. This increased the mean free paths and vibration frequency of the phonons, which resulted in the observed increase in thermal properties.

Thermal properties, Borosilicate glass, Sulfur sol↗