Reliability of Materials and Components for Solid Oxide Fuel Cells
Planar stack solid-oxide fuel cells (SOFCs) require seals that must operate reliably under demanding conditions for lifetimes of 40000 hours. This includes temperature fluctuations between 800°C and RT during on and off cycles, thermal stresses, oxidizing environments and chemical degradation to name a few. This comprehensive report provides results from long term testing of two commercially available multicomponent barium alkali silicate glasses: SCN and G6, chosen as sealing candidates. In this scope, the glass seals were deposited on YSZ and Al 2 O 3 substrates simulating electrolytes (Zrbased) and coatings (both zirconia and Al 2 O 3 ). The seal-substrate couples were subjected to 800°C under air and steam+H 2 +N 2 environments up to 40000 hours to test their integrity under real operating conditions. Extensive studies on the effects of exposure have been conducted over the span of testing at various time intervals. Within the context of characterization, mechanical properties such as density, roughness, thermal expansion and glass transition, viscosity and wettability behavior; and microstructural properties such as glass chemistries, defect formation (cracks and pores), phase transformations (devitrification) and glass-interface reactions are investigated. Results and discussions are provided with a focus on the degradation of the properties over long term interrupted testing.