S8DR shield examination
The SNAP 8 developmental reactor lithium hydride shield was examined after being irradiated for over 7000 hours at relatively low temperature. A crack was located in the seam weld of the containment vessel, probably the result of hot short cracking under thermal stress. The LiH was visually examined at two locations and its appearance was typical of low temperature irradiated LiH. The adherence of the chrome oxide emittance coating was found to be excellent.
Mason, D. G.↗