Publications and source records attributed to Mcdonald, G..
High quality SiC ceramic foams, which have only recently become available, have for the first time made possible the construction of low density ceramic fiber-ceramic foam sandwiches for high temperature applications. This report describes the construction of some ceramic fiber-ceramic foam structures and the preliminary measurement of strength at elevated temperature.
Report summarizes design of ceramic coats for metal parts in heat engines. Ceramic coat used to reduce transfer of heat from hot gas to cylinder wall, piston, turbine blade, or other internally-cooled metal part. Enables use of higher gas temperatures needed for higher efficiencies, permits use of less cooling air, or extends life of metal part by reducing temperature.
Some early history of ceramic applications is presented. Finite element modeling of components to determine service and fabrication loads found inelastic behavior and residual stresses to be significant to component life. Inelastic behavior mitigates peak strains but enhances residual strains. Results of furnace, Mach 0.3 burner, and engine tests are discussed and categorized into design criteria (loading, geometry, fabrication, materials, analysis, and testing). These design rules and finite element analyses are brought to bear on two test cases: turboshaft engine seals, and rocket thrust chambers.
Components fabricated of, or coated with, ceramics have lower parasitic cooling requirements. Techniques are discussed for fabricating thin-shell ceramic components and ceramic coatings for applications in rocket or jet engine environments. Thin ceramic shells with complex geometric forms involving convolutions and reentrant surfaces were fabricated by mandrel removal. Mandrel removal was combined with electroplating or plasma spraying and isostatic pressing to form a metal support for the ceramic. Rocket engine thrust chambers coated with 0.08 mm (3 mil) of ZrO2-8Y2O3 had no failures and a tenfold increase in engine life. Some measured mechanical properties of the plasma-sprayed ceramic are presented.
A method is described to electrodeposit noble metals such as platinum and ordinary metals such as copper on and within plasma-sprayed ceramic materials and ceramic fiber materials. Low-density ceramic fiber bodies were vacuum impregnated with plating solution and attached to an electrode. Light micrographs illustrating the density and location of deposited materials are presented and discussed. Voids in the plasma-sprayed ceramic were filled with deposits that vary from spherical to lens-shaped circular and have particle size corresponding to the full range of void size. Multiple coatings of ceramic and metal can be sequenced.
Experimental and analytical studies were conducted to determine the acceptability of a ribbon-burner simulation of engine conditions for testing ceramic-lined turbine tip shrouds. The calculated values reveal that the ribbon burner establishes at least as harsh a thermal environment as is present at any time within the turbine shroud. Comparisons were made with ceramic components in a turboshaft engine.
Residual stress in a ZrO2-Y2O3 ceramic coating resulting from the plasma spraying operation is calculated. The calculations were done using the finite element method. Both thermal and mechanical analysis were performed. The resulting residual stress field was compared to the measurements obtained by Hendricks and McDonald. Reasonable agreement between the predicted and measured moment occurred. However, the resulting stress field is not in pure bending.
Ceramic gas-path seals were fabricated and successfully operated over 1000 cycles from flight idle to maximum power in a small turboshaft engine. The seals were fabricated by plasma spraying zirconia over a NiCoCrAlX bond coat on the Haynes 25 substrate. Coolant-side substrate temperatures and related engine parameters were recorded. Post-test inspection revealed mudflat surface cracking with penetration to the ceramic bond-coat interface.
Components fabricated of, or coated with, ceramics have lower parasitic cooling requirements. Techniques are discussed for fabricating thin-shell ceramic components and ceramic coatings for applications in rocket or jet engine environments. Thin ceramic shells with complex geometric forms involving convolutions and reentrant surfaces were fabricated by mandrel removal. Mandrel removal was combined with electroplating or plasma spraying and isostatic pressing to form a metal support for the ceramic. Rocket engine thrust chambers coated with 0.08 mm (3 mil) of ZrO2-8Y2O3 had no failures and a tenfold increase in engine life. Some measured mechanical properties of the plasma-sprayed ceramic are presented.
Ceramic gas-path seals were fabricated and successfully operated over 1000 cycles from flight idle to maximum power in a small turboshaft engine. The seals were fabricated by plasma spraying zirconia over a NiCoCrAlX bond boat on the Haynes 25 substrate. Coolant-side substrate temperatures and related engine parameters were recorded. Post-test inspection revealed mudflat surface cracking with penetration to the ceramic bond-coat interface.
Experimental and analytical studies were conducted to determine the acceptability of a ribbon-burner simulation of engine conditions for testing ceramic-lined turbine tip shrouds. The calculated values reveal that the ribbon burner establishes at least as harsh a thermal environment as is present at any time within the turbine shroud. Comparisons were made with ceramic components in a turboshaft engine.
Metallic and metalloceramic coatings were prepared by thermal decomposition of a number of inorganic and metallo-organic compounds. The compounds were applied by spraying and by immersion, especially on ceramic fibers and fiber forms, which are easily coated by this procedure. Penetration of low-density ceramics is examined, and procedures are described that were used for converting the deposited materials to metals, oxides, or metal oxide films. Multiple-component films were also prepared. Photomicrographs illustrate the structure of these films.
A method is described to electrodeposit noble metals such as platinum and ordinary metals such as copper on and within plasma-sprayed ceramic materials and ceramic fiber materials. Low-density ceramic fiber bodies were vacuum impregnated with plating solution and attached to an electrode. Light micrographs illustrating the density and location of deposited materials are presented and discussed. Voids in the plasma-sprayed ceramic were filled with deposits that vary from spherical to lens-shaped circular and have particle size corresponding to the full range of void size. Multiple coatings of ceramic and metal can be sequenced.
The plastic flow of plasma-sprayed ZrO2-8Y2O3 ceramic has been measured at temperatures up to 1250 C and compared to the plastic flow of pressed and sintered ZrO2-8Y2O3. Plasma spraying of binary oxide ceramics is found to result in a metastable state which is inelastic at high temperature but can also be stabilized or devitrified through heat treating so as to decrease plastic properties. The mechanical properties of the as-plasma sprayed and devitrified ceramic sheet material was measured. An improved algorithm that incorporates the inherently nonlinear thermomechanical field equations was used to determine the influence of inelastic material behavior on the thermomechanical response of ceramic coated seal components. Significant creep was found during the thermal shock and steady heating periods with insufficient time during thermal quench to reverse the process, thereby inducing significant residual stresses into the components.
The residual stresses in a ceramic sheet material used for turbine blade tip gas path seals, were estimated. These stresses result from the plasma spraying process which leaves the surface of the sheet in tension. To determine the properties of plasma sprayed ZrO2-Y2O3 sheet material, its load deflection characteristics were measured. Estimates of the mechanical properties for sheet materials were found to differ from those reported for plasma sprayed bulk materials. Previously announced in STAR as N83-28380
Ceramics on metal substrates for potential use as high temperature seals or other applications are exposed to forces originating from differences in thermal expansion between the ceramic and the metal substrate. This report develops a relationship between the difference in expansion of the ceramic and the substrate, defines conditions under which shear between the ceramic and the substrate occurs, and those under which bending forces are produced in the ceramic. The off-axis effect of compression forces resulting from high temperature plastic flow of the ceramic producing buckling of the ceramic is developed. Shear is associated with the edge or boundary stresses on the component while bending is associated with the distortion of an interior region. Both modes are significant in predicting life of the ceramic. Previously announced in STAR as N83-27016
The creep of plasma sprayed ZrO2-8Y2O3 was measured at temperatures from 98 to 1250 C (180 to 220 F), and compared to creep of identical samples after annealing at temperatures from 98 to 1316 C (1800 to 2400 F). Loads and temperatures which produced significant creep of as sprayed ceramics produced no creep after annealing. Previously announced in STAR as N83-24799
The principal of multiple material layering is well known as an effective method of reducing heat transfer; however, thermal gradients can impose significant loads and lead to delamination and subsequent component failure. An analysis is developed and experimental data are discussed for the thermomechanical effects of multilayered materials on a heat sink substrate of cylindrical geometry subject to thermal cycling. The geometry is heated in cross-flow by a high-velocity flame and cooled in crossflow by ambient-temperature air from a critical flow orifice. Each layer of material possesses a threshold beyond which small changes in temperature or mechanical loading greatly influence the life in thermal cycling of the layered materials. Comparisons are made between the thermomechanical loads predicted by various numerical codes for the linear case and by a simplified analytic model.