A creep apparatus to explore the quenching and ageing phenomena of PVC films

A creep apparatus has been constructed for an in situ determination of length and length change. Using this apparatus, the creep behavior of PVC thin films associated with quenching and aging was studied. The more severe the quench through the glass transition temperature, the greater is the instantaneous elastic deformation and the subsequent creep behavior. As aging proceeds, the quenched films gradually lose the ductility incurred by quenching. These results agree well with the well-known phenomena of physical aging. Thus, the changes reflecting molecular mobilities due to quenching and aging can be properly monitored by such a creep apparatus.

Lee, H. H. D.↗

NASA NTRS1982

Rapid quenching effects in glassy polymers

Using a specially constructed microbalance for hydrostatic weighing, density changes in PVC thin film due to rapid quenching through the glass transition temperature were observed. The more severe the quench, the greater the free volume content. Isobaric volume recovery of PVC was also studied by volume dilatometry. Both show aging of relaxing molecular rearrangements taking place as a linear function of logarithmic aging time at room temperature. Distribution of retardation times and Primak's distributed activation energy spectra were applied to the volume recovery data. The concomitant changes in mechanical properties of PVC after quenching were monitored by tensile creep stress-stran to failure rates. All reflect the presence of excess free volume content due to rapid quenching.

Mcgarry, F. J.↗

NASA NTRS1981

Rapid quenching effects in PVC films

Using a specially constructed microbalance for hydrostatic weighing, density changes in PVC thin films (with no additives, 30-100 micrometers thick), due to rapid quenching (approximately 300 C/sec) through the glass transition temperature, have been observed. The more severe the quench, the greater is the free volume content. Isobaric volume recovery of PVC has also been studied by volume dilatometry. Both show aging of relaxing molecular rearrangements takes place as a linear function of logarithmic aging time at room temperature. Distribution of retardation times and Primak's distributed activation energy spectra have been applied to the volume recovery data. The concomitant changes in mechanical properties of PVC after quenching have been monitored by tensile creep and stress-strain to failure. All reflect the presence of excess free volume content, due to rapid quenching.

Lee, H. D.↗

NASA NTRS1979

Toughening of thermosetting polyimides

Work directed toward increasing the resistance to crack propagation of thermoset polyimides is described. Rubber modification and Teflon microfiber impregnation techniques for increasing fracture toughness are investigated. Unmodified Kerimid 601 has a fracture surface work value of 0.20 in-lbs/sq in. Dispersed particles of amine terminated butadiene acrylonitrile liquid rubber or of silicone rubber do not raise this value much. By contrast, 5 percent of well fibrillated Teflon produces an eight-fold increase in fracture toughness. Further process improvements should increase this factor to 20-30.

Gollob, D. S.↗

NASA NTRS1976

Surface crack growth in fiber composites

The results of an experimental study of damage extension and failure in glass and graphite/epoxy laminates containing partially through-thickness surface cracks are presented. The laminates studied are divided between those containing four plies, 90/0/0/90, 15/-15/-15/15, and 45/-45/-45/45, and those containing 12-16 plies of the general configurations 0/90, + or - 45, and 0/+ or - 60. Most of the results are for surface cracks of various lengths and several depths. Stable damage extension in laminates containing surface cracks is predominantly delamination between plies, and tends to be much more extensive prior to failure than is the case with through-thickness cracks, resulting in approximately notch-insensitive behavior in most cases. A greater tendency for notch-sensitive behavior is found for 0/90 graphite/epoxy laminates for which stable damage extension is more limited. The rate of damage extension with increasing applied stress depends upon the composite system and ply configuration as well as the crack length and depth. An approximate semiempirical method is presented for estimating the growth rate of large damage-regions.

Im, J.↗