Two groups of refractory metal compositions have been developed that are very useful as high temperature brazing alloys for sealing between ceramic and metal parts. Each group consists of various compositions of three selected refractory metals which, when combined, have characteristics required of good braze alloys.
Two phases have been completed, of a program whose ultimate objective is the development of an alkali metal resistant, thermal shock resistant, leak-tight, and neutron radiation resistant ceramic-to-metal seal capable of operation at 1200 C for three to five years. The first phase involved the screening of platinum-base, vanadium-base and vanadium-niobium base brazes for the joining of Cb-1Zr or T-111 alloys to high purity alumina. The second phase involved studies of the performance of sealed capsule samples during 5000-hour aging tests at 800, 1000, and 1200 C in high vacuum. Sealed capsules which were made using pure vanadium braze, and were brazed at 1850 C for one minute, survived 64 thermal cycles to 1200 C at the heating/cooling rate of 100 C/minute. Vanadium braze samples survived 5000-hour aging tests at 800, 1000, and 1200 C. One thermally cycled sample survived a subsequent 5000-hour aging period at 1000 C, but another, at 1200 C, did not survive. It was concluded that a pure vanadium braze used to bond high purity alumina to Cb-1Zr alloy is the best of the systems studied, but that additional studies must be performed to establish its service temperature limitations for the desired three to five years' service.