High-temperature ohmic contact to n-type 6H-SiC using nickel
Specific contact resistances measured at elevated temperatures for Ni ohmic contacts to 6H-SiC were reported. The specific contact resistances were measured with the linear transmission line method at both room temperature and at 500 C and yielded values less than 5 x 10(exp -6) ohm sq cm at both temperatures. The trend shows a decreasing contact resistance at higher temperature. The annealed metal film is a nickel silicide with substantial mixing of C throughout the silicide layer.