Medina, Francisco | Search NASA

DOE OSTI2024

On the Mechanical Behavior of LP-DED C103 Thin-Wall Structures

Laser Powder Directed Energy Deposition (LP-DED) can produce thin-wall features on the order of 1 mm. These features are essential for large structures operating in extreme environments such as regeneratively cooled nozzles and heat exchangers, which often make use of refractory metals. In this work, the mechanical behavior of LP-DED C103 was investigated via quasi-static tensile testing and low cycle fatigue (LCF) testing. The effects of vacuum stress relief (SR) and hot isostatic pressing (HIP) heat treatments were investigated for specimens in the vertical and horizontal build orientations during tensile testing. The AB and SR properties were lower than literature values for wrought and laser powder bed fusion (L-PBF) bulk components but higher than electron beam powder bed fusion (EB-PBF). The application of a HIP cycle improved strength by 7% and ductility by 27% past the initial as-built condition. Fracture images reveal that interlayer stress concentration sites are responsible for fracture in specimens in the vertical orientation. Meanwhile, fracture in the horizontal specimens mainly propagates at a slanted angle typical of plane stress conditions. The LCF results show cycles to failure ranging from 100 cycles to 8000 cycles for max strain levels of 2% and 0.5%, respectively. Fractography on the fatigue specimens reveals an increasing propagation zone as max strain levels are increased. The impact of these findings and future work are discussed in detail.

36 MATERIALS SCIENCE↗

DOE OSTI2024

Parameter development and characterization of laser powder directed energy deposition of Nb – Alloy C103 for thin wall geometries

This work focuses on the parameter development and microstructural characterization of Nb-based alloy C103 for thin wall structures produced via laser powder – directed energy deposition (LP – DED). Laser power and scanning speeds were varied as part of a design of experiments to identify adequate print parameters. Combinations were evaluated for relative density, porosity, and geometrical accuracy. A combination of a laser power of 1420 W and scanning speed of 14 mm/s resulted in a relative density >99%, exhibited a consistent weld bead profile and was used for further microstructural evaluation. A mix of optical and scanning electron microscopy (SEM) revealed small, slightly elongated grains along the edges and large epitaxial grains in the central region along the Build – Transverse view. Scanning electron microscopy (SEM) and energy dispersive spectroscopy (EDS) analysis revealed Hf rich columnar cells in the center that transition into an evenly spaced cellular structure towards the edges of the built sample. Electron backscatter diffraction (EBSD) scans show a sharp [001] texture when looking at the cross section of the sample along the build direction. The Build – Scan view revealed a zig – zag pattern that follows the back – and – forth deposition strategy that was used. Finally, microhardness measurements were taken in the as – built (AB) and stress relieved (SR) conditions to baseline preliminary mechanical properties. The AB condition exhibited a large amount of scatter in the data and averages up to 11% larger than the SR condition. The reduction in scatter upon applying the SR cycle are indicative of a large concertation of dislocations present in the AB condition.

36 MATERIALS SCIENCE↗