DOE OSTI2023

Investigation of the silicon coated film characteristics on tungsten surface in EAST fusion device

Siliconization using 10 % SiD 4 + 90 % He assisted by ion cyclotron range of frequency discharge (ICRF) or glow discharge (GD) was performed in EAST with full tungsten (W) diverters. It was found that the coated Si film on W sample at a higher baking temperature (160 °C) was smoother than that at a lower baking temperature (60 °C). This was mainly because physically adsorbed gaseous impurities were released at a higher baker temperature. This process improved the adhesion between the film and the surface of W. An increase in the ICRF working power from 20 kW to 40 kW further increased the Si content and the film thickness by 1.5 times. The cleaning efficiency of ICRF on the surface of the W sample before siliconization was higher at 40 kW than that at 20 kW, which facilitated the removal of oxides and other compounds from the surface of W. The ratio of silicon/oxygen (Si/O) and the thickness improved considerably due to greater ionization and deposition of SiD 4 . Additionally, siliconization via GD was more uniform and 1.5 nm thicker than that via ICRF, which was because of the greater working gas pressure, coating duration, and homogeneity in GD. These results might be used as a reference for evaluating the effect of siliconization on plasma performance and its application in fusion devices.

70 PLASMA PHYSICS AND FUSION TECHNOLOGY↗

DOE OSTI2022

Evidence of vapor shielding effect on heat flux loaded on flowing liquid lithium limiter in EAST

For this study, a lithium (Li) vapour layer was formed around a flowing liquid Li limiter to shield against the plasma incident power and reduce limiter heat flux in the EAST tokamak. The results revealed that after a plasma operation of a few seconds, the layer became clear, which indicated a strong Li emission with a decrease in the limiter surface temperature. This emission resulted in a dense vapour around the limiter, and Li ions moved along the magnetic field to form a green shielding layer on the limiter. The plasma heat flux loaded on the limiter, measured by the probe installed on the limiter, was approximately 52% lower than that detected by a fast-reciprocating probe at the same radial position without the limiter in EAST. Additionally, approximately 42% of the parallel heat flux was dissipated directly with the enhanced Li radiation in the discharge with the liquid metal infused trenches (LIMIT) limiter. This observation revealed that the Li vapour layer exhibited an excellent shielding effect to liquid Li on plasma heat flux, which is a possible benefit of liquid-plasma-facing components in future fusion devices.

70 PLASMA PHYSICS AND FUSION TECHNOLOGY↗

DOE OSTI2021

Type-I ELM mitigation by continuous lithium granule gravitational injection into the upper tungsten divertor in EAST

Large edge-localized modes (ELMs) were mitigated by gravitational injection of lithium granules into the upper X-point region of the EAST device with tungsten plasma-facing components. The maximum ELM size was reduced by ~ 70% in high βN H-mode plasmas. Large ELM stabilization was sustained for up to about 40 energy confinement times, with constant core radiated power and no evidence of high-Z or low-Z impurity accumulation. The lithium granules injection reduced the edge plasma pedestal density and temperature and their gradients, due to increased edge radiation and reduced recycling from the plasma-facing components. Ideal stability calculations using the ELITE code indicate that the stabilization of large ELMs correlates with improved stability of intermediate-n peeling-ballooning modes, due to reduced edge current resulting from the profile changes. The pedestal pressure reduction was partially offset by a core density increase, which resulted in a modest ~ 7% drop in core stored energy and normalized energy confinement time. We surmise that the remnant small ELMs are triggered by the penetration of multiple Li granules just past the separatrix, similar to small ELMs triggered by deuterium pellet [S. Futatani et al., Nucl. Fusion 54 (2014) 073008]. This study extends previous ELM elimination with Li powder injection [R. Maingi et al., Nucl. Fusion 58 (2018) 024003] in EAST because 1) use of small, dust-like powder and the related potential health hazards were eliminated, and 2) use of macroscopic granules should be more applicable to future devices, due to deeper penetration than dust particles, e.g. inside the separatrix with velocities ~ 10 m/s in EAST.

EAST↗