Engineering topics
Meng, Yongtao
Publications and source records attributed to Meng, Yongtao.
Highly sustained electrodes and electrolytes for salty alkaline and neutral water splitting
A corrosion resistant anode is provided for oxygen evolution reaction in water including chloride ions. The anode includes: (1) a substrate; (2) a passivation layer coating the substrate; and (3) an electrocatalyst layer coating the passivation layer. Polyanion adjusted alkaline seawater electrolyte for hydrogen generation by electrolysis is also provided.
Large Scale Synthesis of Manganese Oxide/Reduced Graphene Oxide Composites as Anode Materials for Long Cycle Lithium Ion Batteries
Manganese oxides have been frequently used as cathodes in primary batteries. Applications of manganese oxides in secondary batteries are limited by low electrical conductivity and rapid capacity fading because of electrode pulverization and aggregation. In this study, a solid-state synthetic strategy is presented that successfully combines nanosize (~ 50 nm) nickel doped α-MnO 2 with reduced graphene oxides as highly stable composite anodes in lithium ion batteries. The synthesis approach is easy to scale up and suitable for industrial applications. Here, the rationally designed Ni-α-MnO 2 /RGO was tested in galvanostatic half coin cells for Li + charge-discharge studies. The results show that this composite maintains a high capacity of 615 mAh g -1 even after 200 cycles at a high current rate of 1 C (830 mA g -1 ), and with a high Coulombic efficiency near 99%. The anodes exhibit excellent rate capability in a wide range of rate testing from 0.2 to 10 C, without showing capacity decay. This superior anode performance is ascribed to the reduced size of α-MnO 2 domains that are well dispersed in an RGO matrix, which affords good ionic/elec. cond., low charge transfer resistance and mitigates issues of vol. expansion of the anodic active materials. This study opens up an avenue for developing the manufacturing of high-performance electrodes for real applications, such as batteries in electrical vehicles.
Highly active oxygen evolution integrated with efficient CO 2 to CO electroreduction
Electrochemical reduction of CO 2 to useful chemicals has been actively pursued for closing the carbon cycle and preventing further deterioration of the environment/climate. Since CO 2 reduction reaction (CO 2 RR) at a cathode is always paired with the oxygen evolution reaction (OER) at an anode, the overall efficiency of electrical energy to chemical fuel conversion must consider the large energy barrier and sluggish kinetics of OER, especially in widely used electrolytes, such as the pH-neutral CO 2 -saturated 0.5 M KHCO 3 . OER in such electrolytes mostly relies on noble metal (Ir- and Ru-based) electrocatalysts in the anode. Here, we discover that by anodizing a metallic Ni–Fe composite foam under a harsh condition (in a low-concentration 0.1 M KHCO 3 solution at 85 °C under a high-current ~250 mA/cm 2 ), OER on the NiFe foam is accompanied by anodic etching, and the surface layer evolves into a nickel–iron hydroxide carbonate (NiFe-HC) material composed of porous, poorly crystalline flakes of flower-like NiFe layer-double hydroxide (LDH) intercalated with carbonate anions. The resulting NiFe-HC electrode in CO 2 -saturated 0.5 M KHCO 3 exhibited OER activity superior to IrO 2 , with an overpotential of 450 and 590 mV to reach 10 and 250 mA/cm 2 , respectively, and high stability for >120 h without decay. We paired NiFe-HC with a CO 2 RR catalyst of cobalt phthalocyanine/carbon nanotube (CoPc/CNT) in a CO 2 electrolyzer, achieving selective cathodic conversion of CO 2 to CO with >97% Faradaic efficiency and simultaneous anodic water oxidation to O 2 . The device showed a low cell voltage of 2.13 V and high electricity-to-chemical fuel efficiency of 59% at a current density of 10 mA/cm 2 .