DOE OSTI2024

Recycled graphite enabled superior performance for lithium ion batteries

Recycling graphite attracts growing attention since cumulative amount of spent Li-ion batteries and the shortage of graphite supply chain. Although various recycling methods have been reported, the recycled graphite cannot reach the strict commercial standards of purity, scalability, efficiency, and capacity, preventing it from battery manufacturing. Herein, the important roles of defects and functional groups on the graphite surface are deeply studied, and a closed-loop graphite recycling process with the surface recovery and modification for the graphite from the end-of-life batteries is demonstrated. The recovered graphite delivers a purity of over 99.9 % and an average initial coulombic efficiency of 91.5 %. Compared with commercial graphite in industrial standard battery testing parameters, full cells with recovered graphite possess enhanced rate reversibility, doubled cycle life, over 10 % higher capacity along with half anode material cost. In conclusion, these impressive results not only underscore the transformative potential of surface reconstruction and modification in graphite recycling, but also present economic feasibility and sustainable pathway for significantly improving battery performance and addressing global resource challenges via integration with the hydrometallurgical recycling process.

25 ENERGY STORAGE↗

DOE OSTI2024

Acid Etching‐Driven Self‐Assembly of Mn‐Shell Inducing Rock‐Salt Phase for Enhanced Single‐Crystal Ni‐Rich Cathodes

With the wide adoption of Li‐ion batteries, Ni‐rich cathode is considered as one of the most promising candidates of cathodes due to its high energy density and low cost. However, stability decreased with increasing Ni content in the Ni‐rich cathode. To solve this bottleneck, many strategies, such as coating, doping, surface modification, and special morphologies, have been developed. Herein, we introduce a groundbreaking approach for enhancing Ni‐rich cathode through an innovative acid etching process that promotes Mn shell self‐assembly, inducing a rock‐salt phase on the surface. This method not only simplifies the Ni‐rich cathode modification process, but also significantly improves the structural stability and electrochemical performance of Ni‐rich cathode. Our findings demonstrate that developed single‐crystal Ni‐rich cathode shows 3–34 % better stability compared to both commercial modified Ni‐rich cathode and unmodified counterparts. The unique Mn shell effectively mitigates reversible phase shifts during cycling, contributing to a remarkable enhancement in cycling stability. Additionally, this novel fabrication technique paves the way for cost‐effective production of high‐performance cathode materials, offering substantial benefits for lithium‐ion battery technology. And this study proves the potential of this method in advancing the design and development of durable, high‐capacity cathode materials for next‐generation batteries.

Ni-rich cathode↗

DOE OSTI2024

Understanding the Effects of Bi Modification on the Properties of Ni-Rich Cathodes

With the skyrocketing market demands for energy storage, lithium ions batteries (LIB) with higher energy density are urgently needed. Cathodes play a critical role in determining the energy density of LIB, and the most popular one is Ni-rich cathode due to its high capacity. However, due to the fast structural degradation, Ni-rich cathode materials should be further modified to achieve higher stability. Herein, we introduce bismuth ions in LiNi 0.83 Co 0.11 Mn 0.06 O 2 cathodes by adding Bi 2 O 3 during sintering to optimize the specific capacity and cycle stability. By adding 0.1% mol Bi, the Li + diffusion and structural stability are effectively optimized, leading to improved electrochemical performances. Further, the modified sample delivers much higher specific capacity (222.9 mAhg -1 , 0.05 C) than unmodified sample (204 mAhg -1 , 0.05 C). Meanwhile, the specific capacity of optimized sample after 100 cycles at 0.33 C is 27.75 mAhg -1 higher than that of unmodified sample. Therefore, this work demonstrates that Bi modification can be regarded as a possible solution to optimizing the electrochemical performance of Ni-rich cathodes.

25 ENERGY STORAGE↗

DOE OSTI2023

Regulating Anionic Redox via Mg Substitution in Mn-Rich Layered Oxide Cathodes Enabling High Electrochemical Stability for Sodium-Ion Batteries

Here, with the limited resources and high cost of lithium-ion batteries (LIBs) and the ever-increasing market demands, sodium-ion batteries (SIBs) gain much interest due to their economical sustainability, and similar chemistry and manufacturing processes to LIBs. As cathodes play a vital role in determining the energy density of SIBs, Mn-based layered oxides are promising cathodes due to their low cost, environmental friendliness, and high theoretical capacity. However, the main challenge is structural instability upon cycling at high voltage. Herein, Mg is introduced into the P2-type Na 0.62 Ni 0.25 Mn 0.75 O 2 cathode to enhance electrochemical stability. By combining electrochemical testing and material characterizations, it is found that substituting 10 mol% Mg can effectively alleviate the P2–O2 phase transition, Jahn-Teller distortion, and irreversible oxygen redox. Moreover, structural integrity is greatly improved. These lead to enhanced electrochemical performances. With the optimized sample, a remarkable capacity retention of 92% in the half cell after 100 cycles and 95% in the full cell after 170 cycles can be achieved. Altogether, this work provides an alternative way to stabilize P2-type Mn-based layer oxide cathodes, which in turn, put forward the development of this material for the next-generation SIBs.

25 ENERGY STORAGE↗

DOE OSTI2023

Unraveling the nature of sulfide ions in hydrometallurgical recycling of NCM622 cathode material

The use of lithium-ion batteries (LIBs) has increased dramatically since its initial inception in the late 20th century. Such a surge in the LIB market and industry has resulted in a huge demand for mineral resources. Besides, the large scale of production will lead to massive amounts of waste batteries in the end. As such, recycling is seen as an end-of-pipe process to resolve sustainability and environmental concerns. The hydrometallurgical recycling is considered to be the most prominent method to recover cathode materials from spent LIBs owing to its high leaching efficiency and low energy costs. A series of procedures including pretreatment of the spent LIBs, acid leaching of the black mass, chemical co-precipitation of the hydroxide precursor, and sintering of the cathode active material need to be operated precisely. In this aspect, the impurities introduced during the process could pose a serious threat to the reaction stability as well as recycling consistency. Here, the impact of sulfide ions on recovered LiNi 0.6 Co 0.2 Mn 0.2 O 2 (NCM622) cathode material with the method of hydrometallurgy is first investigated in detail. This study shows that hydrometallurgical process is not obviously influenced by sulfide impurity. No signs of secondary phase or impurity inclusion are spotted in synthesized cathodes. Under 5 at % sulfide concentration conditions, the obtained NCM622 cathode exhibits a capacity of 159.4 mAh/g after 100 cycles at 1/3C, which is at the same level as virgin benchmark. The difference in rate performance between cathodes with and without additional sulfide is less than 2 % or even smaller. In short, the results indicate a neutral status of sulfide ions in hydrometallurgical recycling.

25 ENERGY STORAGE↗

DOE OSTI2022

Modeling assisted synthesis of Zr-doped Li 3-x In 1-x Zr x Cl 6 with ultrahigh ionic conductivity for lithium-ion batteries

All-solid-state lithium-ion batteries (ASSLBs) are an important milestone for the future of energy storage because of their capability of impressive energy density and outstanding safety. However, oxide and sulfide solid-state electrolytes (SSEs) suffer from either low ionic conductivity or poor chemical stability. In contrast, halide-based SSEs, are promising as candidate materials owing to high conductivity, good stability, and broad cathode compatibility. Though element doping of the SSEs is an effective and common approach to further improve their electrochemical properties, dopant exploration and optimization through solely experimental trials are both costly and time-consuming. For this aspect, computational simulations for dopant element and concentration screening are adopted in this research and zirconium is selected as a suitable dopant for Li 3 InCl 6 . Further, the synthesized Li 2.75 In 0.75 Zr 0.25 Cl 6 exhibited Li ionic conductivity of 5.82 x 10 -3 Scm -1 at room temperature, which is the highest among reported halide SSEs. The ASSLB formed with Li 2 CoO 2 -Li 2.75 In 0.75 Zr 0.25 Cl 6 -Li/In delivers a high initial capacity of 129.3 mAh∙g -1 . Conclusively, this work provides an effective approach which combines computational modeling and experimental verification for the development of halide SSEs with improved stability and conductivity. The successful design approach and compelling results provide further possibilities and capabilities in future SSE research.

25 ENERGY STORAGE↗

DOE OSTI2022

The Effects of Phosphate Impurity on Recovered LiNi 0.6 Co 0.2 Mn 0.2 O 2 Cathode Material via a Hydrometallurgy Method

From portable electronics to electric vehicles, lithium-ion batteries have been deeply integrated into our daily life and industrial fields for a few decades. The booming field of battery manufacturing could lead to shortages in resources and massive accumulation of battery waste, hindering sustainable development. Therefore, hydrometallurgy-based approaches have been widely used in industrial recycling to recover cathode materials due to their high efficiency and throughput. Further, impurities have always been a great challenge for hydrometallurgical recycling, introducing challenges to maintain the consistency of product quality because of potential unintended effects caused by impurities. Herein, after comprehensive investigation, we first report the impacts of phosphate impurity on a recycled LiNi 0.6 Co 0.2 Mn 0.2 O 2 ("NCM622") cathode via a hydrometallurgy method. We demonstrate that a passivation layer of Li 3 PO 4 is formed at grain boundaries during sintering, which significantly raises the activation barrier and hinders lithium diffusion. In addition, the distinct degradation of cathode electrochemical properties is observed from poor particle morphology and high cation mixing as a result of phosphate impurity. Cathode powders with 1 at. % phosphate impurity retain a capacity of 146 mAh/g after 100 cycles at 0.33C, 6% less than that of a virgin cathode. Furthermore, cathodes with higher phosphate concentrations perform even worse in electrochemical tests. Therefore, phosphate impurities are detrimental to the hydrometallurgical recycling of NCM cathode materials and need to be excluded from the recycling process.

25 ENERGY STORAGE↗

DOE OSTI2022

Underlying limitations behind impedance rise and capacity fade of single crystalline Ni-rich cathodes synthesized via a molten-salt route

Layered oxide LiNi x Mn y Co z O 2 (NMC) cathodes are often synthesized as polycrystalline secondary particles. Due to intergranular fracture stemming from volume changes of randomly oriented primary particles during charge/discharge, the synthesis of larger single-crystalline cathodes is of high interest. In this work, molten salt assisted growth of micron-sized Ni-rich crystals is achieved with excellent crystallinity, low cation mixing, and negligible impurities. However, electrochemical performance is compromised by high surface reactivity resulting in decomposition of electrolyte and subsequent formation of a thick CEI layer. While intergranular fracture is eliminated, planar gliding and severe intragranular fracture along the (003) plane occurs in the high voltage region within the first few cycles and is associated primarily with H2 to H3 structural transitions. In addition, H2 to H3 transitions are highly irreversible with cyclic voltammograms revealing polarization growth within <5 cycles. Subsequently, the single-crystalline material exhibited markedly reduced available capacity and enhanced capacity fade from sharp impedance growth compared to its polycrystalline counterpart. Here, this work furthers a fundamental understanding into the limitations of single-crystalline Ni-rich cathodes, and the obstacles limiting the advantages offered by the single-crystalline morphology.

25 ENERGY STORAGE↗

DOE OSTI2020

Understanding fundamental effects of Cu impurity in different forms for recovered LiNi 0.6 Co 0.2 Mn 0.2 O 2 cathode materials

When identifying and developing lithium ion battery recycling technologies, understanding the role of impurities is always a concern as they may have an impact on electrochemical performance, material stability, or lifetime for recovered active materials. In this work we show that Cu impurity in different forms could play very different roles on the recovered LiNi 0.6 Co 0.2 Mn 0.2 O 2 (NCM622). Cu metal impurity could easily short the cell, while Cu ion impurity could play a positive role due to partially substitution of the Ni 2+ sites to lower the cation mixing degree. In specific, NCM622 material with certain amount (0.34 at%) of Cu ion impurity delivers high initial specific charge/discharge capacity of 211.8 and 186.0 mAh g -1 at 0.05 C, which are 12.2 and 14.1 mAh g -1 higher than those of virgin NCM622 cathode. Moreover, a superior retention capacity of 171.3 mAh g -1 after 90 cycles at 0.33 C, and striking rate capability are achieved in this NCM622 cathode sample. These results clearly indicate that Cu metal impurity should be avoided and the ionic Cu impurity should be controlled with optimal concentration during recycling process for spent LIBs.

25 ENERGY STORAGE↗