STUDIES ON PIPELINE POLYETHYLENES IN HYDROGEN GAS ENVIRONMENTS USING IN-SITU AND EX-SITU CHARACTERIZATION METHODS

Polymeric materials are commonplace in the natural gas infrastructure as distribution pipes, coatings, seals, and gaskets. Under the auspices of the U.S. Department of Energy HyBlend program, one of the means to reduce greenhouse gas emissions is with replacing natural gas, either partially or completely, with hydrogen. This approach makes it imperative that we conduct near-term and long-term materials compatibility research in these relevant environments. Insights into the effects of hydrogen and hydrogen gas blends on polymer integrity can be gained through both ex-situ and in-situ analytical methods. Our work represented here highlights a study of the behavior of pipeline polyethylene (PE) materials, including HDPE (Dow 2490 and GDB50) and MDPE (Ineos and legacy Dupont Aldyl A), when exposed to hydrogen by means of in-situ X-ray scattering and ex-situ Raman spectroscopy techniques. Samples were tested in ex-situ hydrogen and argon gas environments and in-situ hydrogen environments to identify differences due to permeation and solubility of these gases. These methods complemented each other because Raman spectroscopy could capture permanent effects after materials were removed from gaseous environments, and in-situ X-ray scattering analysis collected real-time data to elucidate the impact of the gas environment on polymer microstructure. Data collected revealed that the aforementioned polymers did not show significant changes in crystallinity and microstructure under the exposure conditions tested. Our findings from these studies will help establish real-time effects caused by hydrogen gas transport through pipeline polyethylenes by way of its influence on polymer structure and chemistry, which is directly related to pipeline mechanical strength and longevity of service.

Hydrogen materials compatibility, Natural gas pipe↗
DOE OSTI2023

Accelerated Aging Scoping Study of Additively Manufactured Coupons

Additive manufacturing (AM) is a relatively new technological advancement that allows for rapid prototyping, development of intricate shapes, and reduction in manufacturing time. The materials of interest for this project are Ultem 1010, ABS M30, FDM Nylon 12, PC, and PPSF. However, little is known regarding the aging behavior of these AM materials. The limited aging study outlined herein was designed to compare the chemical, physical, and mechanical properties of AM parts as they experience accelerated aging at 70 °C for a total of 24 weeks. In general, ABS M30 stood out as it appeared to undergo chemical and physical changes leading to increase in density and an overall more brittle material, making this commonly used material not attractive for long-term use.

36 MATERIALS SCIENCE↗
DOE OSTI2020

Dispenser Reliability: Materials R&D. A Hydrogen Fueling Infrastructure Research and Station Technology (H2FIRST) Report

Dispensers are the top cause of maintenance events and down-time at hydrogen fueling stations. In an effort to help characterize and enable improvements in dispenser reliability, an extensive accelerated lifetime testing set-up was designed and built at NREL involving components typically part of dispensing operations at fueling stations. Device Under Test (DUTs) included different components such as normally open valves, normally closed valves, fueling nozzles, breakaways devices and filters. Conditions of testing included pressures, and flow rates similar to light duty fuel cell electric vehicles fueling at -40°C, and -20°C for thousands of cycles in hydrogen. Tested components (failed and non-failed) were disassembled at SNL and polymeric O-rings were carefully retrieved and cataloged for chemical and physical characterization. Data collected was compared to similar O-rings from unexposed or non-tested components for hydrogen effects, and failure modes. Degradation analyses, based on select polymer chemistries common across all component types, their location within components, visual assessment of damage coupled with strong hydrogen effects from chemical characterization, was completed and presented to NREL and DOE. Overall, the failure rate amongst the components was not as high as expected for the test conditions. Among the component types tested, breakaways were the most susceptible to damage under these test conditions, with fueling nozzles a close second. The proper combination of selection of the right polymer and optimum component design was found to make a strong difference in component reliability under severe dispenser operating conditions. Physical degradation of polymers, rather than chemical changes due to low temperature hydrogen exposure, is more prevalent as failure mode for these test conditions. The nature and the extent of the degradation was much less at -20°C as compared to -40°C. The damage and failure rates were higher at lower temperatures than at higher test temperatures. As expected, increasing the number of cycles at the lowest test temperature (-40°C) increased damage. This indicates that cycling at the low temperature of -40°C required by SAE J2601 can reduce component life in fuel dispensing operations

08 HYDROGEN↗
DOE OSTI2019

Compatibility of polymers in super-critical carbon dioxide for power generation systems: High level findings for low temperatures and pressure conditions

Polymers such as PTFE (polytetrafluorethylene or Teflon), PEEK (polyetheretherketone), EPDM (ethylene propylene cliene monomer) rubber, Viton, EPR (ethylene propylene rubber), Nylon, Nitrile rubber, and perfluoroelastomers are commonly employed in super critical CO 2 (sCO2) energy conversion systems. O-rings and gaskets made from these polymers face stringent performance conditions such as elevated temperatures, high pressures, pollutants and corrosive humid environments. Critical knowledge gaps about polymer degradation from sCO2 exposure need to be addressed. To understand these effects, we have studied nine commonly used polymers subjected to elevated temperatures under isobaric conditions of sCO2 pressure. The polymers (PEEK, Nylon, PTFE, EPDM, Nitrile rubber, EPR, Neoprene, perfluoroelastomer FF 202 and Viton) were exposed for 1000 hours at 100°C to 25 MPa sCO2 pressure in an autoclave. In a second study, elastomers perfluoroelastomer (FF202) and EPDM were exposed to 25 MPa sCO2 for 1000 hours at 150°C. Samples were extracted for ex-situ characterization at t = 200 hours and then at the completion of the test at t=1000 hours. The polymer samples were examined for physical and chemical changes by Dynamic Mechanical and Thermal Analysis (DMTA), Fourier Transform Infrared (FTIR) spectroscopy, and compression set. Density and mass changes immediately after removal from test and 48 hours later, and optical microscopy techniques were also used. Microcomputer tomography (micro CI) data was generated on select specimens. Super-critical CO 2 effects have been identified as either physical or chemical effects. For each polymer, the dominance of one type of effect over the other was evaluated. Attempts were also made to qualitatively link sCO2 effects such as lowering or increase in glass transition temperatures, storage modulus changes, mass and compression set changes, chemical changes seen in FTIR analyses and blister and void formation seen post-exposure to polymer microstructure-related mechanisms such as plasticization of the polymer matrix, escape of volatiles from the polymer during depressurization, and filler and plasticizer effects on microstructure with rapid depressurization rates.

36 MATERIALS SCIENCE↗