DOE OSTI2024

Quantification of Swelling in Hematite Pellets Reduced Using Hydrogen–Nitrogen Gas Mixture

Iron ore pellets are reduced in a 50%H 2 –50%N 2 1 atm gas mixture at 750, 800, 850, 900, and 950 °C while simultaneously documenting swelling (change in pellet radius) and weight change. Swelling increases with increasing temperature, with catastrophic swelling (>20% of reduction swelling index) observed at 850, 900, and 950 °C. As the pellet is reduced, the pellet radius increases until 40–50% reduction is achieved, followed by a decrease in diameter beyond 40–50% reduction at 750 and 850 °C. At 950 °C, the pellet radius continues to increase with additional pellet reduction without any subsequent decrease in diameter. Scanning electron microscopy (SEM) analysis shows that the neighboring grains inside the pellet sinter together at 750 and 850 °C, whereas the individual grains sinter internally at 950 °C. SEM analysis and observations suggest that the reduction process at 750 and 850 °C can be approximated as a topochemical reaction process, while the reduction process at 950 °C can no longer be approximated as a topochemical reaction process. In conclusion, an empirical equation for the radius of the pellet is derived with fitting parameters dependent on temperature and the degree of reduction of the pellet undergoing reduction based on the experimental data.

08 HYDROGEN↗

DOE OSTI2023

Modeling the First Hydrogen Direct Reduction Pilot Reactor for Ironmaking in the USA Using Finite Element Analysis and Its Validation Using Pilot Plant Trial Data

Direct reduction of hematite pellets with hydrogen (H 2 ) was used to produce directly reduced iron (DRI) in a pilot scale reactor at a pellet feed rate of 21.4 kg/h. At a steady state, operational parameters of the pilot plant (gas recycling rate and inlet temperature) along with key reactor output parameters, the pellet metallization, and the internal temperature profile of the reactor were reported for two scenarios with high recycle and low recycle rate of H 2 . Scenario 1, with a high recycle rate of 400 L/min H 2 along with external heating of 870 °C, gave an average metallization of 91.8%, while Scenario 2, with low recycle rate of 100 L/min H 2 and external heating of 850 °C gave a metallization of 67.8% due to the higher moles of H 2 available for reduction and the external energy required for the endothermic reduction reaction in Scenario 1 as compared with Scenario 2. Finite element analysis was used to build a model of the shaft reactor, which was validated against the metallization and internal temperature profile data. The average metallization values predicted by the model were very close to the metallization values obtained from the pilot plant samples, with 90.9% average metallization for Scenario 1 and 65.6% average metallization for Scenario 2. The internal temperature profiles in the lower region of the reactor obtained from the model were very close to these pilot plant data, with a maximum difference of 52.7 °C and 67.6 °C for Scenarios 1 and 2, respectively. The pilot plant reactor model was used extensively in the commissioning of the pilot plant and to predict the startup outcomes for a given set of operating parameters.

08 HYDROGEN↗

DOE OSTI2023

Reduction of Iron‐Ore Pellets Using Different Gas Mixtures and Temperatures

Direct reduction of iron ore (DRI) is gaining an increased attention due to the growing need to decarbonize industrial processes. The current industrial DRI processes are performed using reformed natural gas, which results in CO 2 emission, although it is less than carbothermic reduction in the blast furnace. Carbon‐free reduction may be realized through the utilization of green H 2 as a reducing agent, in place of natural gas. Herein, the effects of various gas mixtures and temperature on the reduction kinetics of the hematite iron‐ore pellets are focused on in this work. Pellets are reduced at 700, 800, 850, and 900 °C in hydrogen and using various gas mixes at 850 °C. Morphology of the pellets is investigated with the help of scanning electron microscopy and mercury intrusion porosimetry. The effects of temperature and gas composition on the reduction kinetics and porosity of the pellets are discussed. A notable effect of reduction rate on the internal structure of the pellets is detected, slower reduction rate yielded bigger pores offsetting the gas composition. Higher temperature results in coarser pores and higher porosity. Finally, increase of CO content in the gas mix also leads to bigger pore size.

36 MATERIALS SCIENCE↗