NASA NTRS1976

Heat shield characterization: Outer planet atmospheric entry probe

A full scale carbon phenolic heat shield was fabricated for the Outer Planet Probe in order to demonstrate the feasibility of molding large carbon phenolic parts with a new fabrication processing method (multistep). The sphere-cone heat shield was molded as an integral unit with the nose cap plies configured into a double inverse chevron shape to achieve the desired ply orientation. The fabrication activity was successful and the feasibility of the multistep processing technology was established. Delaminations or unbonded plies were visible on the heat shield and resulted from excessive loss of resin and lack of sufficient pressure applied on the part during the curing cycle. A comprehensive heat shield characterization test program was conducted, including: nondestructive tests with the full scale heat shield and thermal and mechanical property tests with small test specimen.

Mezines, S. A.↗

NASA NTRS1976

Experimental evaluation of outer planets probe thermal insulation concepts

An experimental program was conducted to evaluate various thermal insulation concepts for use in the Outer Planets Probe (OPP) during entry and descent into the atmospheres of Jupiter, Saturn, and Uranus. Phenolic fiberglass honeycomb specimens representative of the OPP structure were packed and tested with various fillers: Thermal conductivity measurements were made over a temperature range of 300 K to 483 K and pressures from vacuum up to 10 atmospheres in helium and nitrogen gas environments. The conductivity results could not be fully explained so new test specimens were designed with improved venting characteristics, and tested to determine the validity of the original data. All of the conductivity data showed results that were substantially higher than expected. The original test data in helium were lower than the data from the redesigned specimens, probably due to inadequate venting of nitrogen gas from the original specimens. The thermal conductivity test results show only a marginal improvement in probe thermal protection performance for a filled honeycomb core compared to an unfilled core. In addition, flatwise tension tests showed a severe bond strength degradation due to the inclusion of either the powder or foam fillers. In view of these results, it is recommended that the baseline OPP design utilize an unfilled core.

Grote, M. G.↗

NASA NTRS1974

Outer planet probe entry thermal protection. II - Heat shielding requirements

Solutions are presented for the material thermal response for heat shields of blunt probes entering Saturn and Uranus. Both monolithic and sandwich concepts were considered having exposed charring ablative or reflective materials. The solutions show that (1) Teflon heat shields are sized by mass loss considerations, other materials (unless entering the Uranus cold-dense atmosphere) by heat soak considerations, (2) steeper entries require less heat shield mass, (3) sizing requirements vary little about the bodies for heat soak dominated materials, and (4) carbon-phenolic appears superior overall, but silica is superior for the steeper entries and the high helium content atmospheres.

Nicolet, W. E.↗