Grain boundary formation through particle detachment during coarsening of nanoporous metals

Significance Nanoporous metals are prototypical bicontinuous structures that have a large surface area and many applications. We demonstrate that an in-grain orientation spread develops during coarsening in nanoporous metals, leading to the formation of a nanocrystalline–nanoporous structure. The process of particles detaching and reattaching as the structure coarsens is identified as a mechanism of grain boundary formation. Coarsening the structure results in significant particle detachment with detachment rates that vary drastically with changes in the volume fraction and volume fraction inhomogeneities in the nanostructure. These results demonstrate that particle detachment must be understood to have full control of the nanocrystalline–nanoporous structure and improve material properties.

36 MATERIALS SCIENCE↗

DOE OSTI2021

Simultaneous Multi-Bragg Peak Coherent X-ray Diffraction Imaging

The simultaneous measurement of two Bragg reflections by Bragg coherent X-ray diffraction is demonstrated on a twinned Au crystal, which was prepared by the solid-state dewetting of a 30 nm thin gold film on a sapphire substrate. The crystal was oriented on a goniometer so that two lattice planes fulfill the Bragg condition at the same time. The Au 111 and Au 200 Bragg peaks were measured simultaneously by scanning the energy of the incident X-ray beam and recording the diffraction patterns with two two-dimensional detectors. While the former Bragg reflection is not sensitive to the twin boundary, which is oriented parallel to the crystal–substrate interface, the latter reflection is only sensitive to one part of the crystal. The volume ratio between the two parts of the twinned crystal is about 1:9, which is also confirmed by Laue microdiffraction of the same crystal. The parallel measurement of multiple Bragg reflections is essential for future in situ and operando studies, which are so far limited to either a single Bragg reflection or several in series, to facilitate the precise monitoring of both the strain field and defects during the application of external stimuli.

47 OTHER INSTRUMENTATION↗