Failure analysis of solid oxide fuel cells nickel-yttria stabilized zirconia anode under siloxane contamination
In this study, the failure process of the solid oxide fuel cell (SOFC) Ni-yttria-stabilized zirconia (YSZ) anode is investigated with D4 siloxane (octamethylcyclotetrasiloxane) contamination. In order to evaluate the influence of the electrochemical reaction on the siloxane deposition process, the SOFC experiments were operated at open circuit voltage (OCV) and 50 mA cm -2 conditions at 800°C. During the failure process, electrochemical, morphology and exhaust gas component analysis testing are conducted at the critical points. An equivalent circuit model and corresponding microstructure parameter calculations for separated physicochemical processes were utilized for the quantitative analysis of the failure process. Further, the results confirm the siloxane chemical adsorption deposition mechanism proposed in previous work. As a result, the failure of the anode was attributed to the gas diffusion blockage by dense silicon dioxide layer formation. The anode failure process with siloxane contamination is faster when the anode is operated under polarization.
25 ENERGY STORAGE↗
An energy storage dispatch optimization for demand-side management in industrial facilities
An energy storage (ES) dispatch optimization was implemented to test lithium-ion battery ES, supercapacitor ES, and compressed air ES on two different industrial facilities – one intermittent process facility and one continuous process facility. The model first shows the capability of optimizing the size of a single technology on a single industrial facility to maximize the return on investment. Then, for the same profile, the model identifies significant differences in the optimal size for different technologies based on their performance parameters. Third, the model identifies differences in the optimal size for each technology based on the facilities profile. Here the results show compressed air ES yields the highest return on investment for both facilities and provides insight for future development of ES systems.
25 ENERGY STORAGE↗
Investigating the Influence of Ni, ZrO 2 , and Y 2 O 3 from SOFC Anodes on Siloxane Deposition
Siloxanes, as a type of impurity in biogas, can poison the Ni-YSZ anode of SOFCs. However, the influence of individual components of the anode, such as Ni, ZrO 2 , and Y 2 O 3 , on the siloxane deposition process has not been investigated extensively. In this study, Ni, ZrO 2 , and Y 2 O 3 pellets were exposed to H 2 + N 2 + H 2 O + D4 (octamethylcyclotetrasiloxane, 2.5 ppmv) and H 2 + N 2 + D4 (2.5 ppmv siloxane) gas mixtures at 750 °C to investigate their affinity and tolerance for siloxane degradation. Surface morphology analysis and electrochemical analysis including electrochemical impedance spectroscopy (EIS), related distribution of relaxation times (DRT) analysis and equivalent circuit modeling with complex nonlinear least square (CNLS) fitting were conducted. Here, a microstructure parameter—tortuosity factor to porosity ratio $\tau /\varepsilon $ calculated by diffusion polarization resistance was utilized for siloxane deposition evaluation. After comparing pellets surface morphology changes before and after experiments and $\tau /\varepsilon $ change following the contamination, Ni is considered as a major factor in siloxane deposition reactions in Ni-YSZ anode.
25 ENERGY STORAGE↗
Degradation Comparison of Cyclic and Linear Siloxane Contamination on Solid Oxide Fuel Cells Ni-YSZ Anode
The solid oxide fuel cell (SOFC) nickel-yttria stabilized zirconia (Ni-YSZ) anode degradation due to different types of siloxane contamination is investigated. A cyclic structure siloxane, octamethylcyclotetrasiloxane (D4), and a linear structure siloxane, decamethyltetrasiloxane (L4), are mixed with H 2 +N 2 as the fuel for SOFCs at 750°C. The electrochemical characterization results after stability experiments suggest that the SOFC contaminated with cyclic siloxane, D4, had higher degradation. Pure YSZ pellets with different surface hydroxylation extents were also tested to investigate the D4/L4 adsorption and deposition process. Postmortem SEM/WDS, XRD and Raman analysis all indicate that cyclic siloxane has more deposition than linear siloxane on the anode. Further analysis demonstrates that high adsorption and low desorption rates of cyclic siloxane on YSZ are linked to the degradation. Besides the silicon deposition, SiC and amorphous carbon deposition were also observed from the XRD and Raman analysis.
25 ENERGY STORAGE↗
A review of energy storage technologies for demand-side management in industrial facilities
Demand-side management (DSM) in industrial facilities provides an opportunity for substantial amounts of energy cost savings, since industrial facilities are the largest energy consuming sectors globally. In this work, energy storage (ES) technologies are critically reviewed and compared with industrial DSM in mind. ES technologies reviewed herein include lithium-ion battery energy storage (BES), sodium-sulfur BES, lead-acid BES, flow BES, supercapacitor ES, superconducting magnetic ES, thermal ES, flywheel ES, pumped hydro ES, and compressed air ES. The fundamentals of these energy storage technologies are reviewed in detail including recent developments, followed by case studies and extensive comparisons. These comparisons include, but are not limited to cost per cycle analyses, levelized cost of energy analyses, and comparisons between performance, transient, and cost characteristics. Here, some key properties analyzed include the rated power, power density, efficiency, lifetime, discharge time, capital costs, and O&M costs.
25 ENERGY STORAGE↗
Siloxane Deposition on the Ni-YSZ Solid Oxide Fuel Cell Anode Exposed to Bio-Syngas
Siloxane, a common contaminant present in biogas, is known for adverse effects on cogeneration prime movers. In this study, the siloxane deposition products and mechanism in the solid oxide fuel cell nickel-yttria stabilized zirconia (Ni-YSZ) anode are investigated analytically and experimentally. An SOFC with Ni-YSZ anode and pure Ni/YSZ pellets were exposed to a simulated biogas-reformate fuel with octamethylcyclotetrasiloxane (D4) contamination at 750 °C. The electrochemical characterization results show that the SOFCs performance degradation caused by D4 contamination is irreversible. Morphology and XRD results illustrate that silicon and carbon deposition can both be detected in the anode and pellets. Graphite, SiC and SiO2 are all possible products based on the results of XRD test. Here, according to the formation of graphite and SiC, the new mechanism suggests that carbon is also an essential factor in siloxane contamination of Ni-YSZ anodes besides silicon, which can be explained by the catalytic and electrochemical analysis.
25 ENERGY STORAGE↗
Investigation of Rapid, Moderate Temperature Change Thermal Cycles of a Micro-Tubular Flame-Assisted Fuel Cell
Despite many efforts and improvements over the last few decades, two of the major challenges facing solid oxide fuel cells (SOFCs) are slow heating rates to operating temperature (typically < 5 °C · min–1) and a limited ability to thermal cycle (<200 cycles). Recently, a novel hybrid setup that combines a fuel-rich combustion reformer with a SOFC was developed and utilized to investigate rapid heating, cooling, and thermal cycling of a micro-tubular SOFC. In this work, 3000 moderate thermal cycles are conducted at a heating rate exceeding 140 °C · min–1 and a cooling rate that exceeded 100 °C · min–1. The open-circuit voltage (OCV) was analyzed over the 150 h test, and a low degradation rate of ~0.0008 V per 100 cycles per fuel cell was observed in the absence of the current collector degradation. Unlike a previous test, which was conducted at lower temperatures, significant degradation of the current collector was observed during this test. Electrochemical impedance spectroscopy shows that degradation in the SOFC was due to increases in ohmic losses, activation losses at the cathode, and increased concentration losses.
Electrochemistry↗
Micro-Tubular Solid Oxide Fuel Cell Polarization and Impedance Variation With Thin Porous Samarium-Doped Ceria and Gadolinium-Doped Ceria Buffer Layer Thickness
Abstract Porous buffer layers for anode-supported solid oxide fuel cells (SOFCs) have been investigated for many years with different thicknesses of the buffer layer in each study. In this work, micro-tubular SOFCs having samarium-doped ceria (SDC) and gadolinium-doped ceria (GDC) buffer layers are compared using the current–voltage technique, electrochemical impedance spectroscopy, scanning electron microscopy, and energy-dispersive X-ray spectroscopy. The thickness of the porous SDC and GDC buffer layer is investigated systematically with the thickness varying between 0.3 and 2.0 μm. The power density varies between 212 and 1004 mW/cm2 for samples having different SDC buffer layer thickness. Comparable changes occur for the SOFCs with a GDC buffer layer, but less variation in polarization losses resulted. Variation in electrochemical performance varies due to changes in ohmic resistance, cathode activation polarization, and interfacial reactions between the cathode and electrolyte materials.
Electrochemistry↗
Investigation of startup, performance and cycling of a residential furnace integrated with micro-tubular flame-assisted fuel cells for micro-combined heat and power
Solid Oxide Fuel Cells (SOFCs) offer advantages for micro-Combined Heat and Power (μCHP), but currently suffer from slow startup (>1 h) and limited thermal cycling which reduces the applications, energy savings and economics. In this work, a micro-Tubular SOFC stack is integrated into a residential furnace to create a micro-Tubular Flame-assisted Fuel Cell (mT-FFC) μCHP system. A high power density of 202 mW cm -2 is reported operating in synthesis gas generated from fuel-rich combustion of natural gas/air. Unlike previous reports, instabilities in the polarization are attributed to low temperature of the oxygen reduction reaction at the cathode. The mT-FFC stack achieved peak power density in 6 min after ignition. 200 thermal cycles at an average heating rate of 215 °C.min -1 and average cooling rate of 176 °C.min -1 were conducted and a low degradation rate of 0.0325 V per 100 cycles per fuel cell was achieved. Low NO x emissions (10 ppm) and high combined efficiency is reported.
25 ENERGY STORAGE↗