The room temperature tensile and fatigue response of non-perforated and perforated titanium for laminar flow control application was investigated both experimentally and analytically. Results showed that multiple perforations did not affect the tensile response, but did reduce the fatigue life. A two dimensional finite element stress analysis was used to determine that the stress fields from adjacent perforations did not influence one another. The stress fields around the holes did not overlap one another, allowing the materials to be modeled as a plate with a center hole. Fatigue life was predicted using an equivalent MW flow size approach to relate the experimental results to microstructural features of the titanium. Predictions using flaw sizes ranging from 1 to 15 microns correlated within a factor of 2 with the experimental results by using a flow stress of 260 MPa. By using two different flow stresses in the crack closure model and correcting for plasticity, the experimental results were bounded by the predictions for high applied stresses. Further analysis of the complex geometry of the perforations and the local material chemistry is needed to further understand the fatigue behavior of the perforated titanium.
Johnson, W. Steven↗
Impact damage resistance and residual property assessment of (0/+/-45/90)s SCS-6/Timetal 21S
The impact damage resistance and residual mechanical properties of (0/ +/- 45/90)s SCS-6/Timetal 21S composites were evaluated. Both quasi-static indentation and drop-weight impact tests were used to investigate the impact behavior at two nominal energy levels (5.5 and 8.4 J) and determine the onset of internal damage. Through x-ray inspection, the extent of internal damage was characterized non-destructively. The composite strength and constant amplitude fatigue response were evaluated to assess the effects of the sustained damage. Scanning electron microscopy was used to characterize internal damage from impact in comparison to damage that occurs during mechanical loading alone. The effect of stacking sequence was examined by using specimens with the long dimension of the specimen both parallel (longitudinal) and perpendicular (transverse) to the 0 deg fiber direction. Damage in the form of longitudinal and transverse cracking occurred in all longitudinal specimens tested at energies greater than 6.3 J. Similar results occurred in the transverse specimens tested above 5.4 J. Initial load drop, characteristic of the onset of damage, occurred on average at 6.3 J in longitudinal specimens and at 5.0 J in transverse specimens. X-ray analysis showed broken fibers in the impacted region in specimens tested at the higher impact energies. At low impact energies, visible matrix cracking may occur, but broken fibers may not. Matrix cracking was noted along fiber swims and it appeared to depend on the surface quality of composite. At low impact energies, little damage has been incurred by the composite and the residual strength and residual life is not greatly reduced as compared to an undamaged composite. At higher impact energies, more damage occurred and a greater effect of the impact damage was observed.