NASA NTRS2018

Segregation-Assisted Plasticity in Ni-Based Superalloys

Correlative high resolution transmission electron microscopy and energy dispersive X-ray spectroscopy are used to study deformation-induced planar faults in the single crystal superalloy MD2 crept at 800°C and 650 MPa. Segregation of Cr and Co at microtwins, APBs, CISFs/SISFs and CESFs/SESFs is confirmed and quantified. The extent of this is found to depend upon the fault type, being most pronounced for the APB. The CESF/SESF is studied in detail due to its role as a precursor of the microtwins causing the majority of plasticity under these conditions. Quantitative modelling is carried out to rationalize the findings; the experimental results are consistent with a greater predicted velocity for the lengthening of the CESF/SESF { compared with the other types of fault { and hence confirm its role in the diffusion-assisted plasticity needed for the microtwinning mechanism to be operative.

Barba, D.↗

NASA NTRS2018

Segregation and Phase Transformations Along Superlattice Intrinsic Stacking Faults in Ni-Based Superalloys

In this study, local chemical and structural changes along superlattice intrinsic stacking faults combine to represent an atomic-scale phase transformation. In order to elicit stacking fault shear, creep tests of two different single crystal Ni-base superalloys, ME501 and CMSX-4, were performed near 750 degrees Centigrade using stresses of 552 megapascals and 750 megapascals, respectively. Through high resolution Scanning Transmission Electron Microscopy (STEM) and state-of-the-art energy dispersive x-ray spectroscopy, ordered compositional changes were measured along SISFs (Superlattice Intrinsic Stacking Faults) in both alloys. For both instances, the elemental segregation and local crystal structure present along the SISFs are consistent with a nanoscale to D019 (ordering of a hexagonal close-packed crystal) phase transformation. Another notable observation is prominent Cr- and Co-rich Cottrell atmospheres and new evidence of more complex reordering processes responsible for the formation of these faults. These findings are further supported using density functional theory calculations and High Angle Annular Dark Field (HAADF) STEM image simulations.

STEM-EDS↗

NASA NTRS2003

Observations of Glide and Decomposition of a<101> Dislocations at High Temperatures in Ni-Al Single Crystals Deformed along the Hard Orientation

Ni-44at.% Al and Ni-50at.% single crystals were tested in compression in the hard (001) orientations. The dislocation processes and deformation behavior were studied as a function of temperature, strain and strain rate. A slip transition in NiAl occurs from alpha(111) slip to non-alphaaaaaaaaaaa9111) slip at intermediate temperatures. In Ni-50at.% Al single crystal, only alpha(010) dislocations are observed above the slip transition temperature. In contrast, alpha(101)(101) glide has been observed to control deformation beyond the slip transition temperature in Ni-44at.%Al. alpha(101) dislocations are observed primarily along both (111) directions in the glide plane. High-resolution transmission electron microscopy observations show that the core of the alpha(101) dislocations along these directions is decomposed into two alpha(010) dislocations, separated by a distance of approximately 2nm. The temperature window of stability for these alpha(101) dislocations depends upon the strain rate. At a strain rate of 1.4 x 10(exp -4)/s, lpha(101) dislocations are observed between 800 and 1000K. Complete decomposition of a alpha(101) dislocations into alpha(010) dislocations occurs beyond 1000K, leading to alpha(010) climb as the deformation mode at higher temperature. At lower strain rates, decomposition of a alpha(101) dislocations has been observed to occur along the edge orientation at temperatures below 1000K. Embedded-atom method calculations and experimental results indicate that alpha(101) dislocation have a large Peieris stress at low temperature. Based on the present microstructural observations and a survey of the literature with respect to vacancy content and diffusion in NiAl, a model is proposed for alpha(101)(101) glide in Ni-44at.%Al, and for the observed yield strength versus temperature behavior of Ni-Al alloys at intermediate and high temperatures.

Srinivasan, R.↗

NASA NTRS1992

On the age of stratospheric air and ozone depletion potentials in polar regions

Observations of the nearly inert, man-made chlorofluorocarbon CFC-115 obtained during January 1989 are used to infer the age of air in the lower stratosphere. These observations together with estimated release rates suggest an average age of high-latitude air at pressure altitudes near 17-21 km of about 3 to 5 yr. This information is used together with direct measurements of HCFC-22, HCFC-142b, CH3Br, H-1301, H-1211, and H-2402 to examine the fractional dissociation of these species within the Arctic polar lower stratosphere compared to that of CFC-11 and hence to estimate their local ozone depletion potentials in this region. It is shown that these HCFCs are much less efficiently dissociated within the stratosphere than CFC-11, lowering their ozone depletion potentials to only about 30-40 percent of their chlorine loading potentials. In contrast, the observations of CH3Br and the Halons considered confirm that they are rapidly dissociated within the stratosphere, with important implications for their ozone depletion potentials.