Iodine Modulates the MACl‐Assisted Growth of FAPbI 3 for High Efficiency Perovskite Solar Cells

The preferential growth of α-phase formamidinium perovskite (α-FAPbI 3 ) at low temperatures can be achieved with the incorporation of chloride-based additives, with methylammonium chloride (MACl) being the most common example. However, compared to other less-volatile chloride additives, MACl only remains in the growing perovskite film for a short time before evaporating during annealing, primarily influencing the early stages of film formation. In addition, evaporation of MACl as methylamine (MA 0 ) and HCl can introduce a side reaction between MA 0 and formamidinium (FA), undermining the compositional purity and phase stability of α-FAPbI 3 . In this study, it is demonstrated that addition of iodine (I 2 ) into the FAPbI 3 precursor solution containing MACl suppresses the MA-FA side reaction during annealing. Additionally, MACl evaporation is delayed owing to strong interaction with triiodide. The added I 2 facilitates spontaneous growth of α-FAPbI 3 prior to annealing, with an improved bottom morphology due to the formation of fewer byproducts. Perovskite solar cells derived from an I 2 -incorporated solution deliver a champion power conversion efficiency of 25.2% that is attributed to suppressed non-radiative recombination.

14 SOLAR ENERGY↗

DOE OSTI2022

Hot-Casting-Assisted Liquid Additive Engineering for Efficient and Stable Perovskite Solar Cells

High-performance inorganic–organic lead halide perovskite solar cells (PSCs) are often fabricated with a liquid additive such as dimethyl sulfoxide (DMSO), which retards crystallization and reduces roughness and pinholes in the perovskite layers. However, DMSO can be trapped during perovskite film formation and induce voids and undesired reaction byproducts upon later processing steps. Here, it is shown that the amount of residual DMSO can be reduced in as-spin-coated films significantly through use of preheated substrates, or a so-called hot-casting method. Hot casting increases the perovskite film thickness given the same concentration of solutions, which allows for reducing the perovskite solution concentration. By reducing the amount of DMSO in proportion to the concentration of perovskite precursors and using hot casting, it is possible to fabricate perovskite layers with improved perovskite–substrate interfaces by suppressing the formation of byproducts, which increase trap density and accelerate degradation of the perovskite layers. The best-performing PSCs exhibit a power conversion efficiency (PCE) of 23.4% (23.0% stabilized efficiency) under simulated solar illumination. Furthermore, encapsulated devices show considerably reduced post-burn-in decay, retaining 75% and 90% of their initial and post-burn-in efficiencies after 3000 h of operation with maximum power point tracking (MPPT) under high power of ultraviolet (UV)-containing continuous light exposure.

perovskite-substrate interface↗