Fatigue crack growth under general-yielding cyclic-loading

In low cycle fatigue, cracks are initiated, and propagated under general-yielding cyclic loading. For general-yielding cyclic loading, Dowling and Begley (1976) have shown that fatigue crack growth rate correlates well with the measured Delta J. The correlation of da/dN with Delta J has also been studied by a number of other investigators. However, none of these studies has correlated da/dN with Delta J calculated specifically for the test specimens. Solomon measured fatigue crack growth in specimens in general-yielding cyclic loading. The crack tip fields for Solomon's specimens are calculated, using the finite element method, and the J-values of Solomon's tests are evaluated. The measured crack growth rate in Solomon's specimens correlates very well with the calculated Delta J.

Minzhong, Z.↗

NASA NTRS1986

Fatigue crack growth under general-yielding cyclic-loading

In low cycle fatigue, cracks are initiated and propagated under general yielding cyclic loading. For general yielding cyclic loading, Dowling and Begley have shown that fatigue crack growth rate correlates well with the measured delta J. The correlation of da/dN with delta J was also studied by a number of other investigators. However, none of thse studies have correlated da/dN with delta J calculated specifically for the test specimens. Solomon measured fatigue crack growth in specimens in general yielding cyclic loading. The crack tips fields for Solomon's specimens are calculated using the finite element method and the J values of Solomon's tests are evaluated. The measured crack growth rate in Solomon's specimens correlates very well with the calculated delta J.

Minzhong, Z.↗

NASA NTRS1984

Crack tip field and fatigue crack growth in general yielding and low cycle fatigue

Fatigue life consists of crack nucleation and crack propagation periods. Fatigue crack nucleation period is shorter relative to the propagation period at higher stresses. Crack nucleation period of low cycle fatigue might even be shortened by material and fabrication defects and by environmental attack. In these cases, fatigue life is largely crack propagation period. The characteristic crack tip field was studied by the finite element method, and the crack tip field is related to the far field parameters: the deformation work density, and the product of applied stress and applied strain. The cyclic carck growth rates in specimens in general yielding as measured by Solomon are analyzed in terms of J-integral. A generalized crack behavior in terms of delta is developed. The relations between J and the far field parameters and the relation for the general cyclic crack growth behavior are used to analyze fatigue lives of specimens under general-yielding cyclic-load. Fatigue life is related to the applied stress and strain ranges, the deformation work density, crack nucleus size, fracture toughness, fatigue crack growth threshold, Young's modulus, and the cyclic yield stress and strain. The fatigue lives of two aluminum alloys correlate well with the deformation work density as depicted by the derived theory. The general relation is reduced to Coffin-Manson low cycle fatigue law in the high strain region.

Minzhong, Z.↗