Phase Morphology Dependence of Ionic Conductivity and Oxidative Stability in Fluorinated Ether Solid-State Electrolytes
Not Available
37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗
Engineering topics
Mirmira, Priyadarshini
Publications and source records attributed to Mirmira, Priyadarshini.
Low melting alkali-based molten salt electrolytes for solvent-free lithium-metal batteries
Not provided.
Materials Science↗
Co-intercalation-free ether electrolytes for graphitic anodes in lithium-ion batteries
Carbonate-based electrolytes are widely used in Li-ion batteries but are limited by a small operating temperature window and poor cycling with silicon-containing graphitic anodes. The lack of non-carbonate electrolyte alternatives such as ether-based electrolytes is due to undesired solvent co-intercalation that occurs with graphitic anodes. Here, we show that fluoroethers are the first class of ether solvents to intrinsically support reversible lithium-ion intercalation into graphite without solvent co-intercalation at conventional salt concentrations. In full cells using a graphite anode, they enable 10-fold higher energy densities compared to conventional ethers, and better thermal stability over carbonate electrolytes (operation up to 60 °C) by producing a robust solvent-derived solid electrolyte interphase (SEI). As single-solvent–single-salt electrolytes, they remarkably outperform carbonate electrolytes with fluoroethylene carbonate (FEC) and vinylene carbonate (VC) additives when cycled with graphite–silicon composite anodes. In conclusion, our molecular design strategy opens a new class of electrolytes that can enable next generation Li-ion batteries with higher energy density and a wider working temperature window.
25 ENERGY STORAGE↗
Non-Conductive Polymers Enable Higher Ionic Conductivities and Suppress Reactivity in Hybrid Sulfide-Polymer Solid State Electrolytes
Hybrid ceramic-polymer solid state electrolytes are promising candidates to enable energy-dense lithium metal batteries by leveraging inorganic high ionic conductivity and flexible polymer mechanical properties. However, studies of hybrid electrolytes using sulfide-type inorganics such as Li3PS4 (LPS) have largely focused on combining the inorganic with commercial poly(ethylene oxide) (PEO). PEO has proven to be insufficient for use in hybrid systems because it reacts with LPS and provides a competing pathway for ion transport, therefore producing a hybrid with low conductivity. Our work shows that using nonconductive, nonpolar polyethylene (PE) in a hybrid electrolyte with LPS eliminates both polymer and inorganic degradation and remarkably exhibit higher conductivities than those containing PEO at different polymer and salt concentrations. Using tracer-exchange NMR, we observe that the nonconductive nature of PE allows for iontransport through the inorganic whereas PEO provides a separate, competing pathway for lithium transport. Furthermore, compared to pure LPS, these hybrids enable longer term lithium cycling at 60°C. Our work shows that the path to enabling conductive and stable sulfide hybrids for solid state lithium metal batteries may be through the use of nonconductive, nonreactive polymers.
batteries↗
Effect of Building Block Connectivity and Ion Solvation on Electrochemical Stability and Ionic Conductivity in Novel Fluoroether Electrolytes
Novel electrolytes are required for the commercialization of batteries with high energy densities such as lithium metal batteries. Recently, fluoroether solvents have become promising electrolyte candidates because they yield appreciable ionic conductivities, high oxidative stability, and enable high Coulombic efficiencies for lithium metal cycling. However, reported fluoroether electrolytes have similar molecular structures, and the influence of ion solvation in modifying electrolyte properties has not been elucidated. In this work, we synthesize a group of fluoroether compounds with reversed building block connectivity where ether moieties are sandwiched by fluorinated end groups. These compounds can support ionic conductivities as high as 1.3 mS/cm (30 °C, 1 M salt concentration). Remarkably, we report that the oxidative stability of these electrolytes increases with decreasing fluorine content, a phenomenon not observed in other fluoroethers. Using Raman and other spectroscopic techniques, we show that lithium ion solvation is controlled by fluoroether molecular structure, and the oxidative stability correlates with the “free solvent” fraction. Finally, we show that these electrolytes can be cycled repeatedly with lithium metal and other battery chemistries. Understanding the impact of building block connectivity and ionic solvation structure on electrochemical phenomena will facilitate the development of novel electrolytes for next-generation batteries.
36 MATERIALS SCIENCE↗
Importance of multimodal characterization and influence of residual Li 2 S impurity in amorphous Li 3 PS 4 inorganic electrolytes
Amorphous Li 3 PS 4 (LPS) solid-state electrolytes are promising for energy-dense lithium metal batteries. LPS glass, synthesized from a 3:1 mol ratio of Li 2 S and P 2 S 5 , has high ionic conductivity and can be synthesized by ball milling or solution processing. Ball milling has been attractive because it provides the easiest route to access amorphous LPS with a conductivity of 3.5 × 10 –4 S cm –1 (20 °C). However, achieving the complete reaction of precursors via ball milling can be difficult, and most literature reports use X-ray diffraction (XRD) or Raman spectroscopy to confirm sample purity, both of which have limitations. Furthermore, the effect of residual precursors on ionic conductivity and lithium metal cycling is unknown. In this work, we illustrate the importance of multimodal characterization to determine LPS phase and chemical purity. To determine the residual Li 2 S content in LPS, we show that (1) XRD and 31 P solid state nuclear magnetic resonance (ssNMR) are insufficient and (2) Raman loses sensitivity at concentrations below 12 mol% Li 2 S. Most importantly, we show that 7 Li ssNMR is highly sensitive. Using 7 Li ssNMR, we investigate the effect of ball milling parameters and develop a robust and highly reproducible procedure for pure LPS synthesis. We find that as the residual Li 2 S precursor content increases, LPS conductivity decreases and lithium metal batteries exhibit higher overpotentials and poor cycle life. Furthermore, our work reveals the importance of multimodal characterization techniques for amorphous solid-state electrolyte characterization and will enable better synthetic strategies for highly conductive electrolytes for efficient energy-dense solid-state lithium metal batteries.
25 ENERGY STORAGE↗
Ion-Conducting Dynamic Solid Polymer Electrolyte Adhesives
Cross-linked polymer electrolytes containing structurally dynamic disulfide bonds have been synthesized to investigate their combined ion transport and adhesive properties. Dynamic network polymers of varying cross-link densities are synthesized via thiol oxidation of a bisthiol monomer, 2,2'-(ethylenedioxy)diethanethiol, and tetrathiol cross-linker, pentaerythritol tetrakis(3-mercaptopropionate). At optimal loading of lithium bis(trifluoromethane-sulfonyl-imide) (LiTFSI) salt, the ionic conductivities (σ) at 90 °C are about 1 × 10–4 and 1 × 10–5 S/cm at the lowest and highest cross-linking, respectively. Notably, in comparison to the equivalent nondynamic network, the dynamic network shows a positive deviation in σ above 90 °C, which suggests the enhancement of ion transport occurs from the difference in structural relaxation on account of the dissociation of disulfide bonds. Lap shear adhesion and conductivity tests on ITO-coated glass substrates reveal the dynamic network exhibits a higher adhesive shear strength of 0.2 MPa (vs 0.03 MPa for the nondynamic network) and higher σ after the application of external stimulus (UV light or heat). The adhesive strength and σ are stable over multiple debonding/rebonding cycles and, thus, demonstrating the utility of these structurally dynamic networks as solid polymer electrolyte adhesives.
37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗