Experimental determination of critical resolved shear stress for strain-induced phase transformation
The current investigation reports the first attempt to measure the critical resolved shear stress to initiates strain-induced phase transformation in a three-dimensional polycrystalline aggregate using high-energy diffraction microscopy (HEDM). In situ tensile testing was performed on a Fe38.5Mn20Co20Cr15Si5Cu1.5 metastable alloy exhibiting transformation-induced plasticity (TRIP). Grains with a higher propensity for strain-induced phase transformation were tracked using HEDM. A sharp drop in grain specific stress, coinciding with the appearance of a new ε-hcp grain oriented relative to the parent γ-fcc phase, was taken as evidence of grain-specific stress required to trigger phase transformation. The highest resolved shear stress on the potential transformation systems was identified as the critical resolved shear stress (CRSS) for strain-induced phase transformation. For the studied metastable alloy, CRSS for transformation was determined to be 86±3 MPa which was very close to theoretical CRSS value determined using Schmid factor (89±12 MPa) compared to the value determined using Taylor factor (62±7 MPa).