DOE OSTI2024

Interdependence of Support Wettability ‐ Electrodeposition Rate‐ Sodium Metal Anode and SEI Microstructure

Abstract This study examines how current collector support chemistry (sodiophilic intermetallic Na 2 Te vs. sodiophobic baseline Cu) and electrodeposition rate affect microstructure of sodium metal and its solid electrolyte interphase (SEI). Capacity and current (6 mAh cm −2 , 0.5–3 mA cm −2 ) representative of commercially relevant mass loading in anode‐free sodium metal battery (AF‐SMBs) are analyzed. Synchrotron X‐ray nanotomography and grazing‐incidence wide‐angle X‐ray scattering (GIWAXS) are combined with cryogenic ion beam (cryo‐FIB) microscopy. Highlighted are major differences in film morphology, internal porosity, and crystallographic preferred orientation e.g. (110) vs. (100) and (211) with support and deposition rate. Within the SEI, sodium fluoride (NaF) is more prevalent with Te−Cu versus sodium hydride (NaH) and sodium hydroxide (NaOH) with baseline Cu. Due to competitive grain growth the preferred orientation of sodium crystallites depends on film thickness. Mesoscale modeling delineates the role of SEI (ionic conductivity, morphology) on electrodeposit growth and onset of electrochemical instability.

Lo, Chang‐An↗

DOE OSTI2024

Interdependence of Support Wettability - Electrodeposition Rate- Sodium Metal Anode and SEI Microstructure

Here, this study examines how current collector support chemistry (sodiophilic intermetallic Na 2 Te vs. sodiophobic baseline Cu) and electrodeposition rate affect microstructure of sodium metal and its solid electrolyte interphase (SEI). Capacity and current (6 mAh cm -2 , 0.5–3 mA cm -2 ) representative of commercially relevant mass loading in anode-free sodium metal battery (AF-SMBs) are analyzed. Synchrotron X-ray nanotomography and grazing-incidence wide-angle X-ray scattering (GIWAXS) are combined with cryogenic ion beam (cryo-FIB) microscopy. Highlighted are major differences in film morphology, internal porosity, and crystallographic preferred orientation e.g. (110) vs. (100) and (211) with support and deposition rate. Within the SEI, sodium fluoride (NaF) is more prevalent with Te-Cu versus sodium hydride (NaH) and sodium hydroxide (NaOH) with baseline Cu. Due to competitive grain growth the preferred orientation of sodium crystallites depends on film thickness. Mesoscale modeling delineates the role of SEI (ionic conductivity, morphology) on electrodeposit growth and onset of electrochemical instability.

36 MATERIALS SCIENCE↗

DOE OSTI2024

Alumina – Stabilized SEI and CEI in Potassium Metal Batteries

Aluminum oxide (Al 2 O 3 ) nanopowder is spin-coated onto both sides of commercial polypropene separator to create artificial solid-electrolyte interphase (SEI) and artificial cathode electrolyte interface (CEI) in potassium metal batteries (KMBs). Here, this significantly enhances the stability, including of KMBs with Prussian Blue (PB) cathodes. For example, symmetric cells are stable after 1,000 cycles at 0.5 mA/cm 2 –0.5 mAh/cm 2 and 3.0 mA/cm 2 –0.5 mAh/cm 2 . Alumina modified separators promote electrolyte wetting and increase ionic conductivity (0.59 vs. 0.2 mS/cm) and transference number (0.81 vs. 0.23). Cryo-stage focused ion beam (cryo-FIB) analysis of cycled modified anode demonstrates dense and planar electrodeposits, versus unmodified baseline consisting of metal filaments (dendrites) interspersed with pores and SEI. Alumina-modified CEI also suppresses elemental Fe crossover and reduces cathode cracking. Mesoscale modeling of metal – SEI interactions captures crucial role of intrinsic heterogeneities, illustrating how artificial SEI affects reaction current distribution, conductivity and morphological stability.

25 ENERGY STORAGE↗

DOE OSTI2024

Mechanical Milling – Induced Microstructure Changes in Argyrodite LPSCl Solid-State Electrolyte Critically Affect Electrochemical Stability

Microstructure of argyrodite solid-state electrolyte (SSE) critically affects lithium metal electrodeposition/dissolution. While the stability of unmodified SSE is mediocre, once optimized state-of-the-art electrochemical performance is achieved (symmetric cells, full cells with NMC811) without secondary interlayers or functionalized current collectors. Planetary mechanical milling in wet media (m-xylene) is employed to alter commercial Li 6 PS 5 Cl (LPSCl) powder. Quantitative stereology demonstrates how milling progressively refines grain and pore size/distribution in the SSE compact, increases its density, and geometrically smoothens the SSE-Li interface. Mechanical indentation demonstrates that these changes lead to reduced site-to-site variation in the compact's hardness. Milled microstructures promote uniform early-stage electrodeposition on foil collectors and stabilize solid electrolyte interphase (SEI) reactivity. Analysis of half-cells with bilayer electrolytes demonstrates the importance of microstructure directly contacting current collector, with interface roughness due to pore and grain size distribution being key. For the first time, short-circuiting Li metal dendrite is directly identified, employing 1.5 mm diameter “mini” symmetrical cell and cryogenic focused ion beam (cryo-FIB) electron microscopy. The branching sheet-like dendrite traverses intergranularly, filling the interparticle voids and forming an SEI around it. Importantly, mesoscale modeling reveals the relationship between Li-SSE interface morphology and the onset of electrochemical instability, based on underlying reaction current distribution.

25 ENERGY STORAGE↗

DOE OSTI2023

Promoting Fast Ion Conduction in Li-Argyrodite through Lithium Sublattice Engineering

Fundamental understanding of ionic transport plays a pivotal role in designing and optimizing fast ionic conductors. Here, through a systematic neutron scattering and theoretical investigation, we discovered new insights about how anion sublattice affects Li + distribution and transport in Li-argyrodite. We found that the promotion of Li + conductivities is strongly correlated with a previously overlooked Li + interstitial site (16e), which is critical for realizing intercage Li + migration. More isotropic Li + migration pathways with higher Li + occupancies on the interstitial 16e site are found to be the underlying reason for the much higher Li + conductivity in Li 6 PS 5 Cl relative to the Br- and I-based analogues. We further confirm that they are also the universal driving force for the ultrahigh Li + conductivities in both anion-substituted Li-poor (Li 6–a PS 5–a X a, X = Cl and Br) and cation-substituted Li-rich argyrodite (e.g., Li 6+a GeaP 1–a S 5 I and Li 6+a SiaSb 1–a S 5 I). In conclusion, it is expected this strategy can be generally adopted to improve the ionic conductivity of the broad family of Li-rich argyrodite and beyond.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗

DOE OSTI2023

Tuned Reactivity at the Lithium Metal–Argyrodite Solid State Electrolyte Interphase

Thin intermetallic Li 2 Te–LiTe 3 bilayer (0.75 µm) derived from 2D tellurene stabilizes the solid electrolyte interphase (SEI) of lithium metal and argyrodite (LPSCl, Li 6 PS 5 Cl) solid-state electrolyte (SSE). Tellurene is loaded onto a standard battery separator and reacted with lithium through single-pass mechanical rolling or transferred directly to SSE surface by pressing. State-of-the-art electrochemical performance is achieved, e.g., symmetric cell stable for 300 cycles (1800 h) at 1 mA cm -2 and 3 mAh cm -2 (25% DOD, 60 µm foil). Cryo-stage focused ion beam (Cryo-FIB) sectioning and Raman mapping demonstrate that the Li 2 Te–LiTe 3 bilayer impedes SSE decomposition. The unmodified Li–LPSCl interphase is electrochemically unstable with a geometrically heterogeneous reduction decomposition reaction front that extends deep into the SSE. Decomposition drives voiding in Li metal due to its high flux to the reaction front, as well as voiding in the SSE due to the associated volume changes. Analysis of cycled SSE found no evidence for pristine (unreacted) lithium metal filaments/dendrites, implying failure driven by decomposition phases with sufficient electrical conductivity that span electrolyte thickness. In conclusion, DFT calculations clarify thermodynamic stability, interfacial adhesion, and electronic transport properties of interphases, while mesoscale modeling examines interrelations between reaction front heterogeneity (SEI heterogeneity), current distribution, and localized chemo-mechanical stresses.

25 ENERGY STORAGE↗