Assessment of Cementitious Composites for High-Temperature Geothermal Wells

High-temperature (HT) geothermal wells can provide green power 24 hours a day, 7 days a week. Under harsh environmental and operational conditions, the long-term durability requirements of such wells require special cementitious composites for well construction. This paper reports a comprehensive assessment of geothermal cement composites in cyclic pressure function laboratory tests and field exposures in an HT geothermal well (300–350 °C), as well as a numerical model to complement the experimental results. Performances of calcium–aluminate cement (CAC)-based composites and calcium-free cement were compared against the reference ordinary Portland cement (OPC)/silica blend. The stability and degradation of the tested materials were characterized by crystalline composition, thermo-gravimetric and elemental analyses, morphological studies, water-fillable porosity, and mechanical property measurements. All CAC-based formulations outperformed the reference blend both in the function and exposure tests. The reference OPC/silica lost its mechanical properties during the 9-month well exposure through extensive HT carbonation, while the properties of the CAC-based blends improved over that period. The Modified Cam-Clay (MCC) plasticity parameters of several HT cement formulations were extracted from triaxial and Brazilian tests and verified against the experimental results of function cyclic tests. These parameters can be used in well integrity models to predict the field-scale behavior of the cement sheath under geothermal well conditions.

15 GEOTHERMAL ENERGY↗

DOE OSTI2023

Testing Various Cement Formulations under Temperature Cycles and Drying Shrinkage for Low-Temperature Geothermal Wells

Low-enthalpy geothermal wells are considered a sustainable energy source, particularly for district heating in the Netherlands. The cement sheath in these wells experiences thermal cycles. The stability of cement recipes under such conditions is not well understood. In this work, thermal cycling experiments for intermediate- and low-temperature geothermal well cements have been conducted. The samples were cured either under ambient conditions or under realistic pressure and temperature for 7 days. The samples did not show any signs of failure after performing 10 cycles of thermal treatment between 100 °C and 18 °C. We also tested cement formulations under drying conditions. Drying shrinkage is caused by a reduction in the water content of cement, which leads to capillary forces that can damage cement. Such circumstances lead to tensile stresses causing radial cracks. Most samples exhibited cracks under low humidity conditions (drying). Fiber reinforcement, especially using short PP fibers, improved the cement’s resilience to temperature and humidity changes. Such additives can improve the longevity of cement sheaths in geothermal wells.

36 MATERIALS SCIENCE↗