Mapping the structural trends in zinc aluminosilicate glasses

The structure of zinc aluminosilicate glasses with the composition (ZnO) x (Al 2 O 3 ) y (SiO 2 ) 1-x-y , where 0 ≤ x < 1, 0 ≤ y < 1, and x + y < 1, was investigated over a wide composition range by combining neutron and high-energy x-ray diffraction with 27 Al magic angle spinning nuclear magnetic resonance spectroscopy. The results were interpreted using an analytical model for the composition-dependent structure in which the zinc ions do not act as network formers. Four-coordinated aluminum atoms were found to be in the majority for all the investigated glasses, with five-coordinated aluminum atoms as the main minority species. Mean Al–O bond distances of 1.764(5) and 1.855(5) Å were obtained for the four- and five-coordinated aluminum atoms, respectively. The coordination environment of zinc was not observed to be invariant. Instead, it is dependent on whether zinc plays a predominantly network-modifying or charge-compensating role and, therefore, varies systematically with the glass composition. The Zn–O coordination number and bond distance were found to be 4.36(9) and 2.00(1) Å, respectively, for the network-modifying role vs 5.96(10) and 2.08(1) Å, respectively, for the charge-compensating role. The more open coordination environment of the charge-compensator is related to an enhanced probability of zinc finding bridging oxygen atoms as nearest-neighbors, reflecting a change in the connectivity of the glass network comprising four-coordinated silicon and aluminum atoms as the alumina content is increased.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗

DOE OSTI2022

Structure of diopside, enstatite, and magnesium aluminosilicate glasses: A joint approach using neutron and x-ray diffraction and solid-state NMR

Neutron diffraction with magnesium isotope substitution, high energy x-ray diffraction, and 29 Si, 27 Al, and 25 Mg solid-state nuclear magnetic resonance (NMR) spectroscopy were used to measure the structure of glassy diopside (CaMgSi 2 O 6 ), enstatite (MgSiO 3 ), and four (MgO) x (Al 2 O 3 ) y (SiO 2 ) 1–x–y glasses, with x = 0.375 or 0.25 along the 50 mol. % silica tie-line (1 – x – y = 0.5) or with x = 0.3 or 0.2 along the 60 mol. % silica tie-line (1 – x – y = 0.6). The bound coherent neutron scattering length of the isotope 25 Mg was remeasured, and the value of 3.720(12) fm was obtained from a Rietveld refinement of the powder diffraction patterns measured for crystalline 25 MgO. The diffraction results for the glasses show a broad asymmetric distribution of Mg–O nearest-neighbors with a coordination number of 4.40(4) and 4.46(4) for the diopside and enstatite glasses, respectively. As magnesia is replaced by alumina along a tie-line with 50 or 60 mol. % silica, the Mg–O coordination number increases with the weighted bond distance as less Mg 2+ ions adopt a network-modifying role and more of these ions adopt a predominantly charge-compensating role. 25 Mg magic angle spinning (MAS) NMR results could not resolve the different coordination environments of Mg 2+ under the employed field strength (14.1 T) and spinning rate (20 kHz). The results emphasize the power of neutron diffraction with isotope substitution to provide unambiguous site-specific information on the coordination environment of magnesium in disordered materials.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗