Engineering topics
Moody, Michael P.
Publications and source records attributed to Moody, Michael P..
Microstructural evolution and transmutation in tungsten under ion and neutron irradiation
This study aims to compare the effects of neutron and self-ion irradiation on the mechanical properties and microstructural evolution in W. Neutron irradiation at the HFR reactor to 1.67 dpa at 800 °C resulted in the formation of large Re and Os rich clusters and voids. The post-irradiation composition was measured using APT and verfified against FISPACT modelling. The measured Re and Os concentration was used to create alloys with equivalent concentrations of Re and Os. These alloys were exposed to self-ion irradiation to a peak dose of 1.7 dpa at 800 °C. APT showed that self-ion irradiation leads to the formation of small Os clusters, wheras under neutron irradiation large Re/Os clusters form. Voids are formed by both ion and neutron irradiation, but the voids formed by neutron irradiation are larger. By comparing the behaviour of W-1.4Re and W-1.4Re-0.1Os, suppression of Re cluster formation was observed. Irradiation hardening was measured using nanoindentation and was found to be 2.7 GPa, after neutron irradiation and 1.6 GPa and 0.6 GPa for the self-ion irradiated W-1.4Re and W-1.4Re-0.1Os. The higher hardening is attributed to the barrier strength of large voids and Re/Os clusters that are observed after neutron irradiation.
Origin of the enhanced Nb3Sn performance by combined Hf and Ta doping
Abstract In recent years there has been an increasing effort in improving the performance of Nb 3 Sn for high-field applications, in particular for the fabrication of conductors suitable for the realization of the Future Circular Collider (FCC) at CERN. This challenging task has led to the investigation of new routes to advance the high-field pinning properties, the irreversibility and the upper critical fields ( H Irr and H c2 , respectively). The effect of hafnium addition to the standard Nb-4Ta alloy has been recently demonstrated to be particularly promising and, in this paper, we investigate the origins of the observed improvements of the superconducting properties. Electron microscopy, Extended X-ray Absorption Fine Structure Spectroscopy (EXAFS) and Atom Probe Tomography (APT) characterization clearly show that, in presence of oxygen, both fine Nb 3 Sn grains and HfO 2 nanoparticles form. Although EXAFS is unable to detect significant amounts of Hf in the A15 structure, APT does indeed reveal some residual intragrain metallic Hf. To investigate the layer properties in more detail, we created a microbridge from a thin lamella extracted by Focused Ion Beam (FIB) and measured the transport properties of Ta-Hf-doped Nb 3 Sn. H c2 (0) is enhanced to 30.8 T by the introduction of Hf, ~ 1 T higher than those of only Ta-doped Nb 3 Sn, and, even more importantly the position of the pinning force maximum exceeds 6 T, against the typical ~ 4.5–4.7 T of the only Ta-doped material. These results show that the improvements generated by Hf addition can significantly enhance the high-field performance, bringing Nb 3 Sn closer to the requirements necessary for FCC realization.
Characterisation of nano-scale precipitates in BOR60 irradiated T91 steel using atom probe tomography
Atom probe tomography has characterised the microstructural changes in T91 steel after BOR60 reactor irradiation at five temperatures between 376 °C and 524 °C to doses between 14.6 dpa and 35.1 dpa. Irradiation-induced precipitation and segregation to carbide/matrix interface induced by neutron irradiation has been characterised. Atom probe tomography characterisation shows that Mn, Ni, Si -rich (MNS-rich) clusters form in T91 steel irradiated in BOR60 reactor at temperatures between 376 °C and 415 °C, which is not observed at higher temperatures 460 °C and 524 °C. Additionally, the number density, volume fraction and composition of MNS-rich clusters have been characterised. Ni, Mn, Si and P is found to segregate at carbide matrix interface after irradiation at lower temperature and only P segregation is observed at 524 °C.