Engineering topics
Publications and source records attributed to Morell-Pacheco, Andres.
This presentation titled "Updates on UO 2 -BeO Experiment (IER 523)" covers experiment status, experiment motivation, CED-1 summary, current efforts (CED-2), and includes a concluding summary.
Here, in situ micropillar compression was used to study the deformation of proton-irradiated Hastelloy-N at different damage levels. Multiple pillars were prepared from a single domain along the cross-section of 2.5 MeV proton-irradiated Hastelloy-N. Depending on the location of micropillars, the critical resolved shear stress was obtained as a function of local damage levels. Such an approach eliminates the variation of yield stress due to the difference in the Schmid factor. Microstructural characterization showed that irradiation hardening is contributed by complicated defect structures, including (a) dislocation loops with many in corduroy-like alignments, (2) dislocations pile up, and (3) Cottrell atmosphere. Silicon atoms are found to segregate at dislocation lines and loops and form complicated Cottrell cloud patterns. The critical resolved shear stress, $t_{crss}$, and hardening exponents were both extracted as a function of displacements per atom values up to 2.3. There was a 60% increase in $t_{crss}$ at the highest damage level.
Plasma nitridation was conducted to modify the surfaces of Zircaloy-4. Scanning electron microscopy (SEM), transmission electron microscopy (TEM), and Raman analysis were used to characterize microstructures and phases. Surface indentation and cross-sectional indentation were performed to evaluate mechanical property changes. Nitridation forms a thin layer of ZrN phase, followed by a much deeper layer affected by nitrogen diffusion. The ZrN phase is confirmed by both TEM and Raman characterization. The Raman peaks of ZrN phase show a temperature dependence. The intensity increases with increasing nitridation temperatures, reaches a maximum at 700 °C, and then decreases at higher temperatures. The ZrN layer appears as continuous small columnar grains. The surface polycrystalline ZrN phase is harder than the bulk by a factor of ~8, and the nitrogen diffusion layer is harder by a factor of ~2–5. The activation energy of nitrogen diffusion was measured to be 2.88 eV. The thickness of the nitrogen-hardened layer is controllable by changing the nitridation temperature and duration.
A modified cage plasma nitriding technique is used to coat a Ni film onto a 316L substrate as a protective layer for austenitic steels in molten fluoride salts. The coating is achieved by deposition of Ni atoms sputtered from a Ni cage with a 316L substrate floated at the same potential as the cage to reduce plasma sputtering on the substrate. The Ni coating is porosity-free and precipitation-free and forms a γ-(Fe, Ni) phase due to interdiffusion from the substrate. Beneath the interdiffusion layer exists a thick γ-phase layer mainly affected by long-range nitrogen diffusion along the grain boundary. This layer develops grain boundary Cr nitride precipitates. Ion irradiation on the polished cross-section of the plasma-treated sample shows no void swelling in the surface-deposited Ni layer, very limited void formation in N diffusion layer, and significant void swelling in bulk unaffected by nitrogen. The studies demonstrate the feasibility of the technique for Ni coating and show good swelling resistance of the coating layer and N diffusion-affected layer. Mechanisms are discussed in this paper.