X-ray photoelectron spectroscopy peak assignment for perfluoropolyether oils

Perfluoroalkylpolyether (PFPE) oils are increasingly being used as vacuum pump oils and as lubricants for magnetic recording media and instrumentation for satellites. In this paper, the relative binding energies of three PFPE oils are determined. When sample oils are continuously irradiated during X-ray spectroscopy (XPS) measurements, the relative peak intensity of the spectra is altered significantly, indicating that gaseous products form from the oils during XPS measurements. Thus, attention should be paid to chemical changes when XPE is used to characterize fluorinated carbons such as PFPE oils.

Mori, Shigeyuki↗

NASA NTRS1990

Decomposition of perfluoroalkylpolyethers (PFPE) in ultra-high vacuum under sliding conditions

Reactions of perfluoroalkylpolyethers (PFPE: Fomblin, Demnum and Krytox) were studied during the sliding contact of stainless steel specimens under ultrahigh vacuum conditions. All three fluids reacted with the steel specimens during sliding. Fomblin, which has acetal linkages, decomposed under the sliding conditions generating gaseous products, (COF2 and fluorinated carbons) which were detected by a quadrupole mass spectrometer. Gaseous products were not detected for the Demnum and Krytox fluids. The amount of gaseous products from Fomblin increased with increasing sliding speed. At the end of the sliding experiments, the wear scar and deposits on the specimens were examined by small spot size XPS. The oxide layer on the specimen surface was removed during sliding, and metal fluorides were formed on the worn surface. The surface of the wear scar and deposits were covered with adsorbed PFPE. Based on these results, it was concluded that the decomposition reaction on Fomblin was initiated by contacting the fluid with a fresh metal surface which was formed during sliding.

Mori, Shigeyuki↗

NASA NTRS1989

Degradation and crosslinking of perfluoroalkyl polyethers under X-ray irradiation in ultrahigh vacuum

Degradation of three types of commercially available perfluoroalkyl polyethers (PFPE)-Demnum S200, Fomblin Z25, and Krytox 16256-by X-ray irradiation was studied by using X-ray photoemission spectroscopy (XPS) and a mass spectrometer under ultra-high-vacuum conditions. The carbons in the polymers were characterized by chemical shifts of Cls binding energies. Gaseous products containing COF2 and low-molecular-weight fluorocarbons were formed. From Fomblin Z25, which has acetal linkages (-OCF2O-), a large quantity of COF2 gas was evolved. Liquid products became tacky after a long irradiation time, and some did not dissolve in Freon. High-pressure liquid chromatography (HPLC) showed that molecular weight distribution became broader and that higher molecular weight polymers were formed from Demnum and Krytox. We concluded from these results that degradation and cross-linking took place simultaneously. Demnum crosslinked more easily than the other fluids. The time dependence of both XPS spectra of Cls and mass spectra showed that C-O-bonded carbons in PFPE'S were removed faster than other carbons. There was no substrate effect on the degradation reaction because the first-order rate constants calculated from the change of gaseous products were similar when stainless steel (440C) and gold-coated surfaces were used. Metal fluorides were formed on stainless steel during the reaction. A mechanism for the degradation of PFPE'S is discussed on the basis of their molecular structures.

Mori, Shigeyuki↗

NASA NTRS1989

Reaction of perfluoroalkylpolyethers (PFPE) with 440C steel in vacuum under sliding conditions at room temperature

Reactions of perfluoroalkylpolyethers (PFPE: Fomblin, Demnum and Krytox) were studied during the sliding contact of stainless steel specimens under ultrahigh vacuum conditions. All three fluids reacted with the steel specimens during sliding. Fomblin, which has acetal linkages, decomposed under the sliding conditions generating gaseous products, (COF2 and fluorinated carbons) which were detected by a quadrupole mass spectrometer. Gaseous products were not detected for the Demnum and Krytox fluids. The amount of gaseous products from Fomblin increased with increasing sliding speed. At the end of the sliding experiments, the wear scar and deposits on the specimens were examined by small spot size XPS. The oxide layer on the specimen surface was removed during sliding, and metal fluorides were formed on the worn surface. The surface of the wear scar and deposits were covered with adsorbed PFPE. Based on these results, it was concluded that the decomposition reaction on Fomblin was initiated by contacting the fluid with a fresh metal surface which was formed during sliding.

Mori, Shigeyuki↗

NASA NTRS1989

Tribological reactions of perfluoroalkyl polyether oils with stainless steel under ultrahigh vacuum conditions at room temperature

The reaction between three types of commercial perfluoroalkyl polyether (PFPE) oils and stainless steel 440C was investigated experimentally during sliding under ultrahigh vacuum conditions at room temperature. It is found that the tribological reaction of PFPE is mainly affected by the activity of the mechanically formed fresh surfaces of metals rather than the heat generated at the sliding contacts. The fluorides formed on the wear track act as a boundary layer, reducing the friction coefficient.