NASA NTRS1989

A comparison of predicted and measured strengths of thick notched graphite/epoxy laminates

The effect of thickness on the notched strength of three graphite/epoxy laminates is studied. The strength of the laminates is shown to be a function of laminate thickness. The notched strength of (0/+ or - 45/90)ns and (0/90)ns laminates decreased toward asymptotic values with increasing laminate thickness, while that of the (0/+ or - 45)ns laminate increased toward an asymptotic value with increasing laminate thickness. For all three laminate types, the notched strength decreased with increasing notch size, regardless of thickness. The fracture of the thick laminates was essentially uniform and self-similar with the notch. The 'universal' value of the general toughness parameter developed by Poe (1981) successfully predicts the notched strength of the thick laminates.

Harris, C. E.↗

NASA NTRS1988

Surface crack analysis applied to impact damage in a thick graphite-epoxy composite

The residual tensile strength of a thick graphite/epoxy composite with impact damage was predicted using surface crack analysis. The damage was localized to a region directly beneath the impact site and extended only part way through the laminate. The damaged region contained broken fibers, and the locus of breaks in each layer resembled a crack perpendicular to the direction of the fibers. In some cases, the impacts broke fibers without making a visible crater. The impact damage was represented as a semi-elliptical surface crack with length and depth equal to that of the impact damage. The maximum length and depth of the damage were predicted with a stress analysis and a maximum shear stress criterion. The predictions and measurements of strength were in good agreement.

Poe, C. C., Jr.↗

NASA NTRS1988

Radio emission from RS CVn binaries. III - A VLA survey of 103 systems

The paper presents a 5 GHz radio survey of 103 close late-type stellar binaries. Fifty-three of the 103 candidate stars were detected above an average detection threshold of 0.4 mJy. The median observed radio luminosity is compared with total bolometric luminosity, rotational period, color index (B-V), and Rossby number.

Morris, D. H.↗

NASA NTRS1988

Application of fracture mechanics to predict the strength of filament-wound composite specimens with surface damage

The strength of a thick surface notched filament wound graphite/epoxy tensile specimen was predicted using fracture mechanics analysis. The prediction model depended upon the depth of the surface notch and upon the type of failure. Specimens failed in two stages: first a sublaminate with thickness equal to the depth of the surface cut, and second, for increasing load, a sublaminate with thickness equal to the initial thickness minus the cut depth. Analytical predictions and experimental data were in good agreement.

Morris, D. H.↗

NASA NTRS1987

Radio emission from RS CVn binaries. II - Polarization and spectral properties

Multiepoch radio observations of circular polarization and spectral characteristics of several close, late-type stellar binaries are reported. The median luminosity of four well-studied systems ranged from 16.2 to 17.1 ergs/s/Hz. For individual systems, the fractional circular polarization decreases with increasing luminosity, particularly at frequencies above 5 GHz. Eclipsing binaries have significantly lower average circular polarization compared with noneclipsing systems. Helicity reversal is almost always observed between 1.4 and 4.9 GHz for systems with high orbital inclination. Comparison with ten years of previously published polarization observations for two RS CVn stellar systems show that the same helicity occurs at a given frequency for a given source, indicating a very stable, large-scale magnetic field geometry. These spectral and polarization characteristics strongly support a model of inhomogeneous gyrosynchrotron emission arising from electrons with power law energy spectra interacting with inhomogeneous magnetic fields.

Mutel, R. L.↗

NASA NTRS1986

Fracture of thick laminated composites

The fracture of thick laminated graphite/epoxy composites has been the subject of an extensive research program. The program was divided into three major areas of investigation which included laminate thickness, laminate stacking sequence, and part-through surface flaws. The results from this program are reviewed with emphasis placed on their applicability to the design of thick laminated composite structures.

Harris, C. E.↗

NASA NTRS1986

Effect of laminate thickness and specimen configuration on the fracture of laminated composites

Attention is given to the effect of laminate thickness on graphite/epoxy laminates in the present measurements of fracture toughness in center cracked tension specimens, compact tension specimens, and three-point bend specimens. Crack tip damage development prior to fracture is also studied. The results obtained show fracture toughness to be a function of laminate thickness, being in all cases independent of crack size. The fracture surface of all thick laminates was uniform in the interior and self-similar with the starter notch. With only one exception, the fracture toughness of the thicker laminates was relatively independent of specimen configuration.

Harris, C. E.↗

NASA NTRS1986

Fracture of thick graphite/epoxy laminates with part-through surface flaws

Fracture behavior of tensile specimens containing through-the-thickness flaws and part-through semi-elliptic surface flaws was investigated. The material was T300/5208 graphite/epoxy, with a stacking sequence 0/+ or - 45/90 sub ns. Laminate thicknesses ranged from 8 to 120 plies. Fracture toughness for specimens with through-the-thickness flaws was a function of laminate thickness. Fracture toughness was also independent of crack size. Fracture toughness for the thick laminates was also independent of specimen geometry (center-cracked tension specimen, compact tension specimen, and three-point bend specimen). Using the asymptotic value of fracture toughness and linear elastic isotropic fracture mechanics, the notched strength of tensile specimens with semi-elliptic surface flaws was predicted. The strength ratio is a function of the flaw depth (a/t) and flaw aspect (a/c) ratios. Comparisons between predicted and experimental strengths are good for large values of a/t. The notched strength of filament wound graphite/epoxy tensile specimens with part-through surface flaws was also predicted.

Harris, C. E.↗

NASA NTRS1986

A comparison of the fracture behavior of thick laminated composites utilizing compact tension, three-point bend, and center-cracked tension specimens

An experimental study of the effects of specimen configuration and laminate thickness on the fracture behavior of notched laminated composites is presented. The behavior of (0/+, 45/90)ns, (0/90)ns and (0/+, - 45)ns graphite/epoxy T300/5208 laminates was studied. When fracture toughness was computed at the failing load of the center-cracked tension specimen, laminate thickness significantly influenced fracture toughness. If fracture toughness was computed at the interception of the 5 percent secant line with the load-COD record, fracture toughness was found to be independent of both laminate thickness and specimen configuration. Defined in this manner, fracture toughness can be physically interpreted as an indicator of the onset of significant notch-tip damage.

Harris, C. E.↗

NASA NTRS1985

Comparisons of various configurations of the edge delamination test for interlaminar fracture toughness

Various configurations of Edge Delamination Tension (EDT) test specimens, of both brittle (T300/5208) and toughened-matrix (T300/BP907) graphite reinforced composite laminates, were manufactured and tested. The mixed-mode interlaminar fracture toughness, G sub C, was measured using (30/30 sub 2/30/90 sub N)sub s, n=1 or 2, (35/-35/0/90) sub s and (35/0/-35/90) sub s layups designed to delaminate at low tensile strains. Laminates were made without inserts so that delaminations would form naturally between the central 90 deg plies and the adjacent angle plies. Laminates were also made with Teflon inserts implanted between the 90 deg plies and the adjacent angle (theta) plies at the straight edge to obtain a planar fracture surface. In addition, interlaminar tension fracture toughness, GIc, was measured from laminates with the same layup but with inserts in the midplane, between the central 90 deg plies, at the straight edge. All of the EDT configurations were useful for ranking the delamination resistance of composites with different matrix resins. Furthermore, the variety of layups and configurations available yield interlaminar fracture toughness measurements needed to generate delamination failure criteria. The influence of insert thickness and location, and coupon size on G sub c values were evaluated.

Obrien, T. K.↗

NASA NTRS1985

On the use of crack-tip-opening displacement to predict the fracture strength of notched graphite/epoxy laminates

Using the center-cracked tension specimen geometry, the fracture strength of notched graphite/epoxy laminates is measured experimentally. Four replicate tests are conducted for a variety of laminate-stacking sequences, thicknesses, and notch lengths. Extensive notch-tip damage prior to fracture is characteristic of most laminates. The values of critical crack-tip-opening displacement (CTOD) are calculated from values of crack-opening displacement measured at the notch center line at failure and are found to be independent of notch size for the laminates studied. A Dugdale (1950) model is used along with the estimated CTOD to predict notched laminate strength.

Harris, C. E.↗

NASA NTRS1985

Fracture of thick graphite/epoxy laminates with part-through surface flaws

Fracture behavior of tensile specimens containing through-the-thickness flaws and part-through semi-elliptic surface flaws was investigated. The material was T300/5208 graphite/epoxy, with a stacking sequence 0/+ or - 45/90 sub ns. Laminate thicknesses ranged from 8 to 120 plies. Fracture toughness for specimens with through-the-thickness flaws was a function of laminate thickness. Fracture toughness was also independent of crack size. Fracture toughness for the thick laminates was also independent of specimen geometry (center-cracked tension specimen, compact tension specimen, and three-point bend specimen). Using the asymptotic value of facture toughness and linear elastic isotropic fracture mechanics, the notched strength of tensile specimens with semi-elliptic surface flaws was predicted. The strength ratio is a function of the flaw depth (a/t) and flaw aspect (a/c) ratios. Comparisons between predicted and experimental strengths are good for large values of a/t. The notched strength of filament wound graphite/epoxy tensile specimens with part-through surface flaws was also predicted.

Morris, D. H.↗

NASA NTRS1985

Preliminary report on tests of tensile specimens with a part-through surface notch for a filament wound graphite/epoxy material

The behavior of tensile coupons with surface notches of various semi-elliptical shapes were evaluated for specimens obtained from a filament wound graphite/epoxy cylinder. The quasi-static test results, in some instances, are inadequate for defining complete trend curves and the interpretive analysis is considered to be preliminary. Specimens with very shallow notches were observed to be notch insensitive and the unnotched strength from these specimens was determined to be 54.97 Ksi. The failure strain of the laminate was found to be 1.328%. Specimens with deeper notches were sensitive to notch depth, notch aspect ratio, and specimen width. Using the unnotched strength of 54.97 Ksi and Poe's general toughness parameter, the fracture toughness was estimated to be 27.2 Ksi square root of In. Isotropic linear elastic fracture mechanics together with the estimated fracture toughness correctly predicted the influence of notch depth, aspect ratio, and specimen finitewidth.

Harris, C. E.↗

NASA NTRS1985

The fracture behavior of filament wound cylinders with surface flaws

The behavior of tensile coupons with surface notches of various semielliptical shapes has been evaluated for specimens obtained from a thick filament wound graphite/epoxy cylinder. Specimens with very shallow notches were observed to be notch insensitive and the unnotched strength from these specimens was determined to be 54.97 Ksi with an associated failure strain of 1.328 percent. Specimens with deeper notches were sensitive to notch depth and notch aspect ratio. Isotropic linear elastic fracture mechanics with an estimated fracture toughness of 27.2 Ksi-in.-to the 1/2 correctly predicted the influence of notch depth, aspect ratio and specimen finite width.

Harris, C. E.↗

NASA NTRS1985

An evaluation of the effects of stacking sequence and thickness on the fatigue life of quasi-isotropic graphite/epoxy laminates

Notched and unnotched geometries at 16, 32, and 64-ply thicknesses of a 90/45/0-45 (ns) laminate and a 45/0/-45/90 (ns) laminate were tested in compression-compression fatigue. The fatigue life and the initiation, type, and progression of damage were determined. Interlaminar stresses generated at straight, free edges of axially loaded laminates were used to interpret the test results. The fatigue lives of the notched specimens did not appear to be a strong function of laminate stacking sequence or specimen thickness. The stress concentration at the hole dominated over the interlaminar stresses at the straight free edge. The unnotched specimens of the 90/45/0/-45 (ns) laminate with tensile interlaminar normal stresses delaminated more readily than did the 45/0/-45/90 (ns) laminate with compressive interlaminar normal stress. The life of the 16-ply unnotched specimens was lower than the 32and 64-ply specimens. Delaminations were located at the interface where the maximum shear stress occurred regardless of the sense or magnitude of the interlaminar normal stress. An antibuckling fixture was effective in preventing out-of-plane motion without overconstraining the specimen.

Harris, C. E.↗

NASA NTRS1985

A damage tolerant design parameter for graphite/epoxy laminated composites

The results of an extensive experimental investigation of the fracture behavior of notched graphite/epoxy laminates are presented. Twenty-seven laminates with different stacking sequences and laminate thicknesses have been studied. The data presented herein suggest that a damage tolerant design parameter exists that is relatively independent of ply stacking sequence and laminate thickness.

Harris, C. E.↗

NASA NTRS1985

Role of delamination and damage development on the strength of thick notched laminates

A large, comprehensive program is being conducted at Virginia Tech to study the effect of laminate thickness on the fracture strength of notched laminated composites. Part of this program has been the study of the chracteristics and development of subcritical crack-tip damage prior to failure. The study has concentrated on the center-cracked tension specimen geometry. Subcritical crack-tip damage has been studied using enhanced X-ray radiography and the laminate deply technique. This paper examines he role that delamination plays in affecting the fracture of (0/+ or - 45/90)ns and (0/+ or - 45)ns laminates at various values of n. The study has found that delaminations do occur in thin laminates (n = 1) and affect the strength of the laminate. However, in thick laminates such as (0/+ or 45)90ns, and (0/+ or - 45)20s, there is sufficient constraint to prevent delaminations from occurring in the interior region of he specimen. The final fracture surface is uniform in the interior and self-similar (collinear with the original starter notch), with 'shear-lip' type damage in the form of delaminations and matrix cracking in the first several plies at the surface. These differences in the type of fracture of the thin and thick laminates greatly affect the fracture strength.

Harris, C. E.↗

NASA NTRS1984

Fracture behavior of thick, laminated graphite/epoxy composites

The effect of laminate thickness on the fracture behavior of laminated graphite epoxy (T300/5208) composites was studied. The predominantly experimental research program included the study of the 0/+ or - 45/90 sub ns and 0/90 sub ns laminates with thickness of 8, 32, 64, 96 and 120 plies and the 0/+ or - 45 sub ns laminate with thickness of 6, 30, 60, 90 and 120 plies. The research concentrated on the measurement of fracture toughness utilizing the center-cracked tension, compact tension and three point bend specimen configurations. The development of subcritical damage at the crack tip was studied nondestructively using enhanced X-ray radiography and destructively using the laminate deply technique. The test results showed fracture toughness to be a function of laminate thickness. The fracture toughness of the 0 + or - 45/90 sub ns and 0/90 sub ns laminates decreased with increasing thickness and asymptotically approached lower bound values of 30 ksi square root of in. (1043 MPa square root of mm and 25 ksi square root of in (869 MPa square root of mm respectively. In contrast to the other two laminates, the fracture toughness of the 0/+ or - 45 sub ns laminate increased sharply with increasing thickness but reached an upper plateau value of 40 ksi square root of in (1390 MPa square root of mm) at 30 plies. Fracture toughness was independent of crack size for both thin and thick laminates for all three laminate types except for the 0/90 sub 2s laminate which spilt extensively. The center cracked tension, three point bend and compact tension specimens gave comparable results.

Harris, C. E.↗