NASA NTRS1992

Buffer layers for high-Tc thin films on sapphire

Buffer layers of various oxides including CeO2 and yttrium-stabilized zirconia (YSZ) have been deposited on R-plane sapphire. The orientation and crystallinity of the layers were optimized to promote epitaxial growth of YBa2Cu3O(7-delta) (YBCO) thin films. An ion beam channeling minimum yield of about 3 percent was obtained in the CeO2 layer on sapphire, indicating excellent crystallinity of the buffer layer. Among the buffer materials used, CeO2 was found to be the best one for YBCO thin films on R-plane sapphire. High Tc and Jc were obtained in YBCO thin films on sapphire with buffer layers. Surface resistances of the YBCO films were about 4 mOmega at 77 K and 25 GHz.

Wu, X. D.↗

NASA NTRS1991

Epitaxial yttria-stabilized zirconia on (1 -1 0 2) sapphire for YBa2Cu3O(7-delta) thin films

Epitaxial yttria-stabilized zirconia (YSZ) films were deposited on (1 -1 0 2) sapphire by pulsed laser deposition. The films are formed in a cubic phase with the a axis normal to the substrate surface. Ion beam channeling measurements show that the YSZ films are highly crystalline with a channeling minimum yield of 8 percent. The epitaxial relationship between the film and substrate is further confirmed by a cross-section TEM study. Epitaxial YBa2Cu3O(7-delta) thin films deposited on YSZ/sapphire have Tc and Jc of up to 89 K and 10 to the 6th A/sq cm at 77 K, respectively.

Wu, X. D.↗