Advanced Anion Exchange Membranes with Tunable Water Transport for PGM-Free AEMFCs

This project advanced the synthesis, characterization, and testing of anion exchange membranes for use in fuel cells. Our goal was to improve the water transport in anion exchange membrane fuel cells to improve their performance and durability. Through the work in this project we: 1) developed new composite anion exchange membranes through polymer synthesis and membrane casting into mechanical supports; 2) optimized electrode architecture and cell conditions to achieve; 3) demonstrated an integrated approach to achieving over 1 W/cm 2 in an operating device. While we did not achieve 1000 hours of continuous operation, we demonstrated multiple runs of more than 300 hours of device performance at steady-state.

08 HYDROGEN↗

DOE OSTI2021

Component Development for Alkaline URFCs

Performance, cost, and durability of the catalyst materials are the key factors that govern commercialization of H 2 -based energy conversion devices such as unitized regenerative fuel cells (URFCs). Compared to existing battery systems, URFCs offer superior energy density and performance over prolonged operation. In addition, alkaline URFC systems, can utilize low-cost platinum group metal-free (PGM-free) catalysts, resulting in much lower overall system costs. This project seeks to address the major obstacles faced in URFC systems such as cost and efficiency and establish a URFC technical capability through the strategic partnership between UofSC and SRNL. The research focuses on the development of low-PGM and PGM-free based bifunctional oxygen catalysts and electrodes, as well as the development of a URFC testing capability at SRNL.

25 ENERGY STORAGE↗

DOE OSTI2021

Large Scale Synthesis of Manganese Oxide/Reduced Graphene Oxide Composites as Anode Materials for Long Cycle Lithium Ion Batteries

Manganese oxides have been frequently used as cathodes in primary batteries. Applications of manganese oxides in secondary batteries are limited by low electrical conductivity and rapid capacity fading because of electrode pulverization and aggregation. In this study, a solid-state synthetic strategy is presented that successfully combines nanosize (~ 50 nm) nickel doped α-MnO 2 with reduced graphene oxides as highly stable composite anodes in lithium ion batteries. The synthesis approach is easy to scale up and suitable for industrial applications. Here, the rationally designed Ni-α-MnO 2 /RGO was tested in galvanostatic half coin cells for Li + charge-discharge studies. The results show that this composite maintains a high capacity of 615 mAh g -1 even after 200 cycles at a high current rate of 1 C (830 mA g -1 ), and with a high Coulombic efficiency near 99%. The anodes exhibit excellent rate capability in a wide range of rate testing from 0.2 to 10 C, without showing capacity decay. This superior anode performance is ascribed to the reduced size of α-MnO 2 domains that are well dispersed in an RGO matrix, which affords good ionic/elec. cond., low charge transfer resistance and mitigates issues of vol. expansion of the anodic active materials. This study opens up an avenue for developing the manufacturing of high-performance electrodes for real applications, such as batteries in electrical vehicles.