Naik, R. A.

Publications and source records attributed to Naik, R. A..

At least 19 records

NASA NTRS1994

Comparison Of Models Of Metal-Matrix Composites

Report presents comparative review of four mathematical models of micromechanical behaviors of fiber/metal-matrix composite materials. Models differ in various details, all based on properties of fiber and matrix constituent materials, all involve square arrays of fibers continuous and parallel and all assume complete bonding between constituents. Computer programs implementing models used to predict properties and stress-vs.-strain behaviors of unidirectional- and cross-ply laminated composites made of boron fibers in aluminum matrices and silicon carbide fibers in titanium matrices. Stresses in fiber and matrix constituent materials also predicted.

Bigelow, C. A.↗

NASA NTRS1993

An analysis of fiber-matrix interface failure stresses for a range of ply stress states

A graphite/bismaleimide laminate was prepared without the usual fiber treatment and was tested over a wide range of stress states to measure its ply cracking strength. These tests were conducted using off-axis flexure specimens and produced fiber-matrix interface failure data over a correspondingly wide range of interface stress states. The absence of fiber treatment, weakened the fiber-matrix interfaces and allowed these tests to be conducted at load levels that did not yield the matrix. An elastic micromechanics computer code was used to calculate the fiber-matrix interface stresses at failure. Two different fiber-array models (square and diamond) were used in these calculations to analyze the effects of fiber arrangement as well as stress state on the critical interface stresses at failure. This study showed that both fiber-array models were needed to analyze interface stresses over the range of stress states. A linear equation provided a close fit to these critical stress combinations and, thereby, provided a fiber-matrix interface failure criterion. These results suggest that prediction procedures for laminate ply cracking can be based on micromechanics stress analyses and appropriate fiber-matrix interface failure criteria. However, typical structural laminates may require elastoplastic stress analysis procedures that account for matrix yielding, especially for shear-dominated ply stress states.

Crews, J. H.↗

NASA NTRS1992

Micromechanical combined stress analysis: MICSTRAN, a user manual

Composite materials are currently being used in aerospace and other applications. The ability to tailor the composite properties by the appropriate selection of its constituents, the fiber and matrix, is a major advantage of composite materials. The Micromechanical Combined Stress Analysis (MICSTRAN) code provides the materials engineer with a user-friendly personal computer (PC) based tool to calculate overall composite properties given the constituent fiber and matrix properties. To assess the ability of the composite to carry structural loads, the materials engineer also needs to calculate the internal stresses in the composite material. MICSTRAN is a simple tool to calculate such internal stresses with a composite ply under combined thermomechanical loading. It assumes that the fibers have a circular cross-section and are arranged either in a repeating square or diamond array pattern within a ply. It uses a classical elasticity solution technique that has been demonstrated to calculate accurate stress results. Input to the program consists of transversely isotropic fiber properties and isotropic matrix properties such as moduli, Poisson's ratios, coefficients of thermal expansion, and volume fraction. Output consists of overall thermoelastic constants and stresses. Stresses can be computed under the combined action of thermal, transverse, longitudinal, transverse shear, and longitudinal shear loadings. Stress output can be requested along the fiber-matrix interface, the model boundaries, circular arcs, or at user-specified points located anywhere in the model. The MICSTRAN program is Windows compatible and takes advantage of the Microsoft Windows graphical user interface which facilitates multitasking and extends memory access far beyond the limits imposed by the DOS operating system.

Naik, R. A.↗

NASA NTRS1991

Simplified micromechanical equations for thermal residual stress analysis of coated fiber composites

The fabrication of metal matrix composites poses unique problems to the materials engineer. The large thermal expansion coefficient (CTE) mismatch between the fiber and matrix leads to high tensile residual stresses at the fiber/matrix (F/M) interface which could lead to premature matrix cracking during cooldown. Fiber coatings could be used to reduce thermal residual stresses. A simple closed form analysis, based on a three phase composite cylinder model, was developed to calculate thermal residual stresses in a fiber/interphase/matrix system. Parametric studies showed that the tensile thermal residual stresses at the F/M interface were very sensitive to the CTE and thickness of the interphase layer. The modulus of the layer had only a moderate effect on tensile residual stresses. For a silicon carbide titanium aluminide composite, the tangential stresses were 20 to 30 pct. larger than the axial stresses, over a wide range of interphase layer properties, indicating a tendency to form radial matrix cracks during cooldown. Guidelines for the selection of appropriate material properties of the fiber coating were also derived in order to minimize thermal residual stresses in the matrix during fabrication.

Naik, R. A.↗

NASA NTRS1991

Fracture mechanics analysis for various fiber/matrix interface loadings

Fiber/matrix (F/M) cracking was analyzed to provide better understanding and guidance in developing F/M interface fracture toughness tests. Two configurations, corresponding to F/M cracking at a broken fiber and at the free edge, were investigated. The effects of mechanical loading, thermal cooldown, and friction were investigated. Each configuration was analyzed for two loadings: longitudinal and normal to the fiber. A nonlinear finite element analysis was performed to model friction and slip at the F/M interface. A new procedure for fitting a square-root singularity to calculated stresses was developed to determine stress intensity factors (K sub I and K sub II) for a bimaterial interface crack. For the case of F/M cracking at a broken fiber with longitudinal loading, crack tip conditions were strongly influenced by interface friction. As a result, an F/M interface toughness test based on this case was not recommended because nonlinear data analysis methods would be required. For the free edge crack configuration, both mechanical and thermal loading caused crack opening, thereby avoiding frictional effects. A F/M interface toughness test based on this configuration would provide data for K(sub I)/K(sub II) ratios of about 0.7 and 1.6 for fiber and radial normal loading, respectively. However, thermal effects must be accounted for in the data analysis.

Naik, R. A.↗

NASA NTRS1991

Fracture mechanics analysis for various fiber/matrix interface loadings

Fiber/matrix (F/M) cracking was analyzed to provide better understanding and guidance in developing F/M interface fracture toughness tests. Two configurations, corresponding to F/M cracking at a broken fiber and at the free edge, were investigated. The effects of mechanical loading, thermal cooldown, and friction were investigated. Each configuration was analyzed for two loadings: longitudinal and normal to the fiber. A nonlinear finite element analysis was performed to model friction and slip at the F/M interface. A new procedure for fitting a square-root singularity to calculated stresses was developed to determine stress intensity factors (K sub I and K sub II) for a bimaterial interface crack. For the case of F/M cracking at a broken fiber with longitudinal loading, crack tip conditions were strongly influenced by interface friction. As a result, an F/M interface toughness test based on this case was not recommended because nonlinear data analysis methods would be required. For the free edge crack configuration, both mechanical and thermal loading caused crack opening, thereby avoiding frictional effects. An F/M interface toughness test based on this configuration would provide data for K(sub I)/K(sub II) ratios of about 0.7 and 1.6 for fiber and radial normal loading, respectively. However, thermal effects must be accounted for in the data analysis.

Naik, R. A.↗

NASA NTRS1990

A macro-micromechanics analysis of a notched metal matrix composite

A macro-micromechanics analysis was formulated to determine the matrix and fiber behavior near the notch tip in a center-notched metal matrix composite. Results are presented for a boron/aluminum monolayer. The macro-level analysis models the entire notched specimen using a three dimensional finite element program which uses the vanishing-fiber-diameter model to model the elastic-plastic behavior of the matrix and the elastic behavior of the fiber. The micro-behavior is analyzed using a Discrete Fiber-Matrix (DFM) model containing one fabric and the surrounding matrix. The dimensions of the DFM model were determined by the ply thickness and the fiber volume fraction and corresponded to the size of the notch-tip element in the macro-level analysis. The boundary conditions applied to the DFM model were determined from the macro-level analysis. Stress components within the DFM model were calculated and stress distributions are presented along selected planes and surfaces within the DFM model, including the fiber-matrix interface. Yielding in the matrix was examined at the notch tip in both the macro- and micro-level analyses. The DFM model predicted higher stresses (24 percent) in the fiber compared to the global analysis. In the notch-tip element, the interface stresses indicated that a multi-axial criterion may be required to predict interfacial failure. The DFM analysis predicted yielding to initiate in the notch-tip element at a stress level 28 percent lower than predicted by the global analysis.

Bigelow, C. A.↗

NASA NTRS1990

Micromechanical thermal analysis of interphase region in a titanium aluminide MMC

The high reactivity between the fiber and matrix in silicon carbide/titanium aluminide MMCs leads to the formation of brittle reaction products at the fiber/matrix (F/M) interface. Also, the high thermal expansion coefficient mismatch between the fiber and matrix leads to high tensile residual stresses at the F/M interface, and this can lead to premature cracking during cooldown. One solution to these problems is the use of a metallic fiber coating like Ta which acts as an F/M diffusion barrier and reacts with the matrix to form a beta stabilized compliant layer. A finite element micromechanics analysis was performed to study the effects of Ta and beta interphase layers on the thermal residual stresses during consolidation. A 5-micron-thick beta layer reduced cool-down stresses by 8 percent compared to a 2 percent reduction computed for a Ta layer of the same thickness. Plastic yielding in the Ta was not effective in reducing cool-down stresses. Compliant alpha-2 particles next to the stiffer gamma particles reduced stresses in the gamma particles by less than 2 percent. A simple closed form analysis was developed to calculate thermal residual stresses in a fiber/interphase/matrix system. A 2-micron-thick Ag interphase layer was found to reduce residual stresses by about 11 percent.

Naik, R. A.↗

NASA NTRS1990

Observations of fatigue crack initiation and damage growth in notched titanium matrix composites

The purpose was to characterize damage initiation and growth in notched titanium matrix composites at room temperature. Double edge notched or center open hole SCS-6/Ti-15-3 specimens containing 0 deg plies or containing both 0 and 90 deg plies were fatigued. The specimens were tested in the as-fabricated (ASF) and in heat-treated conditions. A local strain criterion using unnotched specimen fatigue data was successful in predicting fatigue damage initiation. The initiation stress level was accurately predicted for both a double edge notched unidirectional specimen and a cross-plied center hole specimen. The fatigue produced long multiple cracks growing from the notches. These fatigue cracks were only in the matrix material and did not break the fibers in their path. The combination of matrix cracking and fiber/matrix debonding appears to greatly reduce the stress concentration around the notches. The laminates that were heat treated showed a different crack growth pattern. In the ASF specimens, matrix cracks had a more tortuous path and showed considerable more crack branching. For the same specimen geometry and cyclic stress, the (0/90/0) laminate with a hole had far superior fatigue resistance than the matrix only specimen with a hole.

Naik, R. A.↗

NASA NTRS1990

Fatigue damage growth mechanisms in continuous fiber reinforced titanium matrix composites

The role of fiber/matrix interface strength, residual thermal stresses, and fiber and matrix properties on fatigue damage accumulation in continuous fiber metal matrix composites (MMC) is discussed. Results from titanium matrix silicon carbide fiber composites is the primary topic of discussion. Results were obtained from both notched and unnotched specimens at room and elevated temperatures. The stress in the 0 deg fibers was identified as the controlling factor in fatigue life. Fatigue of the notched specimens indicated that cracks can grow in the matrix materials without breaking fibers.

Johnson, W. S.↗

NASA NTRS1990

Ply-level failure analysis of a graphite/epoxy laminate under bearing-bypass loading

A combined experimental and analytical study was conducted to investigate and predict the failure modes of a graphite/epoxy laminate subjected to combined bearing and bypass loading. Tests were conducted in a test machine that allowed the bearing-bypass load ratio to be controlled while a single-fastener coupon was loaded to failure in either tension or compression. Onset and ultimate failure modes and strengths were determined for each test case. The damage-onset modes were studied in detail by sectioning and micrographing the damaged specimens. A two-dimensional, finite-element analysis was conducted to determine lamina strains around the bolt hole. Damage onset consisted of matrix cracks, delamination, and fiber failures. Stiffness loss appeared to be caused by fiber failures rather than by matrix cracking and delamination. An unusual offset-compression mode was observed for compressive bearing-bypass loading in which the specimen failed across its width along a line offset from the hole. The computed lamina strains in the fiber direction were used in a combined analytical and experimental approach to predict bearing-bypass diagrams for damage onset from a few simple tests.

Naik, R. A.↗

NASA NTRS1990

Fatigue damage growth mechanisms in continuous fiber reinforced titanium matrix composites

The role of fiber/matrix interface strength, residual thermal stresses, and fiber and matrix properties on fatigue damage accumulation in continuous fiber metal matrix composites (MMC) will be discussed. Results from titanium matrix/silicon-carbide fiber composites will be the primary topic of discussion. Results have been obtained from both notched and unnotched specimens at room and elevated temperatures. The stress in the 0 deg fibers has been indentified as the controlling factor in fatigue life. Fatigue of the notched specimens indicated that cracks can grow many fiber spacings in the matrix materials without breaking fibers.

Johnson, W. S.↗

NASA NTRS1989

Effects of T-tabs and large deflections in DCB specimen tests

A simple strength of materials analysis was developed for a double-cantilever beam (DCB) specimen to account for geometric nonlinearity effects due to large deflections and T-tabs. A new DCB data analysis procedure was developed to include the effects of these nonlinearities. The results of the analysis were evaluated by DCB tests performed for materials having a wide range of toughnesses. The materials used in the present study were T300/5208, IM7/8551-7, and AS4/PEEK. Based on the present analysis, for a typical deflection/crack length ratio of 0.3 (for AS4/PEEK), T-tabs and large deflections cause a 15 percent and 3 percent error, respectively, in the computer Mode 1 strain energy release rate. Design guidelines for DCB specimen thickness and T-tab height were also developed in order to keep errors due to these nonlinearities within 2 percent. Based on the test results, for both hinged and tabbed specimens, the effects of large deflection on the Mode 1 fracture toughness (G sub Ic) were almost negligible (less than 1 percent) in the case of T300/5208 and IM7/8551-7; however, AS4/PEEK showed a 2 to 3 percent effect. The effects of T-tabs G sub Ic were more significant for all the materials with T300/5208 showing a 5 percent error, IM7/8551-7 a 15 percent error, and, AS4/PEEK a 20 percent error.

Naik, R. A.↗

NASA NTRS1989

Stress analysis method for clearance-fit joints with bearing-bypass loads

Within a multi-fastener joint, fastener holes may be subjected to the combined effects of bearing loads and loads that bypass the hole to be reacted elsewhere in the joint. The analysis of a joint subjected to search combined bearing and bypass loads is complicated by the usual clearance between the hole and the fastener. A simple analysis method for such clearance-fit joints subjected to bearing-bypass loading has been developed in the present study. It uses an inverse formulation with a linear elastic finite-element analysis. Conditions along the bolt-hole contact arc are specified by displacement constraint equations. The present method is simple to apply and can be implemented with most general purpose finite-element programs since it does not use complicated iterative-incremental procedures. The method was used to study the effects of bearing-bypass loading on bolt-hole contact angles and local stresses. In this study, a rigid, frictionless bolt was used with a plate having the properties of a quasi-isotropic graphite/epoxy laminate. Results showed that the contact angle as well as the peak stresses around the hole and their locations were strongly influenced by the ratio of bearing and bypass loads. For single contact, tension and compression bearing-bypass loading had opposite effects on the contact angle. For some compressive bearing-bypass loads, the hole tended to close on the fastener leading to dual contact. It was shown that dual contact reduces the stress concentration at the fastener and would, therefore, increase joint strength in compression. The results illustrate the general importance of accounting for bolt-hole clearance and contact to accurately compute local bolt-hole stresses for combined bearings and bypass loading.

Naik, R. A.↗

NASA NTRS1989

Stress analysis method for clearance-fit joints with bearing-bypass loads

A simple direct stress analysis method is proposed for a laminate with a clearance-fit fastener subjected to combined bearing and bypass loads in tension or compression, including bearing and bypass loads on bolt-hole contact and local stresses. The approach uses a linear-elastic finite element analysis with an inverse formulation; conditions along the bolt-hole interface are specified by constraint equations that limit nodal displacements to a circular arc corresponding to the bolt diameter. The application of the method to the analysis of the effects of bearing-bypass loading on bolt-hole contact angles and local stresses, with the plate material properties representing a quasi-isotropic T300/5208 graphite/epoxy laminate, is discussed.

Naik, R. A.↗

NASA NTRS1989

A comparison of various micromechanics models for metal matrix composites

Four micromechanics models currently used in the analysis of metal matrix composites are reviewed. The four models are the vanishing fiber diameter model, the Aboudi model, the multicell model, and discrete fiber-matrix model. Results predicted by computer programs based on each of the models are compared. Comparisons are made for the laminate properties and laminate stress-strain behavior for boron/aluminum and silicon-carbide/titanium composites. The predictions of constituent stresses are also compared. The predictions are compared to experimental data. Each of the models did a reasonably good job predicting laminate properties and stress-strain behavior. Thus, the discriminator between the models is a question of what type of results are required, the capabilities of the model and program, or the ease of operation. The choice of a model and program depends on several factors and the same program may not be the best choice for all analysis needs. The descriptions and comparisons made in this paper should aid in the choice of a model and program.

Bigelow, C. A.↗

NASA NTRS1989

Effect of a high temperature cycle on the mechanical properties of silicon carbide/titanium metal matrix composites

An investigation is conducted of the effects of the SPF/DB cycle on continuous SiC fiber-reinforced Ti-15V-3Cr-3Al-3Sn composite's matrix, fiber, and matrix-fiber interface. The fibers in question, designated SCS-6, have a carbon core and thin, carbon-rich surface. The fatigue endurance limit at 50,000 cycles for the SPF/DB specimens was 50 percent lower than for the as-fabricated material. The substantial changes in tensile strength, fatigue life, and fracture-surface appearance due to the SPF-DB cycle are explained by a difference in the failure mechanisms due to SPF/DB-induced changes in the fiber/matrix interface strength.

Naik, R. A.↗

NASA NTRS1988

Ply-level failure analysis of a graphite/epoxy laminate under bearing-bypass loading

A combined experimental and analytical study was conducted to investigate and predict the failure modes of a graphite/epoxy laminate subjected to combined bearing and bypass loading. Tests were conducted in a test machine that allowed the bearing-bypass load ratio to be controlled while a single-fastener coupon was loaded to failure in either tension or compression. Onset and ultimate failure modes and strengths were determined for each test case. The damage-onset modes were studied in detail by sectioning and micrographing the damaged specimens. A two-dimensional, finite-element analysis was conducted to determine lamina strains around the bolt hole. Damage onset consisted of matrix cracks, delamination, and fiber failures. Stiffness loss appeared to be caused by fiber failures rather than by matrix cracking and delamination. An unusual offset-compression mode was observed for compressive bearing-bypass laoding in which the specimen failed across its width along a line offset from the hole. The computed lamina strains in the fiber direction were used in a combined analytical and experimental approach to predict bearing-bypass diagrams for damage onset from a few simple tests.

Naik, R. A.↗