DOE OSTI2023

Nanosecond Laser Annealing of NMC 811 Cathodes for Enhanced Performance

Improved performance of lithium-ion batteries (LIBs) plays a critical role in the future of next- generation battery applications. Nickel-rich layered oxides such as LiNi 0.8 Mn 0.1 Co 0.1 O 2 (NMC 811), are popular cathodes due to their high energy densities. However, they suffer from high surface reactivity, which results in the formation of Li 2 CO 3 passive layer. Herein, we show the role of nanosecond pulsed laser annealing (PLA) in improving the current capacity and cycling stability of LIBs by reducing the carbonate layer, in addition to forming a protective LiF layer and manipulating the NMC 811 microstructures. We use high-power nanosecond laser pulses in a controlled way to create nanostructured surface topography which has a positive impact on the capacity retention and current capacity by providing an increased active surface area, which influences the diffusion kinetics of lithium-ions in the electrode materials during the battery cycling process. Advanced characterizations show that the PLA treatment results in the thinning of the passive Li 2 CO 3 layer, which is formed on as-received NMC811 samples, along with the decomposition of excess polyvinylidene fluoride (PVDF) binder. The high-power laser interacts with the decomposed binder and surface Li + to form LiF phase, which acts as a protective layer to prevent surface reactive sites from initiating parasitic reactions. As a result, the laser treated cathodes show relative increase of the current capacity of up to 50%, which is consistent with electrochemical measurements of LiB cells.

25 ENERGY STORAGEā†—
DOE OSTI2023

Microstructure and defect engineering of graphite anodes by pulsed laser annealing for enhanced performance of lithium-ion batteries

We report nanosecond pulsed laser annealing significantly improves cyclability and current carrying capacity of lithium-ion batteries (LIBs). This improvement is achieved by engineering of microstructure and defect contents present in graphite in a controlled way by using pulsed laser annealing (PLA) to increase the number density of Li + ion trapping sites. The PLA treatment causes the following changes: (1) creates surface steps and grooves between the grains to improve Li + ion charging and intercalation rates; (2) removes inactive polyvinylidene difluoride (PVDF) binder from the top of graphite grains and between the grains which otherwise tends to block the Li + migration; and (3) produces carbon vacancies in (0001) planes which can provide Li + charging sites. From X-ray diffraction data, we find upshift in diffraction peak or reduction in planar spacing, from which vacancy concentration was estimated to be about 1.0%, which is higher than the thermodynamic equilibrium concentration of vacancies. The laser treatment creates single and multiple C vacancies which provide sites for Li + ions, and it also produces steps and grooves for Li + ions to enter the intercalating sites. It is envisaged that the formation of these sites enhances Li+ ion absorption during charge and discharge cycles. The current capacity increases from an average 360 mAh/g to 430 mAh/g, and Cā€“V shows significant reduction in SEI layer formation after the laser treatment. If the vacancy concentration is too high and charge-discharge cycles are long, then trapping of electrons by Li + may occur, which can lead to Li 0 formation and Li plating causing reduction in current capacity.

25 ENERGY STORAGEā†—