DOE OSTI2020

A Low-Cost Iron-Based Current Collector for Alkaline Battery Electrodes

The use of three-dimensional porous nickel foam as the current collector of the nickel hydroxide electrode adds significantly to the cost of the nickel-based alkaline rechargeable batteries. Although iron is considerably less expensive than nickel, iron corrodes at the operating potential of the nickel hydroxide electrode. We have found that a 70–100 nm thick thermal coating of cobalt ferrite spinel protects the iron from corrosion. Such a coated iron substrate was found to be stable against corrosion even when polarized anodically at 10 mA cm -2 in 30% potassium hydroxide electrolyte for 1000 h. While the thermal coating of cobalt ferrite protected iron against corrosion, incorporation of lithium ions into the coating was found to enhance the electrical conductivity of the coating. XPS and EXAFS studies confirmed that the enhanced conductivity resulted from an increase in the population of Co 3+ in the ferrite spinel lattice. An inexpensive iron (steel) substrate protected by such a coating when used as a nickel hydroxide battery electrode exhibited a specific capacity of 0.25 Ah g -1 at C/5 discharge rate, comparable to a nickel hydroxide electrode based on a relatively expensive nickel foam substrate. The steel-based electrode also exhibited no noticeable degradation over 150 cycles at C/2 rate. This demonstration of a robust and economical steel substrate presents a unique opportunity for reducing the cost of the nickel hydroxide battery electrode in alkaline batteries

25 ENERGY STORAGE↗
NASA NTRS2007

Reversible Intercalation of Fluoride-Anion Receptor Complexes in Graphite

We have demonstrated a route to reversibly intercalate fluoride-anion receptor complexes in graphite via a nonaqueous electrochemical process. This approach may find application for a rechargeable lithium-fluoride dual-ion intercalating battery with high specific energy. The cell chemistry presented here uses graphite cathodes with LiF dissolved in a nonaqueous solvent through the aid of anion receptors. Cells have been demonstrated with reversible cathode specific capacity of approximately 80 mAh/g at discharge plateaus of upward of 4.8 V, with graphite staging of the intercalant observed via in situ synchrotron X-ray diffraction during charging. Electrochemical impedance spectroscopy and B-11 nuclear magnetic resonance studies suggest that cointercalation of the anion receptor with the fluoride occurs during charging, which likely limits the cathode specific capacity. The anion receptor type dictates the extent of graphite fluorination, and must be further optimized to realize high theoretical fluorination levels. To find these optimal anion receptors, we have designed an ab initio calculations-based scheme aimed at identifying receptors with favorable fluoride binding and release properties.

electrolytes↗
NASA NTRS2006

Battery Control Boards for Li-Ion Batteries on Mars Exploration Rovers

Rechargeable Lithium-ion batteries have been operating successfully on both Spirit and Opportunity rovers for the last two years, which includes six months of Assembly Launch and Test Operations (ATLO), seven months of cruise and about eleven months of surface operations. The Battery Control Boards designed and fabricated in-house would protect cells against overcharge and over-discharge and provide cell balance. Their performance has thus far been quite satisfactory. The ground data o the mission simulation battery project little capacity loss of less than 3% during cruise and 180 sols. Batteries are poised to extend the mission beyond six months, if not a couple of years.

Ewell, R.↗
NASA NTRS2006

Sodium Borohydride/Hydrogen Peroxide Fuel Cells For Space Application

This viewgraph presentation examines Sodium Borohydride and Hydrogen Peroxide Fuel Cells as they are applied to space applications. The topics include: 1) Motivation; 2) The Sodium Borohydride Fuel Cell; 3) Sodium Borohydride Fuel Cell Test Stands; 4) Fuel Cell Comparisons; 5) MEA Performance; 6) Anode Polarization; and 7) Electrode Analysis. The benefits of hydrogen peroxide as an oxidant and benefits of sodium borohydride as a fuel are also addressed.

fuel cells↗
NASA NTRS2005

Investigation of Ruthenium Dissolution in Advanced Membrane Electrode Assemblies for Direct Methanol Based Fuel Cell Stacks

Dissolution of ruthenium was observed in the 80-cell stack. Duration testing was performed in single cell MEAs to determine the pathway of cell degradation. EDAX analysis on each of the single cell MEAs has shown that the Johnson Matthey commercial catalyst is stable in DMFC operation for 250 hours, no ruthenium dissolution was observed. Changes in the hydrophobicity of the cathode backing papers was minimum. Electrode polarization analysis revealed that the MEA performance loss is attributed to changes in the cathode catalyst layer. Ruthenium migration does not seem to occur during cell operation but can occur when methanol is absent from the anode compartment, the cathode compartment has access to air, and the cells in the stack are electrically connected to a load (Shunt Currents). The open-to-air cathode stack design allowed for: a) The MEAs to have continual access to oxygen; and b) The stack to sustain shunt currents. Ruthenium dissolution in a DMFC stack can be prevented by: a) Developing an internally manifolded stacks that seal reactant compartments when not in operation; b) Bringing the cell voltages to zero quickly when not in operation; and c) Limiting the total number of cells to 25 in an effort to limit shunt currents.

alternative power sources↗
NASA NTRS2005

Investigation of Ruthenium Dissolution in Advanced Membrane Electrode Assemblies for Direct Methanol Based Fuel Cells Stacks

This viewgraph presentation gives a detailed review of the Direct Methanol Based Fuel Cell (DMFC) stack and investigates the Ruthenium that was found at the exit of the stack. The topics include: 1) Motivation; 2) Pathways for Cell Degradation; 3) Cell Duration Testing; 4) Duration Testing, MEA Analysis; and 5) Stack Degradation Analysis.

Direct Methanol Fuel Cells, (DMFC)↗
NASA NTRS2004

Lithium-sulfur dioxide batteriess on Mars Rovers

Lithium-sulfur dioxide batteries exhibit voltage delay, which tends to increase at low discharge temperatures, especially after extended storage at warm temperatures. In the absence of a depassivation circuit, as provided on earlier missions, e.g., Galileo, we were required to depassivate the lander primary batteries in a unique manner. The batteries were brought onto a shunt-regulated bus set at preselected discharge voltages, thus affecting depassivation during constant discharge voltage. Several ground tests were performed, on cells, cell strings and battery assembly with five parallel strings, to identify optimum shunt voltages and durations of depassivation. We also examined the repassivation of lithium anodes, subsequent to depassivation. IIn this paper, we will describe these studies, in detail, as well as the depassivation of the lander flight batteries on both Spirit and 0pportunity rovers prior to the EDL sequence and their performance during landing on Mars.

Surampudi, S.↗
NASA NTRS2004

Lithium-sulfur dioxide batteries on Mars rovers

NASA's 2003 Mars Exploration Rover (MER) missions, Spirit and Opportunity, have been performing exciting surface exploration studies for the past six months. These two robotic missions were aimed at examining the presence of water and, thus, any evidence of life, and at understanding the geological conditions of Mars, These rovers have been successfully assisted by primary lithium-sulfur dioxide batteries during the critical entry, descent, and landing (EDL) maneuvers. These batteries were located on the petals of the lander, which, unlike in the Mars Pathfinder mission, was designed only to carry the rover. The selection of the lithium-sulfur dioxide battery system for this application was based on its high specific energy and high rate discharge capability, combined with low heat evolution, as dictated by this application. Lithium-sulfur dioxide batteries exhibit voltage delay, which tends to increase at low discharge temperatures, especially after extended storage at warm temperatures, In the absence of a depassivation circuit, as provided on earlier missions, e.g., Galileo, we were required to depassivate the lander primary batteries in a unique manner. The batteries were brought onto a shunt-regulated bus set at pre-selected discharge voltages, thus affecting depassivation during constant discharge voltages. Several ground tests were preformed, on cells, cell strings and battery assembly with five parallel strings, to identify optimum shunt voltages and durations of depassivation. We also examined the repassivation of lithium anodes, subsequent to depassivation. In this paper, we will describe these studies, in detail, as well as the depassivation of the lander flight batteries on both Spirit and Opportunity rover prior to the EDL sequence and their performance during landing on Mars.

Lithium-SO2 batteries↗
NASA NTRS2004

High power, gel polymer lithium-ion cells with improved low temperature performance for NASA and DoD applications

Both NASA and the U.S. Army have interest in developing secondary energy storage devices that are capable of meeting the demanding performance requirements of aerospace and man-portable applications. In order to meet these demanding requirements, gel-polymer electrolyte-based lithium-ion cells are being actively considered, due to their promise of providing high specific energy and enhanced safety aspects.

high power li-ion batteries↗
NASA NTRS2003

Fuel cell environmental life cycle assessment : a progress report

Energy generation using fuel cells offers the possibility of high conversion efficiency and reduced pollution. Thus, in the futue, conventional methods of energy generation using coalfired power plants, natural gas turbines and internal combustion engines can potentially be replaced by fuel cells. The United States, Japan and several countries in Europe are currently developing fuel cells for transportation, distributed energy generation and portable electronics applications. On a system basis, the efficiency of chemical to electrical energy conversion in fuel cells can be as high as 45%. Also, because of the lower operating temperatures compared to turbines and internal combustion engines, emissions such as carbon monoxide and nitrogen oxides are extremely small. An assessment of the environmental impact of fuel cells over the entire lifecycle is needed to determine the specific benefits in various application scenarios. Such a comparative pollutants assessment must include a "cradle to grave" approach encompassing fuel production, fuel transportation, materials/manufacturing processes, waste management, and recycling. A comparative pollutant model would be a useful tool for industry and government in estimating energy savings and environmental credits, and providing a holistic understanding on regulatory needs. Another important benefit would be the ability to make appropriate comparisons with competitive energy generation technologies such as hybrids, turbines, and internal combustion engines, and to set up realistic targets. Also, exercising the model will assist in the initial screening for potential hot spots and showstoppers and focus on the right component technologies design for manufacturing, designs for input substitution and waste minimization, and prevent any unforeseen burdens.

Narayanan, S. R.↗