Additively Manufactured Molten Salt to Supercritical Carbon Dioxide Heat Exchanger
Design, fabrication, and experimental characterization of the performance of a molten salt (MS)-to-supercritical carbon dioxide (sCO 2 ) heat exchanger (HE) for concentrating solar power (CSP) applications using laser powder bed fusion (LPBF) additive manufacturing (AM) of nickel-based superalloys is presented in this report. The hypothesis is that such additively manufactured HEs will result in a monolithic, compact, low-pressure drop HE that is durable under cyclic operation at high temperature and high pressure in a corrosive salt environment. Two nickel-based superalloys were considered in the project- Haynes 230 (H230) and Haynes 282 (H282). Process windows for LPBF AM were established to provide dense low porosity parts for both alloys. Creep tests results on heat treated AM H230 and H282 samples showed that the AM fabricated specimens were as robust as the wrought specimens and showed no deficit in creep strength at high temperatures. Haynes 282 was down selected for the HE fabrication based on better dimensional tolerance, better corrosion resistance to chloride salt, and higher creep strength.
A Scalable Compact Additively Manufactured Molten Salt to Supercritical Carbon Dioxide Heat Exchanger for Solar Thermal Application
Design of an additively manufactured molten salt (MS) to supercritical carbon dioxide (sCO 2 ) primary heat exchanger (PHE) for solar thermal power generation is presented. The PHE is designed to handle temperatures up to 720 °C on the MS side and an internal pressure of 200 bar on the sCO 2 side. In the core, MS flows through a three-dimensional periodic lattice network, while sCO 2 flows within pin arrays. The design includes integrated sCO 2 headers located within the MS flow, allowing for a counterflow design of the PHE. The sCO 2 headers are configured to enable uniform flow distribution into each sCO 2 plate while withstanding an internal pressure of 200 bar and minimizing obstruction to the flow of MS around it. The structural integrity of the design is verified on additively manufactured (AM) 316 stainless steel sub-scale specimens. An experimentally validated, correlation-based sectional PHE core thermofluidic model is developed to study the impact of flow and geometrical parameters on the PHE performance, with varied parameters including the mass flowrate, surface roughness, and PHE dimensions. A process-based cost model is used to determine the impact of parameter variation on build cost. The model results show that a heat exchanger with a power density of 18.6 MW/m 3 (including sCO 2 header volume) and effectiveness of 0.88 can be achieved at a heat capacity rate ratio of 0.8. As a result, the impact of design and AM machine parameters on the cost of the PHE are assessed.
Optimizing the surface texture and chemistry of laser powder bed fusion (LPBF) Haynes 282 for increased solar absorptance
Explore the source record for details and available documents.
Cost of Using Laser Powder Bed Fusion to Fabricate a Molten Salt-to-Supercritial Carbon Dioxide Heat Exchanger for Concentrating Solar Power
Advances in manufacturing technologies and materials are crucial to the commercial deployment of energy technologies. We present the case of concentrating solar power (CSP) with molten salt (MS) thermal storage, where low-cost, high-efficiency heat exchangers (HXs) are needed to achieve cost competitiveness. Here, the materials required to tolerate the extreme operating conditions in CSP systems make it difficult or infeasible to produce them using conventional manufacturing processes. Although it is technically possible to produce HXs with adequate performance using additive manufacturing, specifically laser powder bed fusion (LPBF), here we assess whether doing so is cost-effective. We describe a process-based cost model (PBCM) to estimate the cost of fabricating a MS-to-supercritical carbon dioxide HX using LPBF. The PBCM is designed to identify modifications to designs, process choices, and manufacturing innovations that have the greatest effect on manufacturing cost. Our PBCM identified HX design and LPBF process modifications that reduced projected HX cost from $\$750$ per kilo-Watt thermal (kW-th) ($\$8$ /cm 3 ) to $\$350$ /kW-th ($\$6/$ cm 3 ) using currently available LPBF technology, and down to $\$220$ /kW-th ($\$4$ /cm 3 ) with improvements in LPBF technology that are likely to be achieved in the near term. The PBCM also informed a redesign of the HX design that reduced projected costs to $\$140$ –160/kW-th ($\$3$ /cm 3 ).
Performance characterization of M-cycle indirect evaporative cooler and heat recovery ventilator for commercial buildings – Experiments and model
Not Available
Performance model of an additively manufactured micro-pin array solar thermal central receiver
Not Available
An additively-manufactured molten salt-to-supercritical carbon di-oxide primary heat exchanger for solar thermal power generation – Design and techno-economic performance
The design and techno-economic performance of a compact additively manufactured (AM) molten salt (MS)-to-supercritical carbon di-oxide (sCO2) primary heat exchanger (PHE) for solar thermal application is described. The PHE design consists of sCO2 flow through an array of microscale pin fins while the MS flows through mm-scale rectangular channels. Constraints imposed by AM using laser powder bed fusion method are considered in the design. Structural and fluid flow simulations are performed to arrive at a viable design of the core and headers. A simplified one-dimensional steady state model for the PHE is developed including the impact of surface roughness from the AM process. A process-based cost model is used to determine the tradeoff between thermofluidic design and manufacturing cost. A parametric study is performed using the thermo-fluidic and cost models to determine the set of geometrical and flow variables that result in high power density and low cost, while restricting the pressure drop on the sCO2 side to less than 2% of line pressure. Flow rates of MS and sCO2 were varied over heat capacity rate ratios ranging from 0.2 to 1. Results indicate that it is possible to design a low-pressure drop AM PHE with an effectiveness of 90% and a power density in excess of 10 MW/m3 (including headers). Fabrication of representative nickel superalloy specimens are shown to demonstrate that low-porosity parts with the requisite dimensional tolerance of PHE core can be generated.
High Flux Microchannel Receiver Development (Final Report)
The opportunity addressed in this project was using microscale heat exchanger technology for improving solar thermal central receiver efficiency. This will result in smaller, less expensive components and reduce the levelized cost of electricity from concentrated solar thermal power. This micro-pin solar receiver (MSR) directly heats high pressure (25 MPa) supercritical carbon dioxide (sCO 2 ) from 550°C to 720°C with an incident flux of at least 120 W/cm 2 at a receiver efficiency of >90% (assuming availability of 95% absorptivity coating), and receiver cost target of less than $\$$150/kWt. Realization of the MSR required an understanding of thermal hydraulic performance of sCO 2 in micro-pin passages, mechanical behavior of high nickel alloys at high temperatures including joints, advanced fabrication methods of high nickel alloys (etching, machining, brazing, welding, diffusion bonding), and the cost implications of these when the concept is scaled to production volumes. The technology can be used with gases (sCO 2 , helium, etc.) or with liquids such as molten salt or liquid metal. Given the high pressure associated with sCO 2 , its use demonstrates a “worst case” scenario, and the successful development of the MSR for this application will result in the development of a technology also applicable to a range of other heat transfer fluids that will enable next generation CSP plants, including support of the Gen3CSP program.
High flux thermal receiver and method of use
A thermal receiver, such as a solar flux thermal receiver, is disclosed comprising a modular arrangement of arrayed microchannels or micropins to heat a working fluid by heat transfer. Disclosed solar receivers provide a much higher solar flux and consequently a significant reduction in thermal losses, size, and cost, relative to known receivers. Unit cell receivers can be numbered up and combined in parallel to form modules, and modules combined to form full scale receivers.