Nelson, Andrew T.

Publications and source records attributed to Nelson, Andrew T..

At least 37 records · Page 2
All sourcesNASA NTRSDOE OSTI
DOE OSTI2023

Accelerated fission rate irradiation design, pre-irradiation characterization, and adaptation of conventional PIE methods for U-10Mo and U-17Mo

Metallic U alloys have high U density and thermal conductivity and thus have been explored since the beginning of nuclear power research. Alloys of U with modest amounts of Mo, such as U-10 wt % Mo (U-10Mo), are of particular interest because the γ-U crystal structure in this alloying addition shows prolonged stability in reactor service. Historically, radiation data on U-10Mo fuels were collected in Na fast reactors or lower temperature research reactor conditions, but little is known about irradiation behavior, particularly swelling and creep, at irradiation temperatures between 250 and 500°C. This work discusses the methodology and pre-irradiation characterization results from a U-Mo irradiation campaign performed in the High Flux Isotope Reactor at Oak Ridge National Laboratory. U-10Mo and U-17Mo samples irradiations are being completed at temperatures ranging from 250 to 500°C to three targeted fission densities between 2 × 10 20 and 1.5 × 10 21 fissions per cubic centimeter. Swelling measurement of the specimen sizes studied here required development and assessment of new methods for volume determination before and after irradiation. Laser profilometry and X-ray computation tomography (XCT) were used to provide preirradiation characterization of samples to determine the error and applicability of each to determine swelling following irradiation. These outcomes are contextualized through use of BISON simulations performed to assess the predicted expansion of U-Mo fuels subjected to the irradiation conditions of this work. Use of existing BISON fuel performance models predicted a maximum of 7% swelling under the irradiation conditions of this study. Pre-irradiation characterization revealed the as-cast U-Mo fuel samples were uniformly large-grained fully cubic U crystals with small U-C/N bearing precipitates and pores distributed throughout. Samples were found to contain a bulk porosity between .4 and 3% because of the casting process. Local porosity in areas far from large, interconnected pores was found by Slice-and-View to be under .2%. Nanometer-sized precipitates rich in C and N were identified in all samples, likely because of impurities during the fabrication process. Dendritic bands were also observed throughout the samples. These bands were characterized by variable Mo content that deviated from the overall Mo content by 2–3 wt %. No other microstructural features were correlated to these bands. Mechanical properties were found to be slightly strengthened compared to literature reports of bulk U-Mo fuels due to the nano-scale precipitates throughout the sample.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗
DOE OSTI2022

Hydrogen effects on thermal diffusivity and electrical resistivity of zircaloy cladding

Thermal diffusivity measurements on Zirconium-based cladding materials have historically been a challenge due to the difficulty to measure on specimens with curved geometries, including nuclear grade Zircaloy cladding materials. Here, in this work, we first used laser flash analysis method and four-probe configuration method to measure the thermal diffusivity and electrical resistivity of Zircaloy tubes respectively, which show good agreement with Zircaloy plates in this work, as well as previously published data. The consistent results proved the applicability of the laser flash analysis setup and four-probe configuration method for investigating thermal diffusivity and electrical resistivity of Zircaloy tubes. We further investigated the hydrogen effect on thermal diffusivity and electrical resistivity of Zircaloy. Hydrogen plays significant roles in the thermal diffusivity of Zircaloy, which depends on the hydrogen concentration. For higher hydrogen contents (1130 and 1820 wppm in this work), where phase transformation (α-Zr + δ-hydride → α-Zr + β-Zr) occurs at 567 °C, thermal diffusivity decreases as a function of temperature at the α-Zr + δ-hydride phase regime, while increase at higher temperature at the α-Zr + β-Zr phase regime. For low hydrogen concentration, where hydride dissolved into α-Zr matrix phase at higher temperature, the thermal diffusivity is lower than non-hydrided Zircaloy-4 with similar temperature-dependent trends. Such observation demonstrates the hydrogen effects on reducing thermal diffusivity of α-Zr phase. Hydrogen increases the electrical resistivity of Zircaloy. Similar to thermal diffusivity results, the phase transformation causes a reversal of temperature-dependent trends in electrical resistivity results in Zircaloy-4 with higher hydrogen contents.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Hydriding, Oxidation, and Ductility Evaluation of Cr-Coated Zircaloy-4 Tubing

Accident-tolerant fuel concepts have been developed recently in diverse research programs. Recent research has shown clear advantages of Cr-coated Zr cladding over bare cladding tubes regarding oxidation behavior under the design basis loss-of-coolant accident condition. However, limited data are available about the hydriding behavior of the Cr coating. For that purpose, Cr-coated Zricaloy-4 tubes were tested to investigate the effects of hydriding, oxidation, and postquench ductility behavior on coated Zr cladding. A high-power impulse magnetron sputtering (HiPIMS) process was used to produce a high-density coating on the Zircaloy-4 tube surface. Coated and uncoated Zircaloy-4 tube specimens underwent one-sided hydriding in a tube furnace filled with pure hydrogen gas at 425 °C. The tubing specimen ends were sealed with Swagelok plugs before the hydriding runs. For uncoated specimens, H analysis of the hydrided specimens indicated that the H content increased as the test time and initial pressure increased. However, almost no change was observed for the coated specimens that were hydrided under the same test conditions. After one-sided hydriding, the hydrided coated and uncoated specimens were exposed to steam at high temperatures for two-sided oxidation studies to simulate accident conditions. The coated specimens showed a slower oxidation: oxygen pickup was 50% lower than the uncoated specimens tested under the same conditions. Ring compression testing was performed to evaluate the embrittlement behavior of the Cr-coated specimens after hydriding and oxidation. The results indicated that the HiPIMS coating provides excellent protection from hydriding and oxidation at high temperatures.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Prospects for additive manufacturing of nuclear fuel forms

Additive manufacturing (AM) is viewed as a critical enabling technology for achieving superior performance and improved economics across many sectors. Although the past decade has seen increased application of AM methods to nuclear reactor cladding and structural materials, exploration of AM as applied to the uranium-bearing nuclear fuel forms has been limited. The two major families of nuclear fuel forms (monolithic, particle/dispersion) are utilized with their own set of core objectives in mind, and their differences require distinct fabrication infrastructures. These reference fabrication methods impose many limitations on nuclear fuels. Further, both currently operating reactors and future concepts have the potential for improved performance if these accepted limitations are relaxed or removed entirely. The primary limitations of reference fabrication processes for the common nuclear fuel forms are outlined in this paper. This groundwork is then used to identify avenues of fuel performance specific to each of these fuel architectures that could be exploited if the restrictions of conventional fuel fabrication are removed. Moreover, multiple targets for AM studies are laid out for each of the major nuclear fuel variants. Finally, key strategic components to guide research activities in AM of nuclear fuels are outlined, with an emphasis on use of modeling and simulation to motivate research aims and embrace of an accelerated testing methodology to screen and quality new fuel forms.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗
DOE OSTI2022

3D printing of additive structures for nuclear fuels

A method for manufacturing a nuclear fuel compact is provided. The method includes forming an additive structure, consolidating a fuel matrix around the additive structure, and thermally processing the fuel matrix to form a fuel compact in which the additive structure is encapsulated therein. The additive structure optionally includes a vertical segment and a plurality of arm segments that extend generally radially from the vertical segment for conducting heat outwardly toward an exterior of the fuel compact. In addition to improving heat transfer, the additive structure may function as burnable absorbers, and may provide fission product trapping.

Terrani, Kurt A.↗
DOE OSTI2022

On the efficacy of post-build thermomechanical treatments to improve properties of Zirconium fabricated using ultrasonic additive manufacturing

Here, hot-isostatic pressing has been applied to Zirconium plate fabricated using the ultrasonic additive manufacturing (UAM) technique to enhance interfacial bond quality. Specimens heated to 800 C for 1 h at 100 MPa pressure showed grain growth across many prior foil-to-foil interfaces, thereby increasing foil adhesion. In addition to the material softening induced by a loss of Hall-Petch strengthening, premature failure of specimens loaded parallel to the build direction was observed. Premature specimen failure was attributed to the local delamination at prior foil-to-foil boundaries where grain growth was pinned by Ti impurities introduced during the UAM process via the interaction between a Ti-alloy buffer foil and the welded Zr-foils underneath. In addition, the presence of Ti along select foil interfaces resulted in the nucleation and growth of secondary (Zr,Ti)(Fe,Cr) laves phases during higher-temperature thermomechanical processing. Using a combination of micro-scale X-ray computed tomography, fractography, and in-situ digital image correlation, the effect of defects along prior foil-to-foil boundaries was revealed as delamination-assisted plasticity accelerated specimen failure in preferred tensile orientations. These findings underscore the importance of impurity control when optimizing weld quality of higher-strength material systems using ultrasonic welding.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Thermal conductivity evaluation of ion irradiated Si 3 N 4 and ZrN ceramics using spatial domain thermoreflectance

Nitride ceramics have been investigated for different applications in the nuclear industry, such as space nuclear power, fusion reactor diagnostics and plasma heating, inert matrix fuels, and accident tolerant fuels. Although thermal conductivity remains one of the most important properties to track following irradiation, traditional techniques such as laser flash and xenon flash are limited to bulk sample characterization, which requires lengthy and cost-consuming neutron irradiation. This work used spatial domain thermoreflectance (SDTR) for the micrometer-scale measurement of thermal conductivity in 15 MeV Ni ion-irradiated silicon nitride and zirconium nitride from 1 to 50 dpa and 300 to 700 °C. Here, the SDTR-measured unirradiated thermal conductivity was found to be consistent with the published data on bulk samples. Electrically conductive ZrN exhibits modest reduction after irradiation which is minimal at the highest irradiation temperatures. In electrically insulating Si 3 N 4 , the reduction is more significant and unlike ZrN, the reduction remains significant even at a higher irradiation temperature. The thermal resistance evolution following irradiation was compared with lattice swelling, which was determined using grazing incidence x-ray diffraction, and radiation-induced defects were observed using transmission electron microscopy. A saturation value was observed between 15 and 50 dpa for thermal conductivity degradation in both nitride ceramics and a direct correlation with high-temperature defect recombination was observed, as well as the potential presence of additional carrier scattering mechanisms.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Oxidation kinetics of SPS-densified U 3 Si 2 fuels—Microstructure impact

Here, U 3 Si 2 is a potential candidate for accident tolerant fuels because of its high uranium density and excellent thermal conductivity in comparison to UO 2 . However, U 3 Si 2 suffers from oxidation, steam corrosion, and subsequent disintegration/pulverization. The detailed investigation of kinetics that incorporates fundamental treatment of oxidation of U 3 Si 2 is scarcely reported, and the oxidation mechanisms have not been fully elucidated. In this paper, the oxidation behavior of microcrystalline (mc - ) and nanocrystalline (nc - ) U 3 Si 2 have been systematically investigated using a thermogravimetric analysis (TGA) apparatus through a series of isothermal and non-isothermal kinetic studies. The isothermal kinetic study with a model-fitting approach indicates oxidation activation energy of 85 kJ/mol for dense mc - U 3 Si 2 and 96.4 kJ/mol for nc - U 3 Si 2 pellets, while the isoconversional approach leads to an activation energy in the range of 70–85 kJ/mol for mc - U 3 Si 2 and 75–86 kJ/mol for nc - U 3 Si 2 with three most common model-free methods, including Kissinger–Akahira–Sunose, Flynn–Wall–Ozawa, and Friedman methods. The derivation of oxidation activation energies using both isothermal and isoconversional methods highlights the approach to evaluate the oxidation resistance of nuclear materials using TGA quantitatively and makes it possible to compare among various nuclear fuels.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗
DOE OSTI2022

In situ synchrotron tensile investigations on ultrasonic additive manufactured (UAM) zirconium

The microstructure evolution during room temperature uniaxial tensile straining of ultrasonic additive manufactured (UAM) zirconium was evaluated using the Advanced Photon Source (APS) facility. Miniature dog-bone tensile specimens of two orientations were cut from a UAM-fabricated zirconium bar for in situ synchrotron tensile tests. Wide-angle X-ray scattering (WAXS) scanning was used to unveil the changes in microstructure of the entire gauge regions throughout the straining. A series of WAXS data analysis methods were utilized to quantify both elastic and plastic deformation mechanisms within the strained specimens. Stress concentrations were identified during early stages of plastic deformation, which become candidate necking positions and eventually lead to failure. Additionally, fracture surface analysis implied that these stress concentration locations may be correlated to the fabrication defects, providing insightful guidance for future improvements of the UAM zirconium fabrication process.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Hydrothermal corrosion and steam oxidation behavior comparison of UAM and conventional Zry-4

Here, hydrothermal corrosion and steam exposures on ultrasonic additively manufactured (UAM) Zircaloy-4 (Zry-4) specimens were conducted to compare to wrought Zry-4 performance in both simulated pressurized water reactor (PWR) operation (330°C, 15 MPa, <50 ppb oxygen, 500h) and representative accident conditions (100% H 2 O(g) at 700, 900, and 1100°C for up to 1h). UAM Zry-4 specimens showed 50% higher mass gain in PWR conditions and 50-80% more mass gain in steam oxidation due to internal oxidation between build layers in both cases. UAM Zry-4 in 900°C steam showed breakaway oxidation leading to sample deformation. Titanium used as an interlayer in the UAM process was detected in the substrate after the 1100°C exposure. Additional experiments to better link as-built defects to oxidation behavior are needed.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Synthesis of U 3 O 8 and UO 2 microspheres using microfluidics

Uranium-bearing microspheres below 50µm with a narrow size distribution allows for a wider variety of fuel forms. To accommodate the smaller size, gel microspheres with a composition of UO 3 ∙nH 2 O∙mNH 3 were synthesized using microfluidics and subsequently converted to U 3 O 8 and UO 2 . To accommodate the slower flow rates required by microfluidics, a more stable broth was established. Additionally, the gelation studies resulted in a broth that was stable for more than two days at 0°C and for close to 3 h at room temperature while still gelling within 25 s. Synthesis of gel microspheres with a narrow size distribution lasted for 5 h and produced ~0.5 g of air-dried material. The gelled microspheres were converted to U 3 O 8 and UO 2 and with sizes of 50 and 40 µm in diameter, respectively.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗
DOE OSTI2022

Identifying chemically similar multiphase nanoprecipitates in compositionally complex non-equilibrium oxides via machine learning

Abstract Characterizing oxide nuclear fuels is difficult due to complex fission products, which result from time-evolving system chemistry and extreme operating environments. Here, we report a machine learning-enhanced approach that accelerates the characterization of spent nuclear fuels and improves the accuracy of identifying nanophase fission products and bubbles. We apply this approach to commercial, high-burnup, irradiated light-water reactor fuels, demonstrating relationships between fission product precipitates and gases. We also gain understanding of the fission versus decay pathways of precipitates across the radius of a fuel pellet. An algorithm is provided for quantifying the chemical segregation of the fission products with respect to the high-burnup structure, which enhances our ability to process large amounts of microscopy data, including approaching the atomistic-scale. This may provide a faster route for achieving physics-based fuel performance modeling.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Improved irradiation resistance of accident-tolerant high-strength FeCrAl alloys with heterogeneous structures

In this work, post–neutron irradiation examination is performed on advanced accident-tolerant fuel (ATF) cladding iron-chromium-aluminum (FeCrAl) alloys with ~10–13at. % Cr, ~10–12 at. % Al, ~1 at. % Mo, and minor alloying elements including Y irradiated to a damage level of 7 displacements per atom (dpa) at irradiation temperatures of 267–282 °C. A compositional dependency of the Cr and Al content is observed on the ratio of sessile and glissile dislocation loops, where the density of a$\langle$100$\rangle$ type loops is somewhat higher than the a/2$\langle$111$\rangle$ type loops. The α' precipitate number density is inversely correlated to the starting Cr concentration of the alloys of interest. The irradiation to a higher dose of 7 dpa results in a higher density of dislocation loops and α' precipitates for the same alloys at a lower irradiation dose, such as 1.8 dpa. In this work, the effect of α' precipitates on the dislocation loop density is discussed, and the presence of α' appears to inhibit the nucleation of loops. Compared with first-generation FeCrAl alloys, these advanced alloys with heterogeneous structure exhibit a lower Cr concentration in α' precipitation at the same dose level; they act as weaker obstacles deviating from the primary hardening contribution from the mature α'. Hence, the overall irradiation-induced hardening decreases; our alloys show improved radiation resistance because of their stronger sink strengths. The results presented in this paper could provide insights for the design and optimization of ATF cladding materials for future fission and space applications.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Properties and microstructure evolution of silicon nitride and zirconium nitride following Ni ion irradiation

We report that silicon nitride and zirconium nitride have been proposed as potential materials for multiple nuclear applications (inert matrix fuels, accident tolerant fuels, space nuclear power, fusion reactor design), yet knowledge on their behavior under irradiation remains limited. Ion irradiations were performed using 15 MeV Ni 5+ ions on Si 3 N 4 and ZrN samples, with midrange doses (around 3 µm) from 1 to 50 dpa and temperatures from 300 to 700°C. Volumetric lattice swelling was determined by grazing incidence X-ray diffraction, defect production and evolution were tracked using Transmission Electron Microscopy, and nanoindentation was performed to quantify the ceramics’ mechanical properties evolution. The results from these irradiation studies on nitride ceramics help fill the current gap present in the literature. Behavior consistent with past work on irradiated Si 3 N 4 was observed with respect to mechanical properties and defect formation up to 15 dpa and 500°C. Failure of the grain boundary sintering aid in Si 3 N 4 was observed above these conditions. Different behavior was observed in both nitrides at 50 dpa and 700°C, where lattice swelling increased past potential saturation values. Unreported cavity formation was witnessed in both materials under all irradiation conditions, with stable number density and slight size increase above 15 dpa. The mechanism for the cavity formation remains to be determined.

36 MATERIALS SCIENCE↗
DOE OSTI2022

High volume packing fraction TRISO-based fuel in light water reactors

We report that for a decade, fully ceramic microencapsulated (FCM) fuel, containing tri-structural isotropic (TRISO) fuel particles in a silicon carbide (SiC) matrix, has been investigated as an accident-tolerant fuel for light water reactors (LWRs). Other examples exist of TRISO-based concepts for LWR fuels with different matrix materials. Previous studies assumed TRISO particle volume packing of approximately 0.44 in SiC (or another) matrix, the highest realistic packing fractions possible with conventional manufacturing. Recent advances in advanced manufacturing have yielded the development and demonstration of a fuel form that consists of conventionally manufactured TRISO particles in a 3D-printed SiC matrix with significantly higher possible TRISO packing fractions (0.5–0.7). This increased uranium loading enhances the viability of using TRISO-based particle fuel forms in LWRs. The viability of high-packing-fraction TRISO-based particle fuel forms in LWRs is assessed from the perspective of fuel cycle length, achievable fuel burnup, reactivity coefficients, and fuel cycle performance. Higher-packing-fraction TRISO-based fuel enables either longer cycle lengths (by ~25% at a packing fraction of 0.55 relative to 0.44) at a constant enrichment or decreased enrichments (by ~25% at a packing fraction of 0.55 relative to 0.44) at a constant cycle length. Studies of different fuel kernel types (uranium nitride, uranium oxycarbide, and uranium carbide) yield similar results, although the cycle length of uranium oxycarbide is shorter than for uranium nitride or uranium carbide (due to the lower density of uranium oxide). This work also characterized the production of 14 C resulting from neutron absorption in 14 N during operation for uranium mononitride fuel kernels; the ratio of 14 C/N was 1–2 at. % at discharge. For the fuel cycle evaluation, the activity of spent nuclear fuel and high-level waste at 100 and 100,000 years was lower for high-packing-fraction fuels than for conventional LWR fuel. Environmental impact metrics were similar overall, but higher on the front end of the fuel cycle and lower on the back end of the fuel cycle. Reactivity coefficients of higher-packing-fraction TRISO-based fuel were reasonable compared with those of conventional fuels.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗
DOE OSTI2022

Additive manufacturing of ceramic materials for energy applications: Road map and opportunities

Among engineering materials, ceramics are indispensable in energy applications such as batteries, capacitors, solar cells, smart glass, fuel cells and electrolyzers, nuclear power plants, thermoelectrics, thermoionics, carbon capture and storage, control of harmful emission from combustion engines, piezoelectrics, turbines and heat exchangers, among others. Advances in additive manufacturing (AM) offer new opportunities to fabricate these devices in geometries unachievable previously and may provide higher efficiencies and performance, all at lower costs. This article reviews the state of the art in ceramic materials for various energy applications. The focus of the review is on material selections, processing, and opportunities for AM technologies in energy related ceramic materials manufacturing. The aim of the article is to provide a roadmap for stakeholders such as industry, academia and funding agencies on research and development in additive manufacturing of ceramic materials toward more efficient, cost-effective, and reliable energy systems.

36 MATERIALS SCIENCE↗
DOE OSTI2022

High-temperature compressive creep tests of U 3 Si 2 with spark plasma sintering: Experiments and finite element modeling

This paper reports a systematic high-temperature creep behavior of dense U 3 Si 2 pellets using a spark plasma sintering (SPS) apparatus at elevated temperatures and pressures under vacuum conditions. The stress exponent was subsequently derived to be 3.21 at 1173 K and 2.17 at 1223 K, respectively, indicating a grain boundary sliding creep mechanism. The creep activation energy was determined to be 203.6 ± 19.0 kJ/mol, which agrees well with the literature. Finite element modeling was performed using the creep parameters fitted from the strain-time plot. Additionally, the results suggest an excellent match with the experimental data, confirming the validity of the experiments. Microstructure characterizations indicate that the main phase of the specimens after creep tests remains to be U 3 Si 2 , with a 4 μm thick layer of nano-sized particles induced from the diffusion between U 3 Si 2 and alumina disc used to avoid electric current passing through the sample. The successful conduct of creep experiments demonstrates the great potential of SPS to perform high-temperature mechanical testing of nuclear fuels under vacuum conditions. The subsequent finite element modeling exhibits excellent capabilities for accurately predicting material performance in the creep tests and provides a practical tool in evaluating nuclear fuels’ performance for a much-extended time scale.

36 MATERIALS SCIENCE↗